    Effect of AMPS(2-acrylamido-2-methylpropane sulfonic acid) content on the properties of polymer gels

    2022-06-02 05:00:28TinCiZhngJiJingGeHoWuHongBinGuoBoLeiJioZhenQin
    Petroleum Science 2022年2期

    Tin-Ci Zhng ,Ji-Jing Ge ,*,Ho Wu ,Hong-Bin Guo ,Bo-Lei Jio ,Zhen Qin

    a School of Petroleum Engineering,China University of Petroleum (East China),Qingdao,266580,Shandong,China

    b Petroleum Engineering Institute,Northwest Branch of Sinopec,Urumqi,830011,Xinjiang,China

    Keywords:Gels 2-Acrylamido-2-methylpropane sulfonic acid Enhanced oil recovery Hydrolysis Syneresis

    ABSTRACT The BST oilfield in the northwestern Taklamakan Desert is a fractured carbonate reservoir,but issues of water breakthrough are becoming increasingly severe with the development of water flooding.Unfortunately,the high-temperature and high-salt conditions (130 °C,71695 mg/L) of the BST oilfield pose challenges for the development of plugging agents.In this study,the effects of 2-acrylamido-2-methylpropane sulfonic acid (AMPS) content on AM/AMPS copolymers and gels were studied through viscosity measurements,nuclear magnetic resonance (NMR),and cryo-scanning electron microscope(Cryo-SEM).Moreover,the AMPS stabilization mechanism of the polymers and gels was explained.Heatresistant and salt-tolerant gel systems were developed,and their gelation properties,thermal stability,injection capacity,and plugging ability were evaluated.Experimental results showed inconsistencies between the effects of AMPS content on the polymers and gels.For the polymers,the thermal stability increased with increased AMPS content in the polymer.However,excessive AMPS content resulted in poor gelation and low strength.The developed gel systems with S30 polymer (AMPS content is approximately 26%) exhibited excellent thermal stability,controllable gelation time,good injection capacity,and plugging ability.The field application results indicated that most production wells had a positive response,with reduced water-cut and increased daily oil production.

    1.Introduction

    Water flooding is a widely used technique to enhance oil recovery and improve oil production rate (Li et al.,2021).However,permeability heterogeneity,gravity segregation,and viscous fingering are the cause of poor sweep efficiency during water flooding (Sie and Nguyen,2021;Seright and Brattekas,2021).Water channeling can also occur after decades of water flooding,leading to earlier water breakthrough,increased water cut,reduced oil recovery,and increased water handling costs.

    Researchers have employed many technologies to reduce water production and improve water displacement recovery,such as polymer flooding (Jouenne,2020;Kang et al.,2015),surfactant flooding (Mohamed et al.,2018;Almahfood and Bai,2021),foam flooding(Zhao et al.,2009;Hu et al.,2020),and gels(Ge et al.,2021;Sun et al.,2020;Elsharafi and Bai,2016).One of the most pervasive technologies is the use of polymer gels due to their low cost,extended shelf life,and simple operation.Under high-temperature and high-salt conditions,polymer gels have better thermal stability and plugging ability.Moradi et al.(1993) developed a gel system consisting of an acrylamide (AM) polymer,formaldehyde,and phenol,which survived 2.5 years of aging at 113°C(or 9 months of aging at 149°C).Dovan et al.(1997) investigated the effects of organic cross-linkers on polymer gels and found that a gel prepared with a polymer,hexamethylenetetramine (HMTA),and hydroquinone (HQ) had excellent thermal stability and a controllable gelation time even under high-temperature conditions.Lashari et al.(2018) prepared a thermally stable gel with PADC,HMTA,and resorcinol,which was stable for 90 days under high-temperature(100°C) and high-salt (51984 mg/L) conditions Liu et al.(2020)also developed a heat-resistant gel that contained a copolymer,bisphenol-A,and HMTA,and displacement experiments showed the plugging ratio of the gel exceeded 95%.

    Phenolic compounds and aldehyde compounds can be employed as cross-linkers to prepare polymer gels for hightemperature and high-salt conditions.In addition to the crosslinkers,the polymers are also vital gel components.However,HPAM polymers undergo hydrolysis,forming acrylate groups under high-temperature conditions(Seright,2010),and the complexation of the acrylate groups and divalent cations causes over-crosslinking and syneresis (Zhang et al.,2015).As a result,the processing method is critical for developing heat-resistant and salt-tolerant gels and improving the stability of the polymer.Numri et al.(2018) found that the introduction of 2-acrylamido-2-methylpropane sulfonic acid (AMPS) inhibits AM hydrolysis and improves polymer resistance to temperature and salt.Moreover,AM/AMPS copolymer gel systems had been prepared,which exhibited excellent stability under high-temperature and high-salt conditions.Albonico and Lockhart (1993) developed a gel system containing a PAAm/AMPS copolymer,HMTA,and phenol,and the system was stable for 150 days at 120°C.Unomah et al.(2018)also investigated the effect of polymer type on gels and found that gels prepared with AM/AMPS copolymers had the best thermal stability.Zhu et al.(2017)also prepared a thermally stable gel containing an AM/AMPS/NVP copolymer,HMTA,and resorcinol,and the gel was stable for 5 months at 150°C.

    Although some heat-resistant and salt-tolerant gel systems have been developed with an AM/AMPS copolymer,phenolic compounds,and aldehyde cross-linkers,the influence and stabilization mechanisms of AMPS are not clear.Thus,this research investigated the properties of gels prepared with different AM/AMPS copolymers through viscosity measurements,nuclear magnetic resonance (NMR),and cryo-scanning electron microscope (Cryo-SEM).The mechanisms of AMPS polymer and gel stabilization were explained,and a suitable gel system for use in the BST oilfield(130°C,71695 mg/L) was developed.

    2.Materials and methods

    2.1.Materials

    Four polymers used in this study were provided by Qingdao Golden Brick Technology Co.,Ltd,the chemical structure of polymers was identified with a NMR spectrometer and their AMPS percent ratios were determined by the elemental analysis method(see in the supplemental material).The details of the four polymers are listed in Table 1 (the molecular weight refers to the viscosity average molecular weight).Hexamethylenetetramine (HMTA) and hydroquinone (HQ) were employed as cross-linkers,which were purchased from Shanghai Aladdin Biochemical Technology Co.,Ltd.Thiourea (TH) was used as an antioxidant,which was purchased from Sinopharm Chemical Reagent Co.,Ltd.Synthetic brine was used to simulate the high-salt conditions of the BST oilfield,and the brine composition is shown in Table 2.

    Table 1Polymer properties.

    Table 2Ion composition of BST formed brine.

    2.2.Methods

    2.2.1.Gelling solution preparation

    First,2 wt% polymer stock solution was prepared according to the following procedures.First,(1) a container with a known amount of brine was vigorously stirred to create a deep vortex,then(2) the polymer was slowly added to the shoulder of the vortex toeffectively wet the polymer beads,and finally(3)the container was sealed to minimize evaporation and was continuously stirred for 24 h to ensure complete dissolution of the polymer (Zhang et al.,2015).Then,pre-weighted TH,HMTA,and HQ were diluted into the brine,and the gelling solution was obtained by mixing the previously obtained brine solution and polymer stock solution.Finally,20 g of prepared gelling solution was transferred into an ampoule,which was placed in an oven (130°C) to initiate crosslinking.

    2.2.2.Gelation time measurements

    Gelation time is an important index that is closely related to operational safety.Sydansk (1990) proposed a method for characterizing the qualitative gel strength (gel strength code method),where the strength of the gel was classified into 10 grades(A-J).In this study,the gels were removed periodically from the oven at set intervals,and the gel strength was determined according to the gel strength code method.Finally,the gelation time was defined as the strength of the gel when it reached grade “F”.

    2.2.3.Viscosity and elastic modulus measurements

    The thermal stability of the polymers was characterized by the viscosity retention over aging time.First,polymer solutions were prepared at 0.6 wt% concentration,then polymer solutions were placed into the oven (130°C),finally the polymer solutions were taken from the oven and the viscosity was measured with an Anton Paar MCR 92 rheometer equipped with a cup &nob setup (CC39),and the measurement time was 5 min.The viscosity retention can be defined by the following expression:

    where Rvis the viscosity retention,η1is the viscosity of the polymer solution after heat treatment,and η0is the initial viscosity.

    The gel strength was characterized by quantifying the elastic modulus,which was measured with an Anton Paar MCR 92 rheometer equipped with a 25-mm parallel plate (PP25).For the elastic modulus measurements,the strain range was set to 1%-500% and the frequency was fixed at 10 rad/s.All the rheological experiments were done at 25°C.

    2.2.4.Syneresis rate measurements

    To evaluate the thermal stability of the gels,the syneresis rate should be measured during gel heat treatment.The syneresis rate can be defined by the following expression:

    where Rsis the syneresis rate of the gels,m1is the weight of the water expelled from the gel after aging,and m0is the weight of the gelling solution (20 g in this study).

    2.2.5.Cryo-SEM measurements

    The gel microstructure was observed by Cryo-SEM,and the samples were prepared according to the following steps.First,(1)the bulk gel was frozen in liquid nitrogen (-160°C),then (2) the water in the gel was sublimed by reducing the pressure,and finally(3) the pre-frozen dried gel was placed onto the conductive adhesive,and the gel surface was sprayed with gold.The gel microstructure was then observed using a scanning electron microscope(SEM,Hitachi SU8010).

    2.2.6.NMR measurements

    A solid-state NMR sample was first prepared,as gels prepared in the brine (71695 mg/L) solution contained large quantities of inorganic salt,which was removed to prevent any adverse effects on the NMR test.However,dehydration cannot occur under hightemperature conditions,as these conditions can accelerate the hydrolysis of the amide group.Therefore,a solvent extraction method was adopted in this study to remove the inorganic salt and water from the bulk gel,according to the following steps.First,(1)the bulk gels were immersed in deionized water 7-10 times(4 h at a time)to remove the salt,next(2)the bulk gels were immersed in ethanol 4-6 times (4 h at a time) to remove water from the gels,and then (3) the bulk gels were placed in a vacuum drying oven(60°C) for 10 h to remove the ethanol.Afterward,the solid-state NMR sample was prepared by grinding the dried bulk gel into a powder.Finally,13C NMR tests were conducted at 400 MHz using a WB solid-state NMR spectrometer.In the solid-state NMR test,the rotation frequency was 3 kHz,the recycle delay was 3 s,the number of increments was set to 10,000,and a CPTOSS impulse sequence was used.

    2.2.7.Flooding test

    The plugging ability of the gel was characterized via a breakthrough pressure gradient,which was measured by a flooding test.The following methods were employed.First,(1) the flooding experiment setup was built according to Fig.1,then(2)the gelling solution was injected into a thin metal tube,the thin metal tube was employed to simulate reservoir fracture,with length of 50 cm,and the inner diameters ranging from 0.8 mm to 1.6 mm,next (3)thin tubes containing gelling solution were sealed and placed into an oven(130°C),then(4)the thin tube was placed in the flooding experiment setup,and the brine was injected into the thin tube,while the pressure along the thin tube was recorded,and finally(5)the breakthrough pressure was defined as the pressure when brine drained from the end of the thin tube.The breakthrough pressure gradient was calculated by dividing the breakthrough pressure by the length of the thin tube.

    3.Results and discussion

    3.1.Polymer screening

    Polymers are essential components of gelling systems,and they significantly affect the gel performance.In this section,thermal stability,gelation properties,and gel strength were measured to obtain a suitable polymer.

    3.1.1.Thermal stability of polymers

    Hydrolysis reactions occur under high-temperature conditions(>75°C),converting AM groups into acrylic acid(AA)and reducing the viscosity of polymer solutions,which is detrimental to gel properties.In this study,the viscosity retention rates of several polymers were adopt to evaluate thermal stability.The mass fraction of the polymer was set to 0.6 wt%,and TH(0.3 wt%)was used as the antioxidant,to prevent oxidative degradation.The viscosity changes of the four polymer types are shown in Fig.2.We found that the viscosity of all the polymers decreased as the aging time increased.However,polymers with more AMPS had a more gradual loss in viscosity compared to polymers with less AMPS.Thus,polymers with higher amounts of AMPS exhibited better stability under high-temperature and high-salt conditions,which was consistent with previous research (Nurmi et al.,2018).The previously described phenomenon occurred due to two reasons:(1)the AMPS group had stronger thermostability than the AM group,and(2) the hydrolysis of the AM group was inhibited by the neighboring AMPS group due to steric and electrostatic repulsion effects.Thus,polymers containing higher amounts of AMPS retain higher thermal stability,which may be best suited for use in developing heat-resistant and salt-tolerant gels.

    3.1.2.Gelation properties

    To further determine polymer suitability,gelation time was assessed.The mass fraction of the polymer(poly)was set to 0.6 wt%,and HMTA and HQ were employed as cross-linkers (CL),with mass fractions between 0.05 wt%and 0.2 wt%.The gels(poly:0.6 wt%,CL:0.20 wt%) that were prepared with different polymers are shown in Fig.3,and these gels were aged for 30 days.We found that the strengths of the gels prepared with S00,S30,and S50 polymers reached grades“H”,“G”,“F”,respectively,but the strength of the gel prepared with S70 only reached grade “C”,indicating that the S70 polymer did not form a strong gel under the BSTconditions(130°C,71695 mg/L).

    Once I digested this insight my feelings changed from those of a needy19 child to ones of a very proud daughter. Looking at my father more objectively allowed me to view him clearly: he was a man of few words; he was intelligent, kind and extremely modest. Ironically I began to feel closer to him in death than I had while he was alive.

    Fig.4 shows the gelation time of the three gelling systems(not including the S70 polymer gel).The gelation time of three gel systems prepared with S00,S30,and S50 polymers were 10-50,21-70,and 24-120 h,respectively.Thus,the three polymer gel types met the field operation requirements.One interesting result was that gelation time increased as the AMPS content increased.One explanation for this phenomenon could be the electrostatic repulsion between the compounds.Sun et al.(2008)found that the cross-linker was negatively charged,and polymers containing AMPS groups were also negatively charged.So the crosslinking reaction was inhabited by the electrostatic repulsion between the AMPS group and cross-linker.Furthermore,the electrostatic repulsion was enhanced with increased AMPS content,thus the gel system containing the S50 polymer (with higher AMPS content)had a longer gelation time.Concerning the phenolic gels,the most suitable polymer was not the most stable one (with the highest AMPS content),polymers containing excessive amounts of AMPS may not form a gel.

    3.1.3.Gel strength

    Gel strength is a vital index related to plugging ability,and in this section,it was quantitatively characterized by elastic modulus.The mass fraction of the polymer (poly) was set to 0.6 wt%,and HMTA and HQ were employed as cross-linkers (CL) with a mass fraction of 0.10 wt%.The storage moduli of the three gelling systems(not including the S70 polymer) are shown in Fig.6.The S00 polymer gel had the highest elastic modulus,and the variations in elastic modulus with aging time were divided into three sections:the slow ascent stage,the plateau stage,and the abrupt ascent stage.It should be noted that the second abrupt ascent stage was induced by the syneresis of the gel,and the elastic modulus reached 50 Pa after 30 days of aging (marked in red in Fig.5),while the syneresis rate at this time was 35%.The plugging capability of a gel was reduced when the syneresis rate increased;therefore,although the gel containing the S00 polymer had the highest elastic modulus,this gel was not suitable for improving conformance.For the S50 polymer gel,the elastic modulus reached its maximum after 2 days of aging,then gradually decreased.The maximum elastic modulus was only about 5 Pa,which meant that the gel prepared with S50 did not have sufficiently strong plugging capabilities.For the S30 polymer gel,the elastic modulus increased with increased aging time and then remained almost constant (11 Pa).Moreover,the syneresis rate of the S30 polymer gel was nearly zero,and the gel had excellent thermal stability.Through a comparative analysis,the gel prepared with the S30 polymer exhibited excellent thermal stability and had a high elastic modulus.Thus,the S30 polymer was chosen for the development of a heat-resistant and salt-tolerant gel suitable for use in the BST oilfield.

    Fig.1.Schematic of the experimental flooding setup.

    Fig.2.The viscosity retention rates of the different polymer solutions (The initial viscosities of S00,S30,S50,S70 polymers are 98.35,108.47,60.84,and 73.12 mPa·s).

    Fig.3.Gels prepared with different polymers (after aging for 30 days).

    3.2.Development of the heat-resistant and salt-tolerant gel

    According to the above experimental results,the S30 polymer was selected for developing a suitable gel for use in the BST oilfield.In this section,gelation time,syneresis rate,injection capacity,and plugging capability were evaluated for the development of a heatresistant and salt-tolerant gel.

    Fig.4.Different polymers prepared as a function of gelation time.

    Fig.5.Elastic modulus of different gelling systems.

    3.2.1.Gelation time measurements

    Gelation time is a vital index for evaluating gelling systems,as gelation time that is too short will negatively affect deep profile control and operational safety.Additionally,the dilution effect may be more extreme when the gelation time is too long.As a result,there are optimal gelation time for gelling systems.In this section,the mass fraction of the polymer was between 0.40 wt%and 1.00 wt%,and the mass fraction of the cross-linker varied from 0.05 wt%to 0.40 wt%.The measured gelation time of the different gelling systems are shown in Fig.6,which indicated that gelation time decreased as the mass fraction of the polymer and cross-linkers increased.When the mass fraction of the polymer or cross-linkers increased,there were more polymer molecules or cross-linker molecules,which provided more crosslinking locations,thus the gelation time was shorter.Therefore,the gelation time of the S30 polymer gels ranged from 9 to 90 h,and the S30 polymer gels were considered suitable for profile control according to the industry standard (Q/SH1020 1493-2014).

    3.2.2.Syneresis rate measurements

    Fig.6.Contour plot of the gelation time of the S30 polymer gels.

    Polymers experience hydrolysis during formation,resulting in the destruction of the gel structure and final syneresis.The gel volume usually decreases after syneresis,and plugging capability is reduced.Thus,the syneresis rate is also an important index for evaluating gelling systems.In this study,the mass fraction of the polymer ranged from 0.40 wt%to 1.00 wt%,and the mass fraction of the cross-linker varied from 0.05 wt% to 0.40 wt%.The measured syneresis rates of the different gelling systems are shown in Fig.7,indicating that the syneresis rate decreased as the mass fractions of the polymer or cross-linker increased.This was the result of crosslinking density,and the gel strength increased when the mass fraction of the polymer or cross-linker increased,and eventually syneresis was inhibited.Thus,to achieve a thermally stable gel,the mass fraction of the polymer and cross-linker must exceed 0.60 wt%and 0.10 wt%,respectively.When the two aforementioned conditions were satisfied,the gel exhibited excellent thermal stability(the syneresis rate was lower than 25% after 180 days of aging).

    The injection capacity of a gel is an important parameter related to operational safety.The lower the injection capacity,the higher the injection pressure,and an injection pressure that is too high may result in formation fracturing and even operational accidents.In this section,the viscosity and injection pressure gradient of the gels were measured to evaluate injection capacity.In the flooding experiments,thin tubes (inner diameters of 0.8,1.2,and 1.6 mm)were used to simulate fracture,and the injection rate varied from 10 to 100 m/d.Based on the previous gelation time and syneresis rate results,three gelling systems were studied:(A) 0.6 wt% of S30+0.1 wt%of HMTA+0.1 wt%of HQ+0.3 wt%of TH,(B)1.0 wt%of S30+0.1 wt%of HMTA+0.1 wt%of HQ+0.3 wt%of TH,and(C)1.0 wt%of S30+0.4 wt%of HMTA+0.4 wt%of HQ+0.3 wt%of TH.Additionally,the viscosity and injection pressure gradient was measured at 90°C due to restricted experimental conditions.Fig.8 illustrates the viscosity curves of the gel systems at 90°C,which indicated that the gelling systems had lower viscosities.Even when the mass fraction of the polymer and cross-linker reached 1.0 wt%and 0.4 wt%,respectively,the viscosity was only 225.74 mPa·s (at the shear rate of 7.3 s-1).The injection pressure gradient is shown in Fig.9,indicating that the injection pressure gradients were generally low,and the maximum injection pressure gradient was only 10 kPa/m,demonstrating that the selected gelling systems had excellent injection capacities.

    Fig.7.The syneresis rates of the different gelling systems.

    Fig.8.The viscosity curves for the different gelling systems.

    3.2.4.Plugging capability measurements

    Fig.9.The injection pressure gradients of the different gelling systems.

    The breakthrough pressure gradient is a direct manifestation of the plugging capability of a gel.In this section,the experimental parameters(thin tubes and gelling systems)were identical to those described in Section 3.2.3.The breakthrough pressure gradients of the gels at different water injection rates are shown in Fig.10,indicating that the breakthrough pressure gradient decreased with an increase in the water injection rate and increased inner diameter of the tube,which was consistent with previous research(Ganguly,2009).Moreover,the breakthrough pressure gradient increased with increased polymer and cross-linker concentrations,and the maximum breakthrough pressure gradient reached approximately 3 MPa/m,thus the gels prepared with the S30 polymer exhibited excellent plugging capabilities.

    Fig.10.Breakthrough pressure gradients of different gelling systems.

    3.3.Stabilization mechanisms of the AMPS group

    Hydrolysis of the AM group occurs under high-temperature conditions,generating an AA group that can complex with divalent cations(such as Ca2+).The complexation reaction can improve crosslinking density,which reduces the hydrophilicity of the gels and ultimately leads to syneresis.Based on the aforementioned experimental results,gels prepared with the S30 and S50 polymers(high AMPS content)exhibited better thermal stability than the S00 polymer(low AMPS content).The13C NMR results of three polymer gel types are shown in Fig.11.The results showed that after aging for 5 days,there were no obvious amide peaks in the13C NMR spectrum for the S00 polymer gels,and almost all of the AM moieties experienced hydrolysis,forming AA moieties.For the S30 polymer gels,the peak at δ=176 ppm corresponded to the amide carbonyl carbon,and the peak at δ=187 ppm corresponded to the carboxyl carbonyl carbon.Thus,both AM and AA moieties were present in the S30 polymer gels after 5 days of aging.For the S50 polymer gels,there were no obvious carbonyl peaks in the13C NMR spectra,and hydrolysis of the AM group did not occur.When the aging duration was extended to 30 days,the proportion of AA moieties increased in the S30 polymer gels,indicating more hydrolysis reactions.In addition,the presence of a carboxyl peak in the13C NMR spectrum of the S50 polymer gels meant that the AM group began to hydrolyze after 30 days of aging.Therefore,based on these results,AMPS inhibited the hydrolysis of AM,which in turn improved the thermal stability of the gels.Moreover,the stabilization effect improved as the AMPS copolymer content increased.

    Fig.11.The 13C NMR results of three polymer gel types:(a) aging for 5 days;(b) aging for 30 days.The inserts represent the magnified signal between δ=150 ppm and δ=200 ppm.

    To visually investigate the stabilization effect of the AMPS group,the microstructure of three polymer gels was analyzed by SEM,as shown in Fig.12.In this section,the mass fractions of the polymer,cross-linker,and antioxidant were set to 0.6 wt%,0.1 wt%,and 0.3 wt%,respectively.As shown in the figure,the S30 and S50 polymer gels had stronger networks than the S00 polymer gel,and small holes were spread throughout the S00 polymer gel network.Besides,the network of the S00 polymer gel was denser compared with gels containing S30 and S50 polymer.This could be because the AA content of S00 polymer was higher than the S30 and S50 polymer after the heat treatment.Due to the increased crosslinking between carboxyl and Ca2+in the S00 polymer gel,the network of the gel was compressed.Thus,the stabilization effect of the AMPS group was observed microscopically.

    4.Field applications

    4.1.BST oilfield background

    The BST oilfield in the northwestern Taklamakan Desert is a fractured carbonate reservoir with edge and bottom water.The reservoir medium includes fracture and matrix media,where the mean porosity and permeability of the matrix are 10% and 12.89×10-3μm2,respectively,and the length and width of the fracture are 3-100 cm and 0.01-1.5 mm,respectively.The midpoint of the pay zone is 4763.19 m,the reservoir temperature is nearly 130°C,and the salinity of the formation brine is approximately 71695 mg/L.The B6H well group in the BST oilfield was selected for profile control treatment,and the B6H well group location is schematically illustrated in Fig.13.The production status of the B6H well group,as of March 2020,is summarized in Table 3,showing that the water content of most of the production wells exceeded 90%,and B3 even reached 97.95%.Thus,conformance improvement was critically needed for enhancing oil recovery in the BST oilfield.

    Table 3Production status of the B6H well group.

    Fig.12.SEM images of different gels after 30 days of aging:(a,d) S00;(b,e) S30;(c,f) S50.

    Fig.13.The schematic of the B6H well group.

    4.2.Field operations

    The polymer gel developed with S30 polymer had better thermal stability compared to S00 polymer gel,and higher gel strength compared to S50 polymer gel.So the S30 polymer gel was selected to conduct the profile control treatments.The field operations were conducted from April 29,2020,to May 3,2020.Fig.14 depicts the tubing pressure,casing pressure,and displacement during operation.The field operation went smoothly,and when 1230 m3of the gelling solution was injected into the formation,the maximum tubing pressure was only about 13 MPa.

    The majority of the production wells responded well after profile control treatment except T4 well.The production performance of the B6H well group(not including T4),is shown in Fig.15.The results indicated that most production wells performed well,exhibiting a decrease in water content and an increase in daily oil production.Taking B2 as an example,the water content decreased from 94.32% to 85.25%,and daily oil production increased from 1.35 t/d to 6.35 t/d.Moreover,the cumulative oil production of the B6H well group rose by 1651 tons as of March 2021,confirming that the developed gelling systems can be used for oilfield applications.

    5.Conclusions

    In this study,AMPS content had varying impacts on polymers and polymer gels.For polymers,the hydrolysis of the AM group was inhibited by AMPS due to steric and electrostatic repulsion effects,and thermal stability improved with increased AMPS content.For polymer gels,the effect of AMPS content was complex.When S00 polymer (without AMPS group) was selected,the developed gel showed poor thermal stability.When the AMPS content was too high,the crosslinking reaction between AM group and cross-linker was hampered due to the electrostatic repulsion,even the S70 polymer (AMPS content:68%) could not form a strong gel.When polymer contained moderate AMPS content,the developed gels showed excellent gelation properties,thermal stability,and strength.Our results showed that the heat-resistant and salttolerant gels fabricated with the S30 polymer (AMPS content:26%)were suitable for use in the BST oilfield(130°C,71695 mg/L).The developed gelling systems had excellent thermal stabilities(the syneresis rate after thermal treatment for 180 days was 0.6%-22.5%),controllable gelation time (9-50 h),good injection capacities (injection pressure gradient:0.228-9.638 kPa/m),and plugging abilities (breakthrough pressure gradient:0.718-3.285 MPa/m).Based upon the13C NMR results,AMPS inhibited the hydrolysis of the AM group,which in turn improved the thermal stability of the gels,and the stabilization effect was enhanced as the AMPS content of the copolymer increased.

    The polymer gel developed with S30 polymer had better thermal stability compared to S00 polymer gel,and higher gel strength compared to S50 polymer gel.So the S30 polymer gel was selectedto conduct the profile control treatments,and the results showed that the majority of the production wells responded well,with increased daily oil production and decreased water content.Moreover,the cumulative oil production of the B6H well group rose by 1651 tons,as of March 2021,indicating that the developed gelling systems were good candidates for use in oilfield applications.

    Fig.14.The operation process of the profile control treatments in the B6H well group.

    Fig.15.Production performance of the B6H well group:(a) B2;(b) B3;(c) B7;(d) B9.

    Acknowledgments

    Financial support from the Major Scientific and Technological Project of CNPC under grant number ZD2019-183-007 is gratefully acknowledged.The authors also thank Sinopec Northwest Company of China for the financial support (34400007-17-ZC0607-0095).

    Appendix A.Supplementary data

    Supplementary data to this article can be found online at https://doi.org/10.1016/j.petsci.2022.01.006.

    两个人免费观看高清视频| 国产在线观看jvid| 亚洲 欧美 日韩 在线 免费| 久久精品国产综合久久久| 午夜久久久久精精品| 国产视频内射| 18禁黄网站禁片午夜丰满| 桃红色精品国产亚洲av| 夜夜爽天天搞| 精品久久久久久久毛片微露脸| 久久天堂一区二区三区四区| 女人高潮潮喷娇喘18禁视频| 日本免费一区二区三区高清不卡| 欧美日韩精品网址| 国产伦在线观看视频一区| 日韩欧美国产在线观看| 91大片在线观看| 伦理电影免费视频| 国产久久久一区二区三区| 法律面前人人平等表现在哪些方面| e午夜精品久久久久久久| 在线观看免费午夜福利视频| 亚洲成av人片免费观看| 十八禁人妻一区二区| 久久亚洲真实| 亚洲国产欧美一区二区综合| 久久精品91无色码中文字幕| 精品久久久久久久末码| 午夜福利在线观看吧| 久久天躁狠狠躁夜夜2o2o| 日韩高清综合在线| 亚洲五月婷婷丁香| 久久精品国产清高在天天线| 亚洲片人在线观看| 美女大奶头视频| 999久久久国产精品视频| 又紧又爽又黄一区二区| 一本综合久久免费| 日日摸夜夜添夜夜添小说| 国产久久久一区二区三区| 一本精品99久久精品77| 法律面前人人平等表现在哪些方面| 欧美成人免费av一区二区三区| 桃色一区二区三区在线观看| 欧美日韩福利视频一区二区| 一本一本综合久久| 亚洲成av人片免费观看| 久久精品91无色码中文字幕| 啪啪无遮挡十八禁网站| 欧美大码av| 成人国语在线视频| 日本一二三区视频观看| 99国产精品一区二区蜜桃av| 在线观看美女被高潮喷水网站 | 中文字幕av在线有码专区| 黑人欧美特级aaaaaa片| 精品第一国产精品| 国产精品 欧美亚洲| 国产v大片淫在线免费观看| 亚洲人成伊人成综合网2020| 三级毛片av免费| 成年女人毛片免费观看观看9| 国产成人欧美在线观看| www.精华液| 亚洲成人中文字幕在线播放| av中文乱码字幕在线| 国产高清视频在线播放一区| 午夜日韩欧美国产| 国产亚洲精品av在线| xxx96com| √禁漫天堂资源中文www| 欧美乱码精品一区二区三区| 国产免费男女视频| 亚洲 欧美 日韩 在线 免费| 亚洲一区二区三区色噜噜| 村上凉子中文字幕在线| 亚洲全国av大片| 国产精华一区二区三区| 亚洲av熟女| 日韩av在线大香蕉| 亚洲国产欧美一区二区综合| 午夜福利在线观看吧| 99riav亚洲国产免费| 国产av一区在线观看免费| 欧美在线一区亚洲| 母亲3免费完整高清在线观看| 国产成人影院久久av| 久久精品成人免费网站| 精品欧美国产一区二区三| 国产真实乱freesex| 国产精品亚洲av一区麻豆| www.精华液| 啦啦啦观看免费观看视频高清| 亚洲av片天天在线观看| 国产成+人综合+亚洲专区| 亚洲国产精品合色在线| 身体一侧抽搐| 999久久久国产精品视频| 巨乳人妻的诱惑在线观看| 久久精品国产亚洲av香蕉五月| 18禁国产床啪视频网站| 亚洲精品美女久久av网站| 久久久久久大精品| 日韩av在线大香蕉| 1024手机看黄色片| 久久久精品国产亚洲av高清涩受| 成年女人毛片免费观看观看9| 久久热在线av| 真人做人爱边吃奶动态| 亚洲自偷自拍图片 自拍| 国产精品亚洲一级av第二区| 亚洲成人久久性| 在线视频色国产色| 久久精品夜夜夜夜夜久久蜜豆 | 国产蜜桃级精品一区二区三区| 老汉色av国产亚洲站长工具| 俄罗斯特黄特色一大片| tocl精华| e午夜精品久久久久久久| 久久伊人香网站| 国产探花在线观看一区二区| 99久久99久久久精品蜜桃| 曰老女人黄片| 99久久久亚洲精品蜜臀av| 丁香欧美五月| 黄片小视频在线播放| videosex国产| 叶爱在线成人免费视频播放| 亚洲精华国产精华精| 久久久久性生活片| 国产单亲对白刺激| 91在线观看av| 在线观看66精品国产| 日韩欧美 国产精品| 五月伊人婷婷丁香| 亚洲成人国产一区在线观看| 国产一区二区在线av高清观看| 国产精品精品国产色婷婷| 日本a在线网址| 丝袜人妻中文字幕| 一本一本综合久久| 亚洲成a人片在线一区二区| 亚洲国产中文字幕在线视频| 欧美久久黑人一区二区| 搡老熟女国产l中国老女人| 小说图片视频综合网站| 天天躁夜夜躁狠狠躁躁| 无遮挡黄片免费观看| 99riav亚洲国产免费| 黄片大片在线免费观看| 亚洲人成电影免费在线| 国产精品久久电影中文字幕| 国产三级黄色录像| 我的老师免费观看完整版| 日韩欧美精品v在线| 一进一出好大好爽视频| 99在线人妻在线中文字幕| 国产黄色小视频在线观看| 18禁裸乳无遮挡免费网站照片| 在线观看免费午夜福利视频| 成人亚洲精品av一区二区| 啦啦啦韩国在线观看视频| 日韩精品中文字幕看吧| 国内少妇人妻偷人精品xxx网站 | ponron亚洲| 亚洲国产精品sss在线观看| 亚洲九九香蕉| 中文字幕精品亚洲无线码一区| 国产精品一区二区免费欧美| 手机成人av网站| 国产三级在线视频| 美女高潮喷水抽搐中文字幕| 亚洲人成77777在线视频| 嫩草影院精品99| 夜夜爽天天搞| e午夜精品久久久久久久| 观看免费一级毛片| 日韩欧美在线二视频| 欧美高清成人免费视频www| 亚洲av成人精品一区久久| 亚洲av中文字字幕乱码综合| 亚洲午夜精品一区,二区,三区| 两个人的视频大全免费| 成人三级黄色视频| 亚洲精品美女久久久久99蜜臀| 色播亚洲综合网| 97超级碰碰碰精品色视频在线观看| 男女那种视频在线观看| 又黄又爽又免费观看的视频| 18禁观看日本| www日本黄色视频网| 嫩草影院精品99| 午夜福利视频1000在线观看| www国产在线视频色| 性欧美人与动物交配| 国产人伦9x9x在线观看| 免费在线观看日本一区| 国产乱人伦免费视频| 亚洲精品一区av在线观看| 欧美黄色片欧美黄色片| 久久天躁狠狠躁夜夜2o2o| 日本撒尿小便嘘嘘汇集6| 国内精品久久久久久久电影| 50天的宝宝边吃奶边哭怎么回事| 精品福利观看| 国产野战对白在线观看| 99在线人妻在线中文字幕| 大型av网站在线播放| xxxwww97欧美| 国产激情欧美一区二区| av福利片在线观看| av在线播放免费不卡| 国产一区二区三区在线臀色熟女| 免费看十八禁软件| 首页视频小说图片口味搜索| 啦啦啦观看免费观看视频高清| 老熟妇乱子伦视频在线观看| 欧美日本亚洲视频在线播放| 琪琪午夜伦伦电影理论片6080| 欧美黑人巨大hd| 久久久久性生活片| 国产精品野战在线观看| 免费无遮挡裸体视频| 婷婷精品国产亚洲av在线| 五月玫瑰六月丁香| 精品久久久久久久末码| 少妇的丰满在线观看| 午夜日韩欧美国产| 一区二区三区高清视频在线| 亚洲激情在线av| 1024视频免费在线观看| 熟女少妇亚洲综合色aaa.| 日韩欧美在线乱码| 日本黄色视频三级网站网址| 久久亚洲精品不卡| 女生性感内裤真人,穿戴方法视频| 18美女黄网站色大片免费观看| 午夜激情福利司机影院| 国产片内射在线| 欧美乱码精品一区二区三区| 日韩欧美 国产精品| 男女下面进入的视频免费午夜| 中文字幕熟女人妻在线| 亚洲熟妇中文字幕五十中出| 91国产中文字幕| 久久久精品国产亚洲av高清涩受| 日韩大尺度精品在线看网址| 欧美不卡视频在线免费观看 | 好男人在线观看高清免费视频| 国产高清videossex| 亚洲欧美精品综合一区二区三区| 欧美av亚洲av综合av国产av| 久久久精品欧美日韩精品| 女警被强在线播放| 成人18禁高潮啪啪吃奶动态图| 精品少妇一区二区三区视频日本电影| 一区福利在线观看| 久久亚洲真实| 国产区一区二久久| 国产亚洲精品av在线| 97碰自拍视频| 99国产综合亚洲精品| 亚洲五月婷婷丁香| 国产aⅴ精品一区二区三区波| 欧美精品亚洲一区二区| 国产真人三级小视频在线观看| 淫秽高清视频在线观看| 精品欧美国产一区二区三| 制服人妻中文乱码| 麻豆成人av在线观看| 99re在线观看精品视频| 两个人视频免费观看高清| 精品久久蜜臀av无| 国产成+人综合+亚洲专区| 亚洲自拍偷在线| 性色av乱码一区二区三区2| 操出白浆在线播放| 亚洲 欧美一区二区三区| 中文亚洲av片在线观看爽| 久久精品aⅴ一区二区三区四区| 免费搜索国产男女视频| 首页视频小说图片口味搜索| 久久久久免费精品人妻一区二区| 国内少妇人妻偷人精品xxx网站 | 草草在线视频免费看| 老鸭窝网址在线观看| www.熟女人妻精品国产| 亚洲人成网站在线播放欧美日韩| 亚洲,欧美精品.| 男人的好看免费观看在线视频 | 久久天堂一区二区三区四区| 18美女黄网站色大片免费观看| 欧洲精品卡2卡3卡4卡5卡区| 日韩精品中文字幕看吧| 一a级毛片在线观看| 免费人成视频x8x8入口观看| 成熟少妇高潮喷水视频| 手机成人av网站| 国产精品久久久av美女十八| 亚洲成人免费电影在线观看| 欧美午夜高清在线| 91国产中文字幕| 91大片在线观看| 三级国产精品欧美在线观看 | 少妇被粗大的猛进出69影院| 1024视频免费在线观看| 观看免费一级毛片| 亚洲国产高清在线一区二区三| 国产精品一及| 欧美成人一区二区免费高清观看 | 高清在线国产一区| 亚洲 欧美 日韩 在线 免费| 88av欧美| 国产欧美日韩一区二区精品| 九色国产91popny在线| 国产午夜福利久久久久久| a级毛片a级免费在线| 最新在线观看一区二区三区| 久久精品亚洲精品国产色婷小说| 日韩成人在线观看一区二区三区| 男女之事视频高清在线观看| 熟女少妇亚洲综合色aaa.| 手机成人av网站| 美女黄网站色视频| 国产熟女午夜一区二区三区| 波多野结衣巨乳人妻| 最好的美女福利视频网| 两个人视频免费观看高清| 日本三级黄在线观看| 变态另类成人亚洲欧美熟女| 免费av毛片视频| 国产av又大| 日韩欧美在线乱码| 久久香蕉精品热| 成人三级黄色视频| 精华霜和精华液先用哪个| 此物有八面人人有两片| 小说图片视频综合网站| 一本大道久久a久久精品| 一区二区三区国产精品乱码| 日韩大尺度精品在线看网址| 久久精品91蜜桃| 一二三四社区在线视频社区8| 可以在线观看的亚洲视频| 国产亚洲精品av在线| 国产精品香港三级国产av潘金莲| 丝袜人妻中文字幕| 高潮久久久久久久久久久不卡| 99国产极品粉嫩在线观看| 欧美日韩乱码在线| 亚洲av电影不卡..在线观看| 日本成人三级电影网站| 91麻豆精品激情在线观看国产| 在线观看免费日韩欧美大片| 成人一区二区视频在线观看| 国产精品久久久久久亚洲av鲁大| 一夜夜www| 黑人欧美特级aaaaaa片| 国产高清视频在线播放一区| 久久中文字幕一级| svipshipincom国产片| 12—13女人毛片做爰片一| 亚洲国产欧美人成| 亚洲一区高清亚洲精品| 小说图片视频综合网站| 国产av不卡久久| 桃色一区二区三区在线观看| 亚洲av熟女| 黄色片一级片一级黄色片| 搡老熟女国产l中国老女人| 色综合亚洲欧美另类图片| 两性夫妻黄色片| 日韩欧美在线乱码| 久久精品夜夜夜夜夜久久蜜豆 | 正在播放国产对白刺激| 国产一级毛片七仙女欲春2| 琪琪午夜伦伦电影理论片6080| 久久久国产成人精品二区| 成年版毛片免费区| 国产精品免费一区二区三区在线| bbb黄色大片| 国产乱人伦免费视频| 美女高潮喷水抽搐中文字幕| 精品一区二区三区四区五区乱码| 国产精品亚洲美女久久久| 久久精品国产亚洲av香蕉五月| 久久这里只有精品19| 又黄又粗又硬又大视频| 91麻豆精品激情在线观看国产| 中文字幕精品亚洲无线码一区| 熟妇人妻久久中文字幕3abv| 国产精品免费一区二区三区在线| 成人av在线播放网站| 又黄又爽又免费观看的视频| 99精品欧美一区二区三区四区| 国产97色在线日韩免费| 国产精品一区二区精品视频观看| 亚洲精品色激情综合| 无人区码免费观看不卡| 天天一区二区日本电影三级| 欧美黄色片欧美黄色片| 免费在线观看黄色视频的| 久久久久国产精品人妻aⅴ院| 色综合亚洲欧美另类图片| 午夜精品久久久久久毛片777| 国产熟女xx| 精品国产美女av久久久久小说| www.www免费av| 91九色精品人成在线观看| 国产免费av片在线观看野外av| 精品欧美国产一区二区三| 搞女人的毛片| 美女高潮喷水抽搐中文字幕| 老司机午夜福利在线观看视频| 久热爱精品视频在线9| 九九热线精品视视频播放| 久久草成人影院| 我的老师免费观看完整版| 色播亚洲综合网| 亚洲av中文字字幕乱码综合| 巨乳人妻的诱惑在线观看| 国产熟女午夜一区二区三区| 精品福利观看| 色综合站精品国产| 亚洲avbb在线观看| 身体一侧抽搐| 亚洲国产精品成人综合色| 日韩大尺度精品在线看网址| 少妇人妻一区二区三区视频| 久久午夜亚洲精品久久| 亚洲一区中文字幕在线| 亚洲国产欧洲综合997久久,| 狂野欧美激情性xxxx| 老熟妇仑乱视频hdxx| 一个人观看的视频www高清免费观看 | 日韩精品中文字幕看吧| 变态另类丝袜制服| 日本三级黄在线观看| 最好的美女福利视频网| 亚洲色图 男人天堂 中文字幕| 一本大道久久a久久精品| 久久久久久久久久黄片| 久久久久国产一级毛片高清牌| 手机成人av网站| 国产亚洲欧美在线一区二区| 国产午夜福利久久久久久| 一a级毛片在线观看| 精品熟女少妇八av免费久了| 又黄又爽又免费观看的视频| 亚洲18禁久久av| 成人三级做爰电影| 亚洲成人久久性| 大型av网站在线播放| 99国产精品99久久久久| 两个人免费观看高清视频| 午夜激情福利司机影院| 麻豆成人av在线观看| 欧美日韩亚洲综合一区二区三区_| 久久人妻av系列| av在线播放免费不卡| 99热6这里只有精品| 久久久久久免费高清国产稀缺| 在线观看美女被高潮喷水网站 | 国模一区二区三区四区视频 | 国产99久久九九免费精品| 日韩 欧美 亚洲 中文字幕| 99热6这里只有精品| 两个人的视频大全免费| 久久精品国产亚洲av高清一级| 久久 成人 亚洲| 在线免费观看的www视频| 欧美丝袜亚洲另类 | 欧美人与性动交α欧美精品济南到| 欧美 亚洲 国产 日韩一| 亚洲,欧美精品.| 国产单亲对白刺激| 精品国产亚洲在线| 最近最新中文字幕大全免费视频| 50天的宝宝边吃奶边哭怎么回事| 一级a爱片免费观看的视频| 一进一出抽搐动态| 一边摸一边做爽爽视频免费| 亚洲av电影在线进入| 精品久久久久久久久久免费视频| 成人国产一区最新在线观看| 久久天躁狠狠躁夜夜2o2o| 日韩国内少妇激情av| videosex国产| 夜夜躁狠狠躁天天躁| 国产精品,欧美在线| 国产成人欧美在线观看| 成人特级黄色片久久久久久久| 亚洲黑人精品在线| 9191精品国产免费久久| 亚洲精品美女久久av网站| 国内久久婷婷六月综合欲色啪| 午夜福利在线在线| 在线观看免费午夜福利视频| 一区二区三区激情视频| 狠狠狠狠99中文字幕| 国产av麻豆久久久久久久| 91麻豆精品激情在线观看国产| 婷婷丁香在线五月| 国产精品久久久久久亚洲av鲁大| 久久性视频一级片| 婷婷精品国产亚洲av| 听说在线观看完整版免费高清| 欧美最黄视频在线播放免费| 岛国视频午夜一区免费看| 日本在线视频免费播放| 亚洲乱码一区二区免费版| 国产成人aa在线观看| 亚洲电影在线观看av| 国模一区二区三区四区视频 | 免费一级毛片在线播放高清视频| 精品乱码久久久久久99久播| 成人18禁高潮啪啪吃奶动态图| 免费看a级黄色片| 很黄的视频免费| 精品国产亚洲在线| 男插女下体视频免费在线播放| 亚洲一区中文字幕在线| 一夜夜www| 特级一级黄色大片| 国产精品av久久久久免费| 99精品在免费线老司机午夜| 91麻豆精品激情在线观看国产| 欧洲精品卡2卡3卡4卡5卡区| 美女免费视频网站| 可以在线观看的亚洲视频| 99久久久亚洲精品蜜臀av| 久久九九热精品免费| 国产黄片美女视频| a级毛片在线看网站| 成人国产综合亚洲| 亚洲七黄色美女视频| 国产精品电影一区二区三区| www.999成人在线观看| 中文在线观看免费www的网站 | 亚洲第一欧美日韩一区二区三区| 又粗又爽又猛毛片免费看| 在线观看日韩欧美| 日韩中文字幕欧美一区二区| 国产精品久久视频播放| 国语自产精品视频在线第100页| 51午夜福利影视在线观看| 国产午夜精品论理片| videosex国产| 真人做人爱边吃奶动态| 亚洲中文av在线| 久久 成人 亚洲| 90打野战视频偷拍视频| 亚洲午夜理论影院| 欧美性猛交黑人性爽| 波多野结衣巨乳人妻| 久久精品综合一区二区三区| 久久 成人 亚洲| 琪琪午夜伦伦电影理论片6080| 黄色毛片三级朝国网站| 国产一区二区激情短视频| 亚洲午夜理论影院| 久久中文字幕人妻熟女| 久久精品国产综合久久久| 亚洲性夜色夜夜综合| 一本综合久久免费| 少妇裸体淫交视频免费看高清 | 巨乳人妻的诱惑在线观看| 精品欧美一区二区三区在线| 久久国产乱子伦精品免费另类| 免费看日本二区| 一a级毛片在线观看| 午夜成年电影在线免费观看| 国产精品久久久久久精品电影| 欧美另类亚洲清纯唯美| 国内揄拍国产精品人妻在线| 一卡2卡三卡四卡精品乱码亚洲| 中文字幕人成人乱码亚洲影| 久久久久国产一级毛片高清牌| www日本黄色视频网| www.精华液| 91麻豆精品激情在线观看国产| 最新美女视频免费是黄的| 国产91精品成人一区二区三区| 久久人妻av系列| 长腿黑丝高跟| 精品久久久久久久人妻蜜臀av| 国产黄a三级三级三级人| 亚洲精品av麻豆狂野| 亚洲九九香蕉| 一本大道久久a久久精品| 两个人视频免费观看高清| 国产精品一区二区精品视频观看| 久久久久国内视频| 国产精品久久久久久久电影 | 一区二区三区高清视频在线| 无人区码免费观看不卡| 亚洲精品一区av在线观看| 亚洲成a人片在线一区二区| 美女大奶头视频| 欧洲精品卡2卡3卡4卡5卡区| 99热只有精品国产| 国产精品电影一区二区三区| 国产亚洲欧美在线一区二区| 又黄又粗又硬又大视频| 岛国在线免费视频观看| 国产黄片美女视频| 一边摸一边抽搐一进一小说| 精品国产亚洲在线| 1024手机看黄色片| 波多野结衣高清无吗| 中出人妻视频一区二区| 日韩欧美精品v在线| 亚洲avbb在线观看| 国产欧美日韩一区二区三| 看免费av毛片|