    Performance characterization of Ni60-WC coating on steel processed w ith supersonic laser deposition

    2015-11-08 07:31:00FangLUOAnrwCOCKBURNMartinSPARKESRooLUPOIZhijunCHENilliamNEILLJianhuaYAORongLIU
    Defence Technology 2015年1期

    Fang LUO*,Anrw COCKBURN,Martin SPARKES,**,Roo LUPOI,Zhi-jun CHEN,W illiam O'NEILL,Jian-hua YAO,Rong LIU

    aCollege of Zhijiang,Zhejiang University of Technology,Hangzhou 310024,Zhejiang,China

    bInstitute for Manufacturing,Departmentof Engineering,University of Cambridge,CB3 OFS,UK

    cDepartmentofMechanical&Manufacturing Engineering,Trinity College Dublin,Dublin 2,Ireland

    dCollege of Mechanical Engineering,Zhejiang University of Technology,Hangzhou 310012,Zhejiang,China

    eDepartmentofMechanical&Aerospace Engineering,Carleton University,1125 Colonel By Drive,Ottawa,Ontario K1S 5B6,Canada

    Received 26 February 2014;revised 29 August 2014;accepted 19 September 2014 Available online 26November 2014

    Performance characterization of Ni60-WC coating on steel processed w ith supersonic laser deposition

    Fang LUOa,*,Andrew COCKBURNb,Martin SPARKESb,**,Rocco LUPOIc,Zhi-jun CHENd,W illiam O'NEILLb,Jian-hua YAOd,Rong LIUe

    aCollege of Zhijiang,Zhejiang University of Technology,Hangzhou 310024,Zhejiang,China

    bInstitute for Manufacturing,Departmentof Engineering,University of Cambridge,CB3 OFS,UK

    cDepartmentofMechanical&Manufacturing Engineering,Trinity College Dublin,Dublin 2,Ireland

    dCollege of Mechanical Engineering,Zhejiang University of Technology,Hangzhou 310012,Zhejiang,China

    eDepartmentofMechanical&Aerospace Engineering,Carleton University,1125 Colonel By Drive,Ottawa,Ontario K1S 5B6,Canada

    Received 26 February 2014;revised 29 August 2014;accepted 19 September 2014 Available online 26November 2014

    Ni60-WC particles are used to improve thewear resistance of hard-facing steel due to their high hardness.An emerging technology that combines laser with cold spraying to deposit the hard-facing coatings is known as supersonic laser deposition.In this study,Ni60-WC is deposited on low-carbon steel using SLD.Themicrostructure and performance of the coatings are investigated through SEM,opticalm icroscopy,EDS,XRD,microhardnessand pin-on-discwear tests.The experimental resultsof the coating processed with the optimalparametersare compared to those of the coating deposited using laser cladding.

    Ni60-WC;Supersonic laser deposition;Laser cladding;M icrostructure;Wear

    1.Introduction

    Ni60 alloy,in combination w ith hard tungsten carbide(WC),isw idely used to improve thewear resistanceof steelas surface coating.Ow ing to an excellentwear resistance,Ni60-WC has been applied in many fields of industry,such as m ining,transport,engineering,manufacturing industries,etc. However,Ni60-WC coatings have been found often to have cracksand pores in them.In recent years,the researchershave attempted to apply various deposition techniques on this type of coating to achieve the crack/flaw-free coatings.The traditional techniques,such as thermal spraying,plasma spraying, arcwelding,and laser cladding(LC),have often been used to produceWC-reinforced Ni60 composite coatings.Wang etal.[1]studied the abrasive resistance of Ni-based coatings w ith WC hard phase prepared by plasma spraying w ith laser posttreatm ent,and tested the abrasive wear resistances of three Ni-WC com posite coatings w ith different contents of WC particles.The results show that the best coating contains the composition of Ni60+60%WC(w t%)but ithas the pores in it.Although the cold spraying techniqueoffershigh deposition efficiency and low oxidation and retains the initial composition and/or phases of coating materials,it cannot be used to deposit the hard particles.In contrast,the arc welding and laser cladding techniques can be used to deposit the hard particles and offer a good metallurgical bonding because a molten pool is formed on the surface of the substrate,but the coating and substrate can be severely deformed due to excessive energy input.In these processes,WC particles are largely dissolved in the melt pool during deposition,whichreduces the hardness of the final coating.Additionally,the thermal stresses induced during the course of welding or cladding can lead to crack formation in the coating,and the low cladding efficiency increases the processing cost of cladding over large areas[2,3].Zhou etal.[4-6]observed the cracks in the Ni60 coatings deposited by laser cladding but achieved fully dense and crack-free Ni-based WC composite coatings and Ni60 coatings prepared using laser induction hybrid rapid cladding w ith an elliptical spot.However,this technique restricts the geometry of substrate to simp le shape,such as flat,shaft,etc.It is not suited for preparing the comp lex products.The key reason why Ni60-WC coatings cannot be app lied in m any areas is that the carbide particles result in the formation of cracksand pores.Therefore,the contentand size of WC grain have an important effect on the characteristics of the coatings[2,7].Matthew et al.[8,9]successfully combined laser cladding w ith cold spraying together to prepare high-density coatings consisting of Tiand Ti alloy,and used cold N2as a carrier gas to reduce the cost of cold spraying.The supersonic laser deposition(SLD)method offers many advantages by combining laser w ith cold spraying,in particular,the use of a laser to control the deposition temperature,which allows hard materials,such as Stellite 6 and carbide[10,11],to be deposited whilemaintains the key advantagesoffered by solid-state cold spraying and replaceshigh costhelium w ith nitrogen.Moreover,the high-speed impactof particleson the substrate produces severe plastic deformation,resulting in a good bonding of the coating and the substrate. Meanwhile,SLD avoids the melting of the coating material and therefore retains the finemicrostructure of the coating and preventsWC from degrading.

    In the present research,since SLD hasmany advantages,such as high deposition rate,low dilution,it could be used to deposithardmaterialon the steel,etc.This paper dem onstrates the influenceof laser poweron the characteristicsof Ni60-WC composite coatings deposited using SLD and compares the results of those deposited using LC.

    Fig.1.Ni60 particles and size distribution.

    Fig.2.WC particles and size distribution.

    2.Experimentalmethods

    2.1.Powder preparation

    The coating m aterial was a m ixed pow der consisting of Ni60 and 30%WC w ith different particle sizes.The contentproportion of Ni60 to WC was optim ized from many experimentsof laser cladding,spray remelting and AC-HVAF spray[1,15].The size of particle in the feed stock powder was analyzed by laser dispersion.The diameter of powder particle was selected based on Refs.[12-17],and the product of the Ni60 spray powder is commercially available.The diameters ofmost particles in Ni-based self-fluxing alloy are in the range from 30μm to 50μm,asshown in Fig.1,and the diametersof most particles in WC powder are approximately 10μm,as shown in Fig.2.It can be observed that the clusters of WC particlesare stuck together and the individualWC particlesare hardly found.The chem ical composition of Ni60 and the weight percentage of each element are given in Table 1.The m ixed 70%Ni60 and 30%WC powder was deposited on carbon steel substrate using a SLD system[8,9,18],and the process parameters for a single track are listed in Table 2.

    Table 1 Chem ical composition of Ni60 pow der.

    Table 2 Process parameters for a single track of SLD.

    Fig.3.Characteristics of coating specimen 1.

    Fig.4.Characteristics of coating specimen 3.

    Initially,the single track was sprayed over a range of operating conditions to identify the laser power ranges required for deposition.To quickly identify the optimal laser power,the operating pressure was kept at 30 bar to give a gas velocity of approxim ately 1000 m s-1and a traverse rate of 10mm s-1for SLD.Low-carbon steel platesw ith dimensions of 160×55×2 mm were used as substrates.

    2.2.Microstructure analysis

    The obtained SLD coating structureswere examined under an opticalmicroscope,in combination w ith A4i image analysis software.The cross-sections of the coating specimens were polished and then etched w ith the chemical solution which consists of 5 g FeCl3,2 m l HCl and 99 m l ethanol.

    A scanning electron m icroscope was used to analyze the surface topography and microstructure of coating specimen. The chem ical compositions of the coatings were evaluated using an energy dispersive spectroscopy(EDS),and the phases in the m icrostructures were identified using an X-ray diffractometer and the X'Pert Pro analysis software.

    3.Results and discussion

    3.1.Single track for SLD

    3.1.1.Coating structure

    The coating specimens 1,3 and 5,asnumbered in Table 2,were selected for analysis.The structures of these specimens are shown in Figs.3-5(a),respectively.A large amount ofsmall,brightand white particles,which sizesof the range from 1μm to 3μm are observed from Fig.3(a);the small pits and poresaredistributed in thematrix.Theelementdistributionsare illustrated in Fig.3(b),show ing peaks and valleys,where the former of the curve(white particle)indicates the peaks:high tungsten and carbon contents,the later(rectangle)indicate the valleys:low tungsten content,and high chrom ium and iron contents.Fig.3(c)shows the scanning graph of elements of coating specimen 1.The brightandwhiteobjectshould beWC,the thin and white dendritic crystals in thematrix are likely to be chromium carbide.These results confirm that the brightand whiteobjectisWC particles,which aredistributed in thematrix w ith FeNi and chromium carbides.Fig.4(a)shows that the largerbrightobjectsaredistributed in thematrixw ith largerpits and pores.Fig.4(b,c)show that the larger polygonal and bright object are WC particles,the small white crystals probably are Cr7C3and Cr23C6,and thematrix may bew ith FeNi.

    Fig.5.Characteristics of coating specimen 5.

    Fig.6.XRD spectra of Ni60-WC pow der and Ni60-WC coatings.

    Fig.7.M icrohardnesses of cross-sections of 5 coating specimens.

    Fig.8.Topographies of coating cross-sections.

    From Fig.4(a)it can be seen that,for coating specim en 3 which was prepared w ith higher laser power,the sizes of the white particles and the smallwhite crystals increasew ith the increase in laser power;the sizes of some WC particles are over 2μm,and they exhibit partially dendritic crystals,as indicated by arrow at top left corner.W ith the increase in laser power,the largeWC particles(light)of coating specimen 5 in Fig.5 are distributed in thedendritic crystalsof Cr7C3,Cr23C6and FeNimatrix.

    It can be seen from Figs.3-5(a)that the crystals of chrom ium carbides grew from thin dendritic crystals to coarse dendritic crystals w ith the increase in laser power;so did the WC particles.Hard phases,such as Cr7C3,Cr23C6and WC particle,are the key factors of improving the hardness and anti-wearing properties of the coatings.

    X-ray diffraction(XRD)analysis was conducted on the coating specimens to confirm the phases formed during deposition.The XRD spectra are shown in Fig.6.The phases of the coatingsdeposited by SLD areCr7C3,Cr23C6,F(xiàn)eNi,and WC.This isquite different from the normal laser cladding ofWC-Ni,where WC in the coating hard ly dissolves and is diffused into laser cladding and form compound.

    3.1.2.Microhardness of cross-sections

    Since the change in the amount of WC results in a large variation in hardness data,the microhardness of coating is m easured along horizontal direction and vertical direction from the interface to the coating surface at constant intervals of 0.4 mm using a digital micro-hardometer.The average hardnessesof five coatingsare shown in Fig.7.It can be seen from Fig.7 that them icrohardnessof coating 1,HV0.3742,is the highest,and themicrohardnessof coating 5,HV0.3687,is the lowest.These results show that the differencesamong the m icrohardnesses are small.Itmay infer that the hardness is dependent on the structure of carbide.Consider this again from Figs.3-7,there is also a correlation among laser power,coating structure and coating hardness.

    Fig.9.Porosity analysis of the coatings.

    Table 3 Process parameters for single tracks and multi-tracks of LC.

    3.1.3.Cross-section topography

    Fig.8 shows the topographies of the coating specimens in Table 2.Coating specimen 1 in Fig.8(a)shows the highest density among the coatings.At the top of coating layer appear many bright and fine WC particles,which is consistentw ith the hardness test result.

    Many pores and smallWC are observed in coating specimen 2 in Fig.8(b).These carbides particles are uniform ly distributed in the coating,but their amount is very little.

    The pits or pores in the coating are increased w ith the increase in laser power.This is because the coating material starts to melt partially in this case.The sizes of Ni60 and carbide particleswere found to be increased w ith the increase in laser power.Oxygen in air can possibly react with some chem ical elements of the coating,such as carbon,to produce gases,resulting in the formation of pores.Fig.8(c-e)show the pits in the coatings.However,most pitsmay notbe pores,as shown in Fig.9;they are the holes leftwhenWC particles are spalled off during polishing.

    Fig.9 presents the analysis of red areas in percentage of pits in the coatings.The dark areasmay represent the pores formed in the SLD process,and the holes due to spallation of WC particles during polishing.It can be seen from Fig.9 that thepercentage of dark areas in coating specimen 1(2 kW laser power)is the least.

    Higher laserenergy can result in stronger adhesion between theWC particles and Ni60 matrix,but it can also reduce the WC content.When the laser powerwas increased from 2 kW to 4 kW,the amount of WC particles decreased,as show in Fig.9.However,the laser power was not sufficiently high to m elt the alloy comp letely;the deposited particles were not comp letely melted.Some areas show the good adhesion between the WC particles and Ni-based matrix,w ith the spallation ofWC particles pull-outbeing avoided during polishing. However,notonly the adhesion between the Ni-based coating and WC isaffected by the input energy,but it isalso affectedby the coefficients of thermal expansion of Ni60 and WC.If their coefficients of thermal expansion are the same,the grow th ratesof these particlesare thesame,the amountof pits or pores would be reduced due to good matching w ith each other,the adhesion between the Ni-based coating and WC would be better at the same laser power.

    The above analysis indicates that coating specimen 1,deposited under a N2atmosphere at a pressure of 30 bar,a temperature of 450°C and a deposition power of 2 kW,is the best among the coating specimens under study.Single track coatings prepared w ith these parameters were further investigated in dilution rate.

    Fig.10.M ulti-track LC coatings.

    Fig.11.Cross-section of SLD coating.

    Table 4 Optimal process parameters formulti-tracks.

    3.2.Comparison of SLD coating with LC coating

    Ni60-WC powderwasdeposited on low-carbon steelby LC w ith laser power of 1.8-2.0 kW and scanning velocity of 3-10 mm s-1,as detailed in Table 3.Only one coating(No.2in Fig.10(a))deposited at laser power of 2 kW and scanning velocity of 10 mm s-1was crack-free.

    Multi-tracksw ith a deposition w idth of 4mm and overlap of 2 mm were made to investigate the performances of the coatingsunder the deposition conditionsw ith laser power of 2 kW and traverse rate of 10 mm s-1.The cracks were also found in these coatings.The cross-sections of LC coatings are shown in Fig.10(b),whichwere compared w ith the SLD coating having a deposition w idth of 4 mm and three layers under the conditions of optimal process(N2atmosphere,pressure of 30 bar,temperature of 450°C,deposition power of 2 kW and traverse velocity of 10 mm s-1).The optimal process parameters of multi-track coating are listed in Table 4.

    Cracksarehardly found in the firstand second layersof the multi-track SLD coating,but they are observed in the third layer,as shown in Fig.11.The cracking may be due to the phase transition of the material at different temperatures,resulting in the change of volume or stress.

    Fig.12.Element line scan of SLD and LC coatings.

    Fig.13.Structures of Ni60-WC coatings.

    Table 5 Element compositions of LC coating.

    3.2.1.Analysis of element dilution

    During the LC process,a high pressure gas supp ly was split and delivered to a nozzle directly via a high pressurepow der feeder where the m etal pow der particles are entrained.The temperature in a deposition zone wasmonitored by a high-speed IR pyrometer(Kleiber).The consistent deposition site conditions weremaintained by using the pyrometer to control the laser power via a PID loop built in to the control software.

    Fig.14.Distribution curves ofmicrohardness and friction coefficients for the Ni60-WC coatings.

    The substrate was held stationary while the nozzle,laser head and pyrometer can bemoved using a CNC X-Y stage,allow ing the samples to be up to 1600mm in diameter.

    Fig.12(a,b)show the line scan of Ni,Cr and W from the interface to the coating(or substrate)along the cross-sections of SLD and LC coatings,the testing distance is 2.7 mm and 2.4mm,respectively.Since thesubstratematerialof SLD does not contain Ni,Cr and W,these results exhibita low dilution rate from the coating to the substrate for SLD.

    Asillustrated in Fig.12(c),the contentsofNi,CrandW in the coatings are higher,and the contents of Ni,Cr and W in the substratesare lower.ThecontentsofNi,W and Crin SLD coating are higher than those in LC coating.Thisshow s that theW orCr reactedw ithC-formingcarbidesin theLCcoating,andNireacted w ith Fe-forming FeNi,which resulted in thedecrease of theelements in the LC coating,that is,higherelementdilution.

    Fig.15.Structures of coating cross-sections.

    3.2.2.Microstructural analysis

    Asshown in Fig.13(a),the smallpolygonaland brightWC particlesare embedded in Ni60matrix.The pits in blackmay be the holes due to the spallation of WC particles during polishing or the pores formed due to the impact among the particles.

    Fig.13(b)show s the clear formation of dendritic crystals. Thewhite eutecticswere distributed along the crystal boundary,and the circular areas of the LC coating weremeasured and analyzed using an energy dispersive X-ray(EDX)detector.The resultsare presented in Table 5.It can be seen that the iron and nickel contents in area A are higher than those in area B,and the tungsten and carbon contents in area B are higher than those in area A.These results,together w ith X-ray diffraction(XRD)analysis results in Fig.6,were used to identify the eutectics form ed during the LC deposition.The phases of the coating deposited using LC are Cr7C3,Cr23C6,F(xiàn)eNi,and Fe7W6;the LC coating has no WC because Fe reactsw ithW-forming Fe7W6.Thismay be attributed to the fact that the inputenergy of LCwasmuch higher than thatof SLD,which led to the formation of Fe7W6.If the processparameters in Table 4 are used,the energy density of SLD is the same as the optim ized energy density of LC,but the laser melts the powder in LC,while the laser heats the deposition area inSLD.Therefore,for LC,themain phase in area A is FeNi,and themain phases in area B are Cr7C3,Cr23C6and Fe7W6.

    A comparison of the phases among Ni60-WC powder,LC coating and SLD coating shows that B2O3is not present in SLD and LC coatings.The reason for thismay be that the area B is oxidized when itwas exposed in air during the powder preparation.B2O3would be vaporized atover 1500°C.

    Fig.16.Worn surface of Ni60-WC coating prepared using SLD.

    Table 6 Element compositionsof debris on SLD coating.

    3.3.M icrohardness and wear resistance

    The frictional and wear forces to which machinery components are subjected result in great loss of energy and material.Hardness is a key property that accounts for the antiwearing ability of materials.Thermal spraying,laser cladding and other surface techniques can be used to deposit the hard particles on the substrates to improve their hardness and wear propertiesagainst the frictional and wear forces thatact on the surfaces of components[15,19-24].

    Fig.14(a)provides the averagem icrohardnessesmeasured for 3 or 5 indentations at constant longitudinal interval of 0.3 mm from the interface to the coating surface(or substrate)using a digital micro-hardometer.The friction coefficients were measured using a pin-on-disc machine with a Si3N4ceramic ball having 5 mm in diameter.The rotational radius was 2.5 mm,the normal load was 200 g,the rotational speed was800 rmin-1,and the testduration timewas2 h.Asshown in Fig.14,the highesthardness value is HV0.3690 that is for the SLD coating.This is due to the fact that the amount of carbides in the coating ashard phases isgreater than that in the LC coating.The lowesthardness value is HV0.3394 that is for the LC coating.This is because of the higher energy density induced by decomposing amassof carbidesashard phases to form Fe7W6.Moreover,F(xiàn)ig.14(a)shows that themicrohardnessof the interface close to thesubstrate ishigher than thatof substrate,which is due to the fact that the input energy resulted in a phase change to lathmartensite.Fig.14(b)shows that the friction coefficient of LC coating isalmost tw ice that of SLD coating.The friction coefficients of LC and SLD coatings show the fluctuations between 0.10-0.40 and 0.13-0.23,respectively.Furthermore,in Fig.15(a),the martensite is present in thinner dentric crystal due to lower energy density of SLD in comparison w ith that of LD in Fig.15(b).Chen et al.[25]proved that themicron scale WC particles can play a very effective role in resisting wearing.

    The worn surface of Ni60-WC coating processed using SLD is shown in Fig.16.Fig.16(a)shows thewear track,and Fig.16(b)shows thewear debris.Thescarswere caused by the abrasion of Si3N4ball,and the scratches are likely due to the cracking of carbide.Fig.16(c)show s the debris at high m agnification;it can be deduced that som e relatively larger bulksw ith irregular shapes are possibly WC particles broken due towearing or coating withWC.The debriswasexaminedusing EDX,and the results are presented in Table 6,which shows that the debris consistsmainly ofWC and FeNi.

    Fig.16(d)showstheweartrackathighmagnification,whereit canbeseen thatamassofWC isembedded in theNialloymatrix. Thematrix w ith the scars lefton theworn surfacewasabraded. High-hard WC on the coating during wearing can protect the coating from wearing.As a result,the wear resistance is improved,and the coating base can support the hard particles,avoidingWC fractureand abscission,retaining thehigh hardness ofWC and losing lessmass.During the later stagesofwearing,the supporting base is continually abraded,and the supporting effectof thebaseisgradually reduced.Asa result,partof theWC phase begins to crack and falloff.Theworn surface transforms into a new layer,and theprocess iscontinually repeated.

    Theworn surface of the Ni60-WC coating prepared using LC is shown in Fig.17.Asseen in Fig.17(a),thewear track is quite different from that in Fig.16(a).Fig.17(b)shows the wear debris.Fig.17(c)shows the obvious,deep and broad wear scars.The debris isgrind to form a laminate on theworn surface.Fig.17(d)shows thata part of the debrismoves away due to the brittle debris pulling outduring wearing,and reveals the topography of the wearing surface.Table 7 shows the element compositions of the debris for LC coating.It can be seen from Table 7 that the contentsof C andW are lower than those in SLD coating,and the contentof Fe ishigher than that of SLD coating.It can be seen from the dilution analysis that the elements of LC coating diffused into the substrate or the elements of the substrate diffused into the coating.It can be seen from Fig.6 and Fig.13(b)that the phases of Ni60-WC coating deposited by laser cladding exclude WC phase,and the tungsten and iron form the com pound Fe7W6.The lost weights,friction coefficients and average hardnesses of SLD and LC are shown in Table 8,respectively,which show that the lost weight and the friction coefficient of SLD coating are lower than thoseof LC coating,and themicrohardnessof SLD ishigher than thatof LC.These data prove thatSLD results in improved tribological properties of Ni60-WC coating in comparison to that produced using LC.

    Fig.17.Worn surfaces of Ni60-WC deposited using LC.

    Table 7 Element compositions of debris on LC coating.

    Element Cr C W Fe Ni W t.%3.27 16.14 8.51 64.6 7.48

    Table 8 Properties of Ni60-WC coatings.

    4.Conclusions

    1)The characteristics of the Ni60-WC com posite coating deposited on low-carbon steel using SLD w ith the variousprocess parameters were studied.The optimal deposition conditions are N2atmosphere,pressure of 30 bar,temperature of 450°C,traverse rate of 10 mm s-1and laser power of 2 kW with respect to themicrohardnessandwear properties of the coating.

    2)The coating deposited using SLD contains Cr7C3,Cr23C6,F(xiàn)eNi,andWC particleswhile the coating deposited using LC contains Cr7C3,Cr23C6,F(xiàn)eNi,and Fe7W6.Both of the coatings do not have B2O3.The interface between the coating and the substrate bonds strongly.WC particles are embedded in the alloy m atrix in the SLD coating,while the carbide is distributed along the grain boundaries for the LC coating.A diluted layer is hard ly found in the coating deposited using SLD.

    3)ThemicrohardnessandwearpropertiesofNi60-WCcoatings depositedusingSLDand LCwereexamined.Comparedwith theLCcoating,thehardnessof theSLD coatingishigher,and its friction coefficientand theweight lossare lower.

    Acknow ledgm ents

    This work was sponsored by the Centre for Industrial Photonics,Institute for M anufacture,Departm ent of Engineering,University of Cambridge;the Natural Science Foundation of China(51271170);China International Science and Technology Cooperation Project(2011DFR50540);Major Scientific and Technological Special Key Industrial Project of Zhejiang Province(2012C11001).

    We would like to express our gratitude to the Key Laboratory of Special Purpose Equipment and Advanced Processing Technology(Zhejiang University of Technology),the M inistry of Education,China,and sincerely thank M r.Yuanhang LU for providing assistance in sample preparation.

    [1]Wang H,Xia WM,Jin YS.A study on abrasive resistance of Ni-based coatings w ith a WC hard phase.Wear 1996;195:47-52.

    [2]Acker KV,Vanhoyweghen D,Persoons R.Influence of tungsten carbide particle size and distribution on thewear resistance of laser cladWC/Ni coatings.Wear 2005;258:194-202.

    [3]Paul CP,A lemohammad H,Toyserkani E.Cladding of WC-12 Co on low carbon steel using a pulsed Nd:YAG laser.Mater Sci Eng:A 2007;464:170-6.

    [4]Zhou SF,Zeng XY,Hu QW,Huang YJ.Analysis of crack behavior for Ni-based WC composite coatings by laser cladding and crack-free realization.Appl Surf Sci2008;255:1646-53.

    [5]Zhou SF,Huang YJ,Zeng XY.A study of Ni-based WC composite coatings by laser induction hybrid rapid cladding w ith elliptical spot. Appl Surf Sci 2008;254:3110-9.

    [6]Huang YJ,Zeng XY.Investigation on cracking behavior of Ni-based coating by laser-induction hybrid cladding.App l Surf Sci 2010;256:5985-92.

    [7]Wittmann B,SchubertWD,Lux B.WC grain grow th and grain growth inhibition in nickeland iron binderhardmetals.Int JRefractMetalsHard M ater 2002;20:51-60.

    [8]Bray M,Cockburn A,O'NeillW.The laser-assisted cold spray process and deposit characterisation.Surf Coat Technol 2009;203:2851-7.

    [9]Cockburn A,Bray M,O'NeillW.The laser-assisted cold spray process. Laser User 2008;53:30-1.

    [10]Lupoi R,Cockburn A,Bryan C,Sparkes M,Luo F,O'Neill William. Hardfacing steelw ith nanostructured coatingsof Stellite-6 by supersonic laser deposition.Light:Sci Appl 2012:1-6.http://dx.doi.org/10.1038/ lsa.2012.10.e10.

    [11]Luo F,Cockburn A,Lupoi R,Sparkes M,O'Neill W.Performance comparison of Stellite 6?deposited on steel using supersonic laser deposition and laser cladding.Surf Coat Technol 2012;212:119-27.

    [12]Wu YS,Qiu WQ,Yu HY,Zhong XC,Liu ZW,Zeng DC,et al.Cycle oxidation behaviour of nanostructured Ni60-TiB2composite coating sprayed by HVOF technique.Appl Surf Sci2011;257:10224-32.

    [13]Zhang XC,Xu BS,Tu ST,Xuan FZ,Wang HD,Wu YX.Effect of spraying power on the m icrostructure and mechanical properties of supersonic plasma-sprayed Ni-based alloy coatings.Appl Surf Sci 2008;254:6318-26.

    [14]Zhang XC,Xu BS,Xuan FZ,Wang HD,Wu YX.M icrostructural and porosity variations in the plasma-sprayed Ni-alloy coatings prepared at different spraying powers.JAlloys Comp 2009;473:145-51.

    [15]Liu SL,Zheng XP.Microstructure and propertiesof AC-HVAF sprayed Ni60/WC composite coating.JA lloys Comp 2009;480(2):254-8.

    [16]Wu YS,Zeng DC,Liu ZW,Qiu WQ,Zhong XC,Yu HY,et al.M icrostructure and sliding wear behaviour of nano structured Ni60-TiB2composite coating sprayed by HVOF technique.Surf Coat Technol 2011;206:1102-8.

    [17]Zhang XC,Xu BS,Xuan FZ,Wang HD,Wu YX.Porosity and effective mechanical properties of plasma-sprayed Ni-based alloy coatings.Appl Surf Sci2009;255:4362-71.

    [18]Lupoi R,Sparkes M,Cockburn A,O'Neill W.High speed titanium coatings by supersonic laser deposition.M ater Lett 2011;65:3205-7.

    [19]Damborenea Jde.Surfacemodification ofmetals by high power lasers. Surf Coat Technol 1998;123(100/101):377-82.

    [20]Li Q,Lei TC,Chen WZ.M icrostructural characterization of WCp reinforced Ni2Cr2B2Si2C composite coatings.Surf Coat Technol 1999;114(223):285-91.

    [21]Przybylow icz J,Kusinski J.Structure of laser cladded tungsten carbide composite coatings.M ater Proc Technol 2001;109(122):154-60.

    [22]Vilar R.Laser cladding.JLaser Appl 1999;11(2):64.

    [23]Wang JY,Wang HC,Wang HF,Zeng ZQ.Preparation of Ni60-WC coating by plasma spraying,plasma re-melting and plasma spray welding on surface of hot forging die.J Wuhan Univ Tech Mater 2012;27(4):640-3.

    [24]Amado JM,TobarMJ,Alvarez JC,Lamas J,Y'a~nez A.Laser cladding of tungsten carbides(Spherotene?)hardfacing alloys for the mining and mineral industry.Appl Surf Sci2009;255:5553-6.

    [25]Chen HH,Xu CY,Chen J,Zhao HY,Zhang L,Wang ZT.M icrostructure and phase transformation of WC/Ni60B laser cladding coatings during dry sliding wear.Wear 2008;264:487-93.

    .Tel.:+86 13867418595.

    **Corresponding author.Tel.:+44(0)1223 332786.

    E-mail addresses:luofang@zjut.edu.cn(F.LUO),m rs46@cam.ac.uk(M. SPARKES).

    Peer review under responsibility of China Ordnance Society.

    http://dx.doi.org/10.1016/j.dt.2014.09.003

    2214-9147/Copyright?2014,China Ordnance Society.Production and hosting by Elsevier B.V.All rights reserved.

    Copyright?2014,China Ordnance Society.Production and hosting by Elsevier B.V.A ll rights reserved.

    美女国产视频在线观看| 男女边吃奶边做爰视频| 国产黄片视频在线免费观看| 国产精品一二三区在线看| 久久久久久久亚洲中文字幕| 人人妻人人澡人人爽人人夜夜 | 国产欧美另类精品又又久久亚洲欧美| 91久久精品国产一区二区成人| 少妇人妻精品综合一区二区| 美女被艹到高潮喷水动态| 国产精品不卡视频一区二区| 亚洲精品自拍成人| 天堂√8在线中文| 一区二区三区免费毛片| 免费黄网站久久成人精品| 国产午夜精品论理片| 久久久久久九九精品二区国产| 国产精品国产三级国产av玫瑰| 91精品伊人久久大香线蕉| 亚洲精品中文字幕在线视频 | 国产 亚洲一区二区三区 | 搡老妇女老女人老熟妇| a级毛色黄片| 少妇的逼水好多| 亚洲欧美一区二区三区黑人 | 久久久久久久亚洲中文字幕| 在线天堂最新版资源| 亚洲国产av新网站| 久久韩国三级中文字幕| 精品亚洲乱码少妇综合久久| 熟女电影av网| xxx大片免费视频| 亚洲国产最新在线播放| 十八禁国产超污无遮挡网站| 精品一区二区三区人妻视频| 色哟哟·www| 久久久色成人| 国产伦精品一区二区三区四那| 免费观看在线日韩| 最近最新中文字幕免费大全7| 一级av片app| 国产伦理片在线播放av一区| 日韩中字成人| 嫩草影院入口| av在线老鸭窝| 欧美不卡视频在线免费观看| 国产伦精品一区二区三区视频9| 国产免费视频播放在线视频 | 七月丁香在线播放| 亚洲av免费高清在线观看| 亚洲av在线观看美女高潮| www.av在线官网国产| 欧美日韩在线观看h| 听说在线观看完整版免费高清| 国产亚洲精品久久久com| av黄色大香蕉| 欧美日韩综合久久久久久| 精品国产三级普通话版| 插阴视频在线观看视频| 日日啪夜夜爽| 国产精品蜜桃在线观看| 美女主播在线视频| 99久久精品热视频| 日本一二三区视频观看| 美女被艹到高潮喷水动态| 成人毛片a级毛片在线播放| 国产男人的电影天堂91| 在线免费十八禁| 中文字幕久久专区| 日韩一本色道免费dvd| 国产精品日韩av在线免费观看| 国产人妻一区二区三区在| 啦啦啦韩国在线观看视频| 边亲边吃奶的免费视频| 最近视频中文字幕2019在线8| 秋霞在线观看毛片| 成人高潮视频无遮挡免费网站| 精华霜和精华液先用哪个| 天美传媒精品一区二区| 亚洲av在线观看美女高潮| 色网站视频免费| 久久久久久久久大av| 午夜老司机福利剧场| 午夜久久久久精精品| 99视频精品全部免费 在线| 一级毛片 在线播放| 亚洲va在线va天堂va国产| 最近最新中文字幕大全电影3| 永久网站在线| 嫩草影院精品99| 亚洲一区高清亚洲精品| 成人高潮视频无遮挡免费网站| 精品国产三级普通话版| 国产片特级美女逼逼视频| 啦啦啦韩国在线观看视频| 男女边摸边吃奶| 久久久精品欧美日韩精品| 青春草国产在线视频| 99re6热这里在线精品视频| 国产真实伦视频高清在线观看| 最近中文字幕高清免费大全6| 内地一区二区视频在线| 身体一侧抽搐| 丰满乱子伦码专区| 亚洲国产成人一精品久久久| 美女脱内裤让男人舔精品视频| 97超视频在线观看视频| 国产精品久久久久久精品电影小说 | 亚洲av男天堂| 熟女人妻精品中文字幕| 成人午夜精彩视频在线观看| 欧美日韩精品成人综合77777| 性插视频无遮挡在线免费观看| 久久久久久久久久久丰满| 国产av码专区亚洲av| 国产一区亚洲一区在线观看| 亚洲欧美一区二区三区国产| 九草在线视频观看| 五月玫瑰六月丁香| 日本黄色片子视频| 成人亚洲欧美一区二区av| 亚洲精品乱久久久久久| 国产精品久久久久久精品电影小说 | 三级毛片av免费| 欧美日本视频| 热99在线观看视频| 国产人妻一区二区三区在| 午夜免费男女啪啪视频观看| 免费高清在线观看视频在线观看| av卡一久久| 观看免费一级毛片| 2022亚洲国产成人精品| 国产黄色小视频在线观看| 亚洲人成网站在线播| 国产毛片a区久久久久| 国产精品久久久久久精品电影| 国产亚洲av嫩草精品影院| 成人欧美大片| 国产精品日韩av在线免费观看| 成人二区视频| 成年女人看的毛片在线观看| 久久综合国产亚洲精品| 十八禁国产超污无遮挡网站| 亚洲欧美日韩无卡精品| 国内精品宾馆在线| 久久精品国产亚洲av涩爱| 成人国产麻豆网| 久久久色成人| 久久久久国产网址| 少妇的逼好多水| 少妇人妻精品综合一区二区| 看免费成人av毛片| 亚洲自偷自拍三级| 韩国高清视频一区二区三区| 成人亚洲欧美一区二区av| 一边亲一边摸免费视频| 青春草国产在线视频| 免费大片黄手机在线观看| 亚洲综合色惰| 国产视频内射| 一级毛片黄色毛片免费观看视频| 观看美女的网站| 女的被弄到高潮叫床怎么办| 亚洲欧美精品自产自拍| 欧美日韩视频高清一区二区三区二| 欧美高清性xxxxhd video| 国产精品一区二区性色av| 色综合站精品国产| 91精品国产九色| 岛国毛片在线播放| 国产一区二区亚洲精品在线观看| 狠狠精品人妻久久久久久综合| 国产熟女欧美一区二区| 日本爱情动作片www.在线观看| 乱码一卡2卡4卡精品| 精品人妻偷拍中文字幕| 深夜a级毛片| 一二三四中文在线观看免费高清| av专区在线播放| 深夜a级毛片| 国产亚洲av嫩草精品影院| 日韩成人伦理影院| 亚洲精品乱久久久久久| 女的被弄到高潮叫床怎么办| 国内少妇人妻偷人精品xxx网站| 国产精品女同一区二区软件| 99热这里只有是精品50| 久久久午夜欧美精品| 69av精品久久久久久| 男女那种视频在线观看| 少妇丰满av| 精品欧美国产一区二区三| 久久久欧美国产精品| 亚洲欧美成人综合另类久久久| 男人和女人高潮做爰伦理| 中文资源天堂在线| 亚洲av福利一区| 久久人人爽人人片av| 国产成人一区二区在线| 久久久国产一区二区| 一级黄片播放器| 成人午夜精彩视频在线观看| 精品国产一区二区三区久久久樱花 | 亚洲精品日本国产第一区| 欧美潮喷喷水| 久久99精品国语久久久| 一本一本综合久久| 日韩国内少妇激情av| 国产男人的电影天堂91| 日日啪夜夜爽| 看非洲黑人一级黄片| 亚洲四区av| 高清视频免费观看一区二区 | 看黄色毛片网站| 又大又黄又爽视频免费| 三级国产精品片| 一级毛片黄色毛片免费观看视频| 亚洲国产精品成人综合色| 大又大粗又爽又黄少妇毛片口| 亚洲熟女精品中文字幕| 亚洲欧美一区二区三区国产| 午夜福利在线观看免费完整高清在| 国产精品精品国产色婷婷| 丝瓜视频免费看黄片| 1000部很黄的大片| 大片免费播放器 马上看| 人人妻人人看人人澡| 日韩不卡一区二区三区视频在线| 建设人人有责人人尽责人人享有的 | 国产高清国产精品国产三级 | 精品人妻熟女av久视频| 久久久久国产网址| 深爱激情五月婷婷| 中文字幕久久专区| 丰满人妻一区二区三区视频av| 国产精品一二三区在线看| 免费观看在线日韩| 午夜福利在线观看吧| 天堂av国产一区二区熟女人妻| 日本色播在线视频| 熟女人妻精品中文字幕| 国产av码专区亚洲av| 日本av手机在线免费观看| 成人综合一区亚洲| 色综合亚洲欧美另类图片| a级毛色黄片| 身体一侧抽搐| 色播亚洲综合网| 久久这里有精品视频免费| 亚洲伊人久久精品综合| 女的被弄到高潮叫床怎么办| av播播在线观看一区| 2021少妇久久久久久久久久久| av在线亚洲专区| 欧美精品国产亚洲| videos熟女内射| 人人妻人人澡欧美一区二区| 亚洲欧美中文字幕日韩二区| 一级毛片黄色毛片免费观看视频| 久久99热这里只频精品6学生| 可以在线观看毛片的网站| 热99在线观看视频| 国产精品蜜桃在线观看| 自拍偷自拍亚洲精品老妇| 日本欧美国产在线视频| 国产精品1区2区在线观看.| 97在线视频观看| 高清在线视频一区二区三区| 97人妻精品一区二区三区麻豆| 亚洲国产色片| 肉色欧美久久久久久久蜜桃 | 精品久久久久久成人av| 神马国产精品三级电影在线观看| 国产精品熟女久久久久浪| 99久久九九国产精品国产免费| 亚洲最大成人av| 男女那种视频在线观看| 99久久中文字幕三级久久日本| 国产精品伦人一区二区| 国产精品无大码| 日韩 亚洲 欧美在线| 高清午夜精品一区二区三区| 亚洲国产最新在线播放| 看十八女毛片水多多多| 69人妻影院| 午夜视频国产福利| 国国产精品蜜臀av免费| 国产日韩欧美在线精品| 亚洲一级一片aⅴ在线观看| 极品教师在线视频| 哪个播放器可以免费观看大片| 亚洲成人久久爱视频| 波野结衣二区三区在线| 亚洲aⅴ乱码一区二区在线播放| 亚洲精品一二三| 777米奇影视久久| 亚洲不卡免费看| 少妇人妻一区二区三区视频| 99热全是精品| 国产精品国产三级专区第一集| 男人和女人高潮做爰伦理| 久久久久久久久久人人人人人人| 69av精品久久久久久| 高清视频免费观看一区二区 | 看十八女毛片水多多多| 一二三四中文在线观看免费高清| 大香蕉久久网| 啦啦啦中文免费视频观看日本| 欧美变态另类bdsm刘玥| 男女国产视频网站| 久久久欧美国产精品| 亚洲内射少妇av| 日本一本二区三区精品| 国产一区亚洲一区在线观看| 国产日韩欧美在线精品| 亚洲av成人av| 午夜精品一区二区三区免费看| 亚洲欧美成人综合另类久久久| 亚洲成人一二三区av| 男女啪啪激烈高潮av片| 精品人妻熟女av久视频| 久久久亚洲精品成人影院| 国产亚洲精品久久久com| av福利片在线观看| 午夜福利视频精品| 不卡视频在线观看欧美| 18禁在线播放成人免费| 久久久久久久久久成人| 国产综合精华液| 免费av观看视频| 日韩在线高清观看一区二区三区| 国产一区二区亚洲精品在线观看| 国产激情偷乱视频一区二区| 高清av免费在线| 丝袜喷水一区| 国产精品国产三级国产av玫瑰| 伊人久久国产一区二区| 婷婷色综合大香蕉| 特大巨黑吊av在线直播| 美女主播在线视频| 免费黄网站久久成人精品| 婷婷色综合大香蕉| 亚洲人成网站在线播| 五月伊人婷婷丁香| 内地一区二区视频在线| 美女国产视频在线观看| av在线老鸭窝| 天堂√8在线中文| 午夜精品一区二区三区免费看| 亚洲精品色激情综合| 精品人妻一区二区三区麻豆| 国产精品国产三级国产av玫瑰| 丝瓜视频免费看黄片| 久久久久精品久久久久真实原创| 极品教师在线视频| 亚洲av成人精品一二三区| 如何舔出高潮| 久久精品国产自在天天线| 晚上一个人看的免费电影| 婷婷色综合大香蕉| 久久精品国产亚洲av天美| 国产不卡一卡二| 亚洲精品第二区| 免费大片黄手机在线观看| 亚洲一级一片aⅴ在线观看| 国产视频内射| 亚洲乱码一区二区免费版| 秋霞在线观看毛片| 国产精品无大码| 婷婷色av中文字幕| 五月伊人婷婷丁香| 日本三级黄在线观看| 久久精品夜夜夜夜夜久久蜜豆| 晚上一个人看的免费电影| 黄片wwwwww| 欧美日韩亚洲高清精品| 久久精品久久久久久噜噜老黄| 国产精品蜜桃在线观看| 99久久精品热视频| 国产精品麻豆人妻色哟哟久久 | 丝袜喷水一区| 久久国产乱子免费精品| 99久国产av精品国产电影| 伊人久久精品亚洲午夜| 在线观看美女被高潮喷水网站| 搞女人的毛片| 女人十人毛片免费观看3o分钟| 国产探花极品一区二区| 午夜福利视频精品| 一级毛片黄色毛片免费观看视频| 精品一区二区三区视频在线| 男人舔奶头视频| 少妇熟女欧美另类| 亚洲自拍偷在线| 极品教师在线视频| 国产成人91sexporn| 伊人久久国产一区二区| 国产男人的电影天堂91| 夜夜爽夜夜爽视频| 菩萨蛮人人尽说江南好唐韦庄| 三级毛片av免费| 老司机影院毛片| 久久99热这里只频精品6学生| www.av在线官网国产| 天天躁日日操中文字幕| 成年女人看的毛片在线观看| 国产美女午夜福利| 人人妻人人澡欧美一区二区| 亚洲av电影不卡..在线观看| 七月丁香在线播放| 可以在线观看毛片的网站| 91久久精品国产一区二区三区| 国产成人午夜福利电影在线观看| 国产黄色小视频在线观看| 精品酒店卫生间| av国产久精品久网站免费入址| 最近中文字幕2019免费版| 久久久久九九精品影院| 成人毛片60女人毛片免费| 成人性生交大片免费视频hd| 日日啪夜夜撸| 91精品国产九色| 国产精品av视频在线免费观看| av黄色大香蕉| 床上黄色一级片| 亚洲精品一二三| 嫩草影院新地址| .国产精品久久| 插阴视频在线观看视频| 亚洲精品aⅴ在线观看| 水蜜桃什么品种好| 街头女战士在线观看网站| 免费看日本二区| 九九久久精品国产亚洲av麻豆| 中文字幕人妻熟人妻熟丝袜美| 在线免费观看的www视频| 欧美潮喷喷水| 一个人免费在线观看电影| 成年版毛片免费区| 最后的刺客免费高清国语| 我的老师免费观看完整版| 国产美女午夜福利| av免费观看日本| 亚洲精品一区蜜桃| 国产 亚洲一区二区三区 | 男女那种视频在线观看| 亚洲精品国产成人久久av| 内射极品少妇av片p| 欧美zozozo另类| 成人亚洲欧美一区二区av| 国产老妇伦熟女老妇高清| 日产精品乱码卡一卡2卡三| 干丝袜人妻中文字幕| 久久这里只有精品中国| 一级爰片在线观看| 国产视频首页在线观看| 精品酒店卫生间| 禁无遮挡网站| 亚洲精品亚洲一区二区| 嘟嘟电影网在线观看| 国产精品久久久久久精品电影| 中文字幕久久专区| 综合色丁香网| 夜夜爽夜夜爽视频| 国产一区二区亚洲精品在线观看| 日韩国内少妇激情av| 丰满少妇做爰视频| 久久久久久九九精品二区国产| 国产69精品久久久久777片| 日韩伦理黄色片| 中文字幕人妻熟人妻熟丝袜美| 一级片'在线观看视频| 亚洲人成网站在线观看播放| 69人妻影院| 熟女电影av网| 久久精品国产亚洲网站| 又大又黄又爽视频免费| 国产探花在线观看一区二区| 天美传媒精品一区二区| 肉色欧美久久久久久久蜜桃 | 亚洲无线观看免费| 国模一区二区三区四区视频| 日韩一本色道免费dvd| 蜜桃亚洲精品一区二区三区| 美女黄网站色视频| 日韩成人伦理影院| 亚洲国产最新在线播放| 天天躁夜夜躁狠狠久久av| 国产v大片淫在线免费观看| www.色视频.com| 日韩电影二区| av在线播放精品| 肉色欧美久久久久久久蜜桃 | 伦精品一区二区三区| 国模一区二区三区四区视频| 久久热精品热| 成年av动漫网址| 一级片'在线观看视频| 欧美激情国产日韩精品一区| 性插视频无遮挡在线免费观看| 纵有疾风起免费观看全集完整版 | av网站免费在线观看视频 | 亚洲精品亚洲一区二区| 亚洲美女搞黄在线观看| 国产国拍精品亚洲av在线观看| 特级一级黄色大片| 插阴视频在线观看视频| 亚洲精品,欧美精品| 欧美成人午夜免费资源| 国产黄a三级三级三级人| 精品少妇黑人巨大在线播放| 99久国产av精品国产电影| 亚洲自拍偷在线| 久久久a久久爽久久v久久| 听说在线观看完整版免费高清| av天堂中文字幕网| 国产美女午夜福利| 日本wwww免费看| 波多野结衣巨乳人妻| 女人十人毛片免费观看3o分钟| 国产精品一区二区性色av| 一级av片app| 五月玫瑰六月丁香| 伊人久久精品亚洲午夜| 五月天丁香电影| 免费观看a级毛片全部| 男女那种视频在线观看| 观看美女的网站| 国产一级毛片七仙女欲春2| 超碰97精品在线观看| 国产成年人精品一区二区| 亚洲国产日韩欧美精品在线观看| 国产精品久久视频播放| 男女边摸边吃奶| av线在线观看网站| 国产成人91sexporn| 欧美变态另类bdsm刘玥| av国产久精品久网站免费入址| 婷婷色麻豆天堂久久| 亚洲美女搞黄在线观看| 亚洲精品国产成人久久av| 三级男女做爰猛烈吃奶摸视频| 日韩 亚洲 欧美在线| 亚洲欧美成人综合另类久久久| 成人午夜精彩视频在线观看| 国产精品久久视频播放| 国产永久视频网站| 成年av动漫网址| 久久久精品94久久精品| 三级经典国产精品| 亚洲人与动物交配视频| www.色视频.com| 日日摸夜夜添夜夜添av毛片| 国产亚洲av嫩草精品影院| 亚洲精品日韩av片在线观看| 国产日韩欧美在线精品| 久久6这里有精品| 亚洲精品aⅴ在线观看| 成年av动漫网址| 国产亚洲最大av| 欧美最新免费一区二区三区| 99热这里只有是精品在线观看| 在线免费观看的www视频| 不卡视频在线观看欧美| 成人av在线播放网站| 婷婷六月久久综合丁香| 国产亚洲精品av在线| 18禁裸乳无遮挡免费网站照片| 国产亚洲5aaaaa淫片| 国产亚洲av片在线观看秒播厂 | 男女那种视频在线观看| 最近中文字幕高清免费大全6| 一区二区三区高清视频在线| av线在线观看网站| 深爱激情五月婷婷| 麻豆久久精品国产亚洲av| 欧美 日韩 精品 国产| 一级a做视频免费观看| 欧美最新免费一区二区三区| 天堂俺去俺来也www色官网 | 别揉我奶头 嗯啊视频| 青春草亚洲视频在线观看| av.在线天堂| 欧美日韩亚洲高清精品| 激情五月婷婷亚洲| 亚洲国产高清在线一区二区三| 特大巨黑吊av在线直播| 男女国产视频网站| 亚洲电影在线观看av| 久久草成人影院| 国国产精品蜜臀av免费| 国产熟女欧美一区二区| 特大巨黑吊av在线直播| av一本久久久久| 欧美日韩一区二区视频在线观看视频在线 | 美女cb高潮喷水在线观看| 深夜a级毛片| 80岁老熟妇乱子伦牲交| 最近手机中文字幕大全| 看非洲黑人一级黄片| 亚洲精品一二三| 在线 av 中文字幕| 久久久成人免费电影| av在线亚洲专区| 久久久久精品性色| 九九久久精品国产亚洲av麻豆| 麻豆成人av视频| 精品一区二区三区视频在线| 亚洲国产精品专区欧美| 日韩国内少妇激情av| 在线免费观看不下载黄p国产| 97超视频在线观看视频| 国产精品.久久久| 美女高潮的动态| 国产一区二区亚洲精品在线观看|