Synthesis and Luminescence Properties of Double Perovskite Ca2Gd1-xTaO6∶xTb3+Green Phosphors

PENG Guang-HuaiWEN He-Rui HAN ZhuoLIAO Jin-Sheng

(1School of Chemical Engineering,Jiangxi University of Science and Technology,Ganzhou,Jiangxi 341000,China)

(2School of Chemistry and Chemical Engineering,Gannan Normal University,Ganzhou,Jiangxi 341000,China)

Abstract:A series of double perovskite Ca2Gd1-xTaO6∶xTb3+(CGTO∶xTb3+)phosphors were prepared by a hightemperature solid-state reaction method.The X-ray diffraction,scanning electron microscopy,photoluminescence spectroscopy,decay curve and quantum efficiency(η)were used to characterize CGTO∶xTb3+phosphors.Under UV excitation,CGTO∶xTb3+phosphors show intense green light emission,which is originated from the characteristic5D4-7F5transition of the Tb3+ion.On the basis of temperature-dependence luminescence spectra,the activation energy of thermal quenching was about 0.181 9 eV for CGTO∶0.15Tb3+phosphor.CGTO∶0.15Tb3+phosphor as optimum doping concentration exhibited intensive green emission with theη of 32.32% under 255 nm excitation.

Keywords:green phosphor;Ca2GdTaO6;luminescence;Tb3+

0 Introduction

Lanthanide doped phosphors have attracted great attention for its high feasibility applications in lighting and display systems[1-5].Green phosphors are of capital importance in solid-state lighting for white light sources,and most of green luminescent materials are Tb3+activated phosphors because of its predominant5D4-7F5transition[6-8].Tb3+shows a strong UV excitation characteristic due to its spin-allowed 4f-5dtransition,and an intense visible emission can be achieved in an appropriate host lattice upon the UV excitation[9-10].Therefore,Tb3+doped phosphors are widely used in fluorescent lamps[6-10].

Recently,double perovskite oxides(A2BB′O6)have been widely used as host materials because of their advanced luminescence and thermal stability[11].In a typical structure with double perovskite,B site coordinated by six oxygen atoms is occupied by orderly arranged B and B′.A site possesses various coordination numbers(8～12)depending on the distortion degree of the crystal structure[12-14].Therefore,the local crystal environment,which is critical for luminescence,can be modulated by changing composition elements.Recently,many M3+-activated(M3+=rare earth element ion)phosphors with double perovskite have been investigated owing to their good luminescence properties,such as Sr2LaSbO6∶Eu3+[12],La2MgTiO6∶Eu3+[13],CaLaMgSbO6∶Eu3+[14],Ca2GdTaO6∶Eu3+[15],Ca2YTaO6∶Dy3+[16], Ca2LaTaO6∶Tb3+and Ba2LaTaO6∶Tb3+[17].Ca2GdTaO6belongs to the A2BB′O6structure with double perovskite,which has the monoclinic crystal structure[15,18-19].In Ca2GdTaO6lattice,Ca2+occupies the A site,while Gd3+and Ta5+situate respectively at the B and B′sites.And Gd3+and Ta5+ions occupied the octahedral sites by sharing one oxygen atom,Ca2+ions were situated in the center of the alternation between octahedrons[18-19].

Herein,we report the preparation of double perovskite-type Ca2Gd1-xTaO6∶xTb3+(CGTO∶xTb3+)phosphors by a high-temperature solid-state reaction method.The luminescence properties of CGTO∶xTb3+phosphors were investigated by changing doping concentration of Tb3+ions in the host.Our results show that CGTO∶xTb3+has good properties as a green phosphor for lighting and display application.

1 Experimental

The samples of CGTO∶xTb3+(x=0,0.05,0.1,0.15,0.2,0.3 and 0.4)were synthesized using a hightemperature solid-state method.Stoichiometric quantities of CaCO3(99.9% ),Tb4O7(99.99% ),Gd2O3(99.99% )and Ta2O5(99.99% )used as the starting materials were finely ground in an agate mortar and transferred into the alumina crucibles to be calcined at 1 500℃for 6 h.Then,the samples were cooled down to room temperature and reground for further measurements.

The phase purity of the samples was checked by powder X-ray diffraction (XRD) performed on a Panalytical X′Pert diffractometer with CuKα1radiation(λ=0.154 187 nm)operating at 40 kV and 40 mA in 2θrange of 10°～80°.The morphology and particle size of CGTO∶0.15Tb3+were characterized by a field emission scanning electron microscope (FE-SEM,Tescan-Orsay Holding,MIRA3 LMH)equipped with the energy dispersive spectra(EDS,Thermo Scientific,Ultra Dry)operated at 20 kV.Photoluminescence luminescence(PL),photoluminescence excitation(PLE),and decay curves were measured on a spectrophotometer(FLS980)equipped with both a xenon lamp(450 W)and a pulse xenon lamp(450 W)as the lighting source.

2 Results and discussion

2.1 Crystal structure and morphology

Fig.1 shows the XRD patterns of CGTO∶xTb3+(x=0,0.05,0.1,0.15,0.2,0.3 and 0.4).It could be seen that all the diffraction peaks of the samples were identified to the standard card of Ca2GdTaO6(PDF No.73-0085)except for a relatively weak peak at 2θ=28.5°marked with the symbol(*).This impurity peak can be attributed to Gd3TaO7(PDF No.38-1409)impurity phase.The Tb3+ions are proposed to occupy the Gd3+sites because the effective radius of Tb3+ions(0.092 3 nm for CN=6)is very close to that of Gd3+ions(0.093 8 nm for CN=6)(CN=coordination number)[20].

Fig.1 XRD patterns of CGTO∶xTb3+

Rietveld refinement analysis was further performed from the powder XRD data using the General Structure Analysis System(GSAS)program.Fig.2a shows the fitted Rietveld refinement data and the difference between the calculated and experimental data of the typical CGTO∶0.15Tb3+phosphor.The detailed refinement results for CGTO∶0.15Tb3+phosphor are listed in Table 1.The smaller residual parameters(Rwp=2.36% andRp=1.5% )and goodness of fit(χ2=3.494 8)for all the fitting data,together with the tiny fluctuation in the difference curves shown in Fig.2,indicate high reliability of the refinement results.The schematic of CGTO crystal structure is shown in Fig.2b.Gd3+ions occupy B sites with six-folded coordination.

Fig.2 (a)Rietveld refinement for XRD patterns of CGTO∶0.15Tb3+phosphor;(b)Crystal structure of CGTO∶0.15Tb3+phosphor

Table 1 Refined crystallographic parameters of CGTO∶0.15Tb3+phosphor

Fig.3a and 3b show SEM images of CGTO∶0.15Tb3+phosphor.The morphology of the sample was ovaloid-like and the particle size was 2～3 μm.In addition,Fig.3c～3g show the distribution of each element of one phosphor particle.The results indicate that Ca,Gd,Ta,O and Tb are evenly distributed.The EDS was used to further characterize the chemical composition of the as-prepared product,and the result of CGTO∶0.15Tb3+phosphor shown in Fig.3h was 39∶17∶3∶19 ofnCa∶nGd∶nTb∶nTa,which was close to the chemical formula of CGTO∶0.15Tb3+.The results confirm that Tb3+ions have been effectively incorporated into the CGTO host lattice,consisting with the XRD analysis above.

Fig.3 (a,b)SEM images of CGTO:0.15Tb3+;(c～g)Distribution of the elements in CGTO:0.15Tb3+;(h)EDS spectrum of CGTO:0.15Tb3+

2.2 Photoluminescence properties

Fig.4a shows the PLE spectrum of CGTO∶0.15Tb3+at room temperature.The PLE spectrum of CGTO:0.15Tb3+,which monitored the PL peak at 543 nm,exhibited an intense peak at 255 nm assigned to the allowed 4f-5dtransition of Tb3+.The PL spectra of CGTO∶xTb3+samples under UV(255 nm)excitation are shown in Fig.4b.The Tb3+luminescence was composed of two series of emission peak at 400～470 nm and 470～700 nm(Fig.4b),which are attributed to Tb3+ions transitions from5D3-7FJ(J=5,4,3)and5D4-7FJ(J=6,5,4,3),respectively[21].Owing to the obvious concentration quenching of the Tb3+luminescence at5D3-7FJ(J=5,4,3)transitions,the emission at 400～470 nm region was very weak[21].Where blue and green as well as red emission centered at 490,543,588 and 623 nm are attributed to the5D4-7FJ(J=6,5,4,3)transitions of Tb3+,respectively[22].As shown in the inset of Fig.4b,the relative integrated intensity of the dominant emission from5D4-7F5transition increased with the increasement of the Tb3+-concentration,reaching maximum atx=0.15 Tb3+doping,and then decreased with the further increasing Tb3+concentration.

Fig.4 Photoluminescence spectra of CGTO∶xTb3+:(a)excitation spectrum of CGTO∶0.15Tb3+,λem=543 nm;(b)emission spectra(λex=255 nm)with the inset showing the relative integrated intensity of the dominant emission from5D4-7F5transition

The CIE chromaticity coordinates for the emission of CGTO∶0.15Tb3+under 255 nm excitation is shown in Fig.5,and the inset at the top right corner is luminescence image of CGTO∶0.15Tb3+irradiated by 254 nm UV lamp.The color coordinates(x,y)of CGTO∶0.15Tb3+phosphor was calculated as(0.348 6,0.562 0).The CIE coordinates belong to green region.The corresponding color temperature can be calculated using the following formula[23]:

Fig.5 CIE chromaticity coordinates of CGTO∶0.15Tb3+(λex=255 nm)and luminescence image(Inset)of CGTO∶0.15Tb3+irradiated by 254 nm UV lamp

wheren=(x-0.332)/(y-0.185 8).The color temperature of CGTO∶0.15Tb3+phosphor was 5 219 K.

To investigate the luminescence concentration quenching,the critical distance(Rc)between two Tb3+ions in CGTO∶xTb3+crystalline can be estimated by the formula[24]:Rc=2[3V/(4πNxc)]1/3(2),whereVis the volume of the unit cell,xcis the critical concentration andNis the number of available crystallographic sites occupied by the activator ions in the unit cell.The Rietveld refinement analysis values ofVandNfor CGTO∶0.15Tb3+crystalline were 0.263 523 nm3and 2,respectively.The critical distance of two Tb3+ions in CGTO∶xTb3+was 1.188 1 nm.It is known that the nonradiative energy transfer mechanism consists of exchange interaction and electric multipolar interaction.The exchange interaction comes into effect only when the typical critical distance between the activators is shorter than 0.5 nm.Here,the critical distance is much longer than 0.5 nm,so the concentration quenching is dominated by the multipole-multipole interaction in CGTO∶xTb3+.According to Dexter theory,the type of electric multipolar interaction among Tb3+ions can be deduced by the following equation[25]:

whereKandβare constants;xis the activator Tb3+concentration;Iis the dominant emission intensity from5D4-7F5transition of CGTO∶xTb3+phosphors;θequals6,8or 10 corresponding to dipole-dipole,dipole-quadrupole or quadrupole-quadrupole interaction,respectively.Fig.6 demonstrated that the relationship between lg(I/x)and lgxwas approximately linear,and the slope was around-1.94,which meant thatθwas about 6.0.The result indicates that the mechanism of concentration quenching for Tb3+luminescence centers is the dipoledipole interaction in the CGTO∶xTb3+host lattice.

Fig.6 Relationship between lg(I/x)and lgx for CGTO∶xTb3+phosphor

Thermal stability is an important parameter of a phosphor.In order to investigate the thermal stability of CGTO∶0.15Tb3+phosphor,we measured PL spectra of CGTO∶0.15Tb3+phosphor with UV excitation 255 nm at different temperatures(25～300 ℃),as shown in Fig.7.The PL intensity of CGTO∶0.15Tb3+phosphor decreased along with the temperature increasing,which is due to thermal quenching.In the process of thermal quenching,the activation energy(ΔE)can be determined by the following Arrhenius equation[26]:IT=I0/{1+cexp[-ΔE/(kT)]}(4),whereI0andITstand for the initial emission intensity and the luminescence intensity of the dominant emission from5D4-7F5transition at temperatureT,respectively;cis a constant for a designated host andkis the Boltzmann constant(8.617×10-5eV·K-1).The activation energy(ΔE)can be calculated by plotting ln[(I0/IT)-1]vs 1/(kT),as shown in Fig.8,and the ΔEof CGTO∶0.15Tb3+that equals the minus slope of the fitting line was determined to be 0.181 9 eV,which was close to the value of 0.2 eV for Ca3Ga2Ge3O12∶Tb3+phosphor[27].

Fig.7 Temperature dependent emission intensity spectra of CGTO∶0.15Tb3+

Fig.8 Plot of ln[(I0/IT)-1]vs 1/(kT)for thermal quenching of CGTO∶0.15Tb3+

To further clarify the concentration quenching of Tb3+in CGTO host,the luminescence decay curves of CGTO∶xTb3+phosphors(λex=255 nm,λem=543 nm)are shown in Fig.9.The luminescence decay curves of Tb3+doped with different Tb3+concentrations can be well fitted into a single-exponential function asI=Aexp(-t/τ)+B(5),whereIis the relative intensity;tis time;AandBare constants;τis the lifetime of the Tb3+ions.The fitting results are listed in Table 2.The lifetime of the Tb3+ions decreased with increasing Tb3+concentration.The decay time decreased from 4.181 7 to 1.719 1 ms,when the Tb3+doping concentration increased from 0.05 to 0.4.It can be attributed to the increased non-radiative energy migration among Tb3+ions.

Fig.9 Luminescence decay curves of CGTO∶xTb3+phosphors under 255 nm excitation

In order to investigate the luminescence efficiency,quantum efficiency(η)of CGTO∶0.15Tb3+was tested under 255 nm excitation,which is shown in Fig.10,and the value was obtained by the following equation[28]:

Fig.10 Excitation line of BaSO4reference and emission spectrum of CGTO∶0.15Tb3+under 255 nm excitation collected using an integrating sphere

Table 2 Lifetime(τ)of Tb3+543 nm emission in CGTO∶xTb3+phosphors under 255 nm excitation

whereLSandESare the emission and excitation spectra of objective samples;ERis the spectrum of the excitation light without the samples in the integrating sphere.The quantum efficiency of CGTO∶0.15Tb3+was calculated to be 32.32% ,which was close to that of LiLaSiO4∶Tb3+(39.8% )[29].

3 Conclusions

In summary,we synthesized CGTO∶xTb3+phosphors by a high-temperature solid-state reaction method.The intense green luminescence corresponding to5D4-7F5transition of Tb3+of the sample was clearly observed under 255 nm excitation.The optimum doping concentration of Tb3+was 0.15.The quantum efficiency of CGTO∶0.15Tb3+was calculated to be 32.32% .CGTO∶Tb3+phosphor exhibited an intensive green emission and high activation energy as well as low thermal quenching occurring under UV light excitation.These results suggest that CGTO∶Tb3+phosphor is a promising green-emitting phosphor for optical devices.

Acknowledgements:This work was financially supported by the National Natural Science Foundation of China(Grant No.51862012)and the Natural Science Foundation of Jiangxi Province(Grants No.20202BAB204008,20165ABC28010)as well as the Innovation Leadership Program of Ganzhou.