    粉末裝載量對金屬注射成形17-4PH不銹鋼力學性能的影響

    2018-05-11 03:15:49喻建李益民李東陽李行
    粉末冶金材料科學與工程 2018年1期
    關(guān)鍵詞:裝載量脫脂粘結(jié)劑

    喻建,李益民,李東陽,李行

    ?

    粉末裝載量對金屬注射成形17-4PH不銹鋼力學性能的影響

    喻建1, 2,李益民1, 2,李東陽2,李行2

    (1. 湖南英捷高科技有限責任公司,長沙 410083;2. 中南大學 粉末冶金國家重點實驗室,長沙 410083)

    在硝酸氣氛下對注射成形17-4PH不銹鋼坯體中的粘結(jié)劑成分POM(polyformaldehyde, 聚甲醛)進行催化脫脂,然后在真空燒結(jié)爐中進行熱脫脂和燒結(jié),研究粉末裝載量和催化脫脂時間對催化脫脂率的影響,以及粉末裝載量對燒結(jié)不銹鋼的顯微組織、致密度與抗拉強度的影響。結(jié)果表明:燒結(jié)不銹鋼的顯微組織為以奧氏體為主和少量鐵素體共同組成的復合組織。隨粉末裝載量從55.1%增加至65.7%,催化脫脂率從7.8%降低到5.2%,但燒結(jié)密度從7.56 g/cm3增加到7.66 g/cm3,燒結(jié)不銹鋼的抗拉強度從1 076 MPa提高到1 204 MPa;130 ℃下隨催化脫脂保溫時間從30延長至90 min,催化脫脂率從4.9%增加至6.7%,在90~150 min時間段內(nèi)催化脫脂率穩(wěn)定在6.7%左右。粉末裝載量為65.7%的注射喂料經(jīng)過90 min催化脫脂,可完全脫除粘結(jié)劑中的POM,催化脫脂率達到6.72%,注射坯形成完整的連通孔道。

    MIM17-4PH不銹鋼;粉末裝載量;催化脫脂;抗拉強度

    17-4PH馬氏體沉淀硬化不銹鋼的強度高、耐腐蝕,切削性能優(yōu)異,在醫(yī)療器械、電子產(chǎn)品、軍工和航空航天等領(lǐng)域有著廣泛的應用。采用MIM工藝以較低成本生產(chǎn)復雜形狀零件,具有生產(chǎn)效率高、性能優(yōu)異等優(yōu)勢[1],尤其適合于加工工藝復雜的小尺寸產(chǎn)品。MIM 17-4PH不銹鋼的脫脂工藝在生產(chǎn)過程中非常重要[2?6],它會直接影響后續(xù)工藝制訂及產(chǎn)品的力學性能,通常的脫脂方法為熱脫脂和溶劑脫脂,產(chǎn)品容易產(chǎn)生缺陷,并且生產(chǎn)周期長。催化脫脂具有脫脂缺陷少,脫脂速率快等優(yōu)點[7?8]。催化脫脂是在酸性氣氛下加熱使粘結(jié)劑中的聚甲醛(POM)快速分解為甲醛氣體,達到快速脫除POM的效果。現(xiàn)階段的MIM17-4PH生產(chǎn)主要采用固定的粉末裝載量,脫脂后注射坯的收縮比一定,燒結(jié)制品的性能單一。而不同行業(yè)領(lǐng)域的產(chǎn)品尺寸大小不一,其力學性能要求也不盡相同,因此單一粉末裝載量的燒結(jié)制品已不能滿足各行業(yè)對于MIM17-4PH性能多元化的要求。過調(diào)整粉末裝載量有望得到不同性能的產(chǎn)品,但目前針對粉末裝載量對MIM17-4PH燒結(jié)制品性能的研究很少。本文作者通過調(diào)整粘結(jié)劑與不銹鋼粉末的配比,制備4組不同粉末裝載量的注射成形生坯,采用催化脫脂和熱脫脂兩步法脫脂,研究粉末裝載量對脫脂率和燒結(jié)后制品的顯微組織與抗拉強度的影響,為MIM17-4PH多元化生產(chǎn)提供實驗基礎(chǔ)。

    1 實驗

    實驗用17-4PH不銹鋼粉末為Osprey公司提供的氣霧化粉末,其成分和性能列于表1,粉末SEM形貌如圖1所示。粘結(jié)劑由聚甲醛(POM)、高密度聚乙烯和少量其它粘結(jié)助劑組成。在催化脫脂中,如果POM含量太低,則較難脫除,POM含量越高,催化脫脂率越高,但脫脂坯的保形性差,所以POM的含量應在一定的范圍內(nèi)。本研究的催化劑組成(質(zhì)量分數(shù))為91%POM、4%高密度聚乙烯(HDPE)、5%其它。

    表1 17-4PH不銹鋼粉末的成分與性能

    取17-4PH不銹鋼粉末1 000 g,按照表2所列數(shù)據(jù)加入粘結(jié)劑,在四罐混料器中混料3 h,然后采用V68制粒機制粒,在80T注射成形機中進行注射成形,得到4組不同粉末裝載量的注射成形生坯。

    圖1 氣霧化17-4PH粉末的SEM形貌

    表2 粘結(jié)劑用量與粉末裝載量

    采用催化脫脂和熱脫脂兩步法進行脫脂。催化脫脂在5510真空脫脂爐中進行,首先在室溫下通入硝酸進行65 min初期催化脫脂,通入量為2 m3/h;然后在室溫下通入硝酸進行40 min中期催化脫脂,通入量為3 m3/h;最后以5 ℃/min升溫至130 ℃,進一步催化脫脂,脫脂時間為30~150 min,硝酸通入量為3.4 mL/min,再以3 ℃/min的速率降至室溫后通入氬氣保護取出樣品。催化脫脂后的樣品干燥2 h后,稱重。在3311真空燒結(jié)爐中進行熱脫脂和燒結(jié),熱脫脂溫度為900 ℃,保溫1 h,使成形坯中的高密度聚乙烯分解而得以脫除。然后以5 ℃/min升溫至1 300 ℃真空燒結(jié),保溫120 min,再以4 ℃/min速率降溫470 ℃,然后隨爐冷卻,得到17-4PH不銹鋼樣品。

    用精度為0.1 mg的電子天平稱量注射成形坯體催化脫脂前和催化脫脂后的質(zhì)量,用催化脫脂后的質(zhì)量損失率表征樣品的催化脫脂率。

    采用阿基米德排水法測定17-4PH燒結(jié)不銹鋼的密度;用 Instron萬能試驗機測量抗拉強度,拉伸速度為1.0 mm/min,并通過JSM-6360掃描電鏡觀察拉伸斷口的形貌。在HDI?1875型布洛維硬度計上測定燒結(jié)樣品的HRB和HRC硬度;用Polyvarmet金相顯微鏡觀察經(jīng)4%的硝酸酒精溶液腐蝕后的17-4PH不銹鋼微觀結(jié)構(gòu)。

    2 結(jié)果與討論

    2.1 催化脫脂率

    2.1.1 粉末裝載量的影響

    圖2所示為不同粉末裝載量的17-4PH不銹鋼注射成形坯130 ℃下催化脫脂90 min后的脫脂率。從圖2看出,催化脫脂率隨粉末裝載量增大而降低,這是因為隨粉末裝載量增大,粘結(jié)劑的用量減小,坯體中POM的含量隨之降低,所以催化脫脂率下降。雖然粉末裝載率最高的試樣F1具有很高的脫脂率,催化脫脂效果最佳,但坯體產(chǎn)生裂紋和破碎,脫脂坯的保形性不好。F3具有較高的脫脂率和較好的保形性,因此選擇試樣F3做進一步研究。

    圖2 17-4PH粉末裝載量對催化脫脂率的影響

    2.1.2 催化脫脂時間的影響

    圖3所示為粉末裝載量為59.4%的MIM坯體催化脫脂率隨130℃下催化脫脂時間的變化。從圖3可看出,在30~90 min內(nèi),催化脫脂率隨催化脫脂時間延長而增加,隨后在90~150 min內(nèi),催化脫脂率基本保持不變。催化脫脂過程大致分為3個階段,第1階段是最初階段(30~60 min),質(zhì)量損失率曲線的斜率最大,表明POM的降解速率最大;第2階段是60~90 min內(nèi),與第1階段相比,POM的降解速率降低;第3階段是90~150 min,脫脂率基本不變。在催化脫脂的最初階段,催化脫脂反應主要在試樣的外圍部分,POM和HDPE的降解產(chǎn)物擴散的阻力小,同時硝酸與POM和HDPE的接觸面積大,因而具有較大的脫脂速率。相比第1階段,第2階段的脫脂速率有所下降,這是因為脫脂反應向試樣內(nèi)部進行,催化劑和聚合物的接觸面積減小,同時通入真空脫脂爐的硝酸氣體擴散的難度增大。在催化脫脂的最后階段中,主粘結(jié)劑POM的脫出率已相當高,當催化反應進行到試樣中心部位時,催化劑與POM的接觸面積很小,硝酸氣體擴散更加困難,因此催化脫脂率基本不變。催化劑氣體與POM的接觸面積以及氣體的擴散速率是催化脫脂速率的主要影響因素。從圖3可見,催化脫脂90 min 時催化脫脂率達到6.72%,脫脂效率最高。

    圖3 催化脫脂率隨脫脂時間的變化

    2.2 顯微組織

    圖4所示為不同粉末裝載量的成形坯在130 ℃下催化脫脂90 min的燒結(jié)試樣顯微組織。從圖4看出,粉末裝載量為55.1%和59.4%的17-4PH燒結(jié)不銹鋼晶粒相對較?。浑S粉末裝載量增加,晶粒逐漸長大,晶粒分布更均勻。

    17-4PH不銹鋼的基體組織主要由奧氏體組成,在粉末裝載量為63.2%和65.7%的燒結(jié)試樣中,奧氏體含量多于粉末裝載量為55.1%和59.4%的試樣,鐵素體也增加,其原因是金屬粉末增多。同時看到,孔隙的分布也與粉末裝載量有一定關(guān)系,當粉末裝載量較低時,孔隙較大,分布較集中和廣泛,隨粉末裝載量增加,孔隙尺寸變小,孔隙數(shù)量減少,這與催化脫脂和熱脫脂過程中粘結(jié)劑脫除有關(guān)。假定A為粘結(jié)劑,B為17-4PH熔體,根據(jù)Fick定律:

    圖4 不同粉末裝載量的17-4PH燒結(jié)不銹鋼的金相組織

    (a) 55.1%; (b) 59.4%; (c) 63.2%; (d) 65.7%

    式中:為擴散通量;eff為成形坯中組元A蒸發(fā)為氣體在聚合物熔體中的有效擴散系數(shù);Δ為粘結(jié)劑濃度梯度,Δ為氣體A在坯塊中的起始濃度;為擴散距離。eff可表示為:

    式中:A為氣體A在B熔體中的實際擴散系數(shù);0為氣體A在B熔體中的初始擴散系數(shù);為活化能;為普適氣體常數(shù);為粉末裝載量;為孔隙曲折因子。催化脫脂過程中,粘結(jié)劑的擴散距離最開始為粘結(jié)劑到坯塊表面的距離,隨著粘結(jié)劑脫除,孔隙不斷生成并向坯塊內(nèi)部擴展,粘結(jié)劑到坯塊表面的擴散距離逐漸增加,最后擴散距離轉(zhuǎn)變?yōu)檎谛纬傻南噜?個孔隙之間的距離。擴散距離與粉末粒徑有關(guān),4組試樣粉末粒徑相同,因此擴散的難易程度與擴散通量有直接聯(lián)系,隨粉末裝載量增加,擴散通量降低,擴散難度增加。結(jié)合式(1)和(2)可知,粉末裝載量對整個熱脫脂的熱力學過程起著重要的作用,粉末裝載量越小,粘結(jié)劑在17-4PH熔體中擴散越容易,因而有更多的粘結(jié)劑被脫除,在試樣內(nèi)部留下更多的空位,經(jīng)燒結(jié)后形成較多的孔隙。

    2.3 致密度

    圖5所示為在130 ℃下催化脫脂90 min后, 17-4PH燒結(jié)不銹鋼密度隨粉末裝載量的變化。

    圖5 17-4PH的燒結(jié)密度隨粉末裝載量的變化

    從圖5看出,隨粉末裝載量從55.1%增加到63.2%,不銹鋼的致密度從7.56 g/cm3增加到7.66 g/cm3,從圖4看出,隨粉末裝載量增加,燒結(jié)不銹鋼的孔隙數(shù)量減少,所以致密度較高。但當粉末裝載量達到63.2%時,隨粉末裝載量進一步增大,燒結(jié)密度總體變化不大,從圖4也看出,當粉末裝載量達到一定比例時,進一步增加粉末裝載量,燒結(jié)試樣的孔隙率變化不大。

    2.4 抗拉強度

    圖6所示為燒結(jié)17-4PH不銹鋼的抗拉強度隨粉末裝載量的變化。MIM 17-4PH的顯微組織是由馬氏體、鐵素體以及殘留的奧氏體組成[9]。WU等[10]的研究表明,孔隙率增加導致MIM17-4PH不銹鋼的抗拉強度降低。從圖4看出,隨粉末裝載量從55.1%增加到59.4%,燒結(jié)密度增大,但密度仍然較低,表明孔隙率仍較大,所以材料的抗拉強度仍然較低,從1 076 MPa小幅提高至1 132 MPa。粉末裝載量為63.2%和65.7%的試樣,密度上升到7.66 g/cm3左右,抗拉強度分別提高到1 169和1 204 MPa。

    圖6 MIM 17-4PH不銹鋼的抗拉強度隨粉末裝載量的變化

    圖7所示為 130 ℃下催化脫脂90 min,不同粉末裝載量條件下制備的MIM 17-4PH燒結(jié)試樣的拉伸斷口形貌。由圖可見,粉末裝載量為55.1%和59.4%的試樣,斷口存在典型的韌窩,但數(shù)量少,韌窩深度較淺,表明材料的延性較差。這是由于注射成形坯體中含有大量的粘結(jié)劑,在粘結(jié)劑脫除之后,留下較多的孔隙,在燒結(jié)致密化過程中,孔隙連通,導致材料塑性較差。同時,粉末裝載量較低時,燒結(jié)后鐵素體含量較少,也使材料的延性降低。粉末裝載量為63.2%和65.7%的試樣,斷口形貌基本呈韌窩狀,韌窩較密集、較深(見圖7(c),(d)),這說明材料的延性較好。從圖7(a)和(b)看出,粉末裝載量為55.1%和59.4%的2個試樣的斷口部位撕裂棱不明顯,有些撕裂棱的長度較大,這都說明材料的強度較差。而在圖7(c)和(d)清晰地看到撕裂棱沿晶界延伸,同時撕裂棱較短小,這表明粉末裝載量提升有助于提高MIM 17-4PH的 強度。

    圖7 不同粉末裝載量條件下MIM 17-4PH的拉伸斷口形貌

    (a) 55.1%; (b) 59.4%; (c) 63.2%; (d) 65.7%

    3 結(jié)論

    1) 采用金屬注射成形法制備17-4PH不銹鋼,采用催化脫脂和熱脫脂兩步法進行脫脂,隨粉末裝載量從55.1%增加到65.7%,催化脫脂率從7.8%降至5.2%,其中粉末裝載量為55.1%的注射試樣,催化脫脂率最高,達到87%;130 ℃下的最佳催化脫脂時間為90 min。

    2) 在催化脫脂時間為30 min的條件下,隨粉末裝載量從55.1%增加到65.7%,17-4PH不銹鋼孔隙率降低,密度從7.56 g/cm3增加到7.66 g/cm3,抗拉強度從1 076 MPa提高到1 204 MPa,其中粉末裝載量為65.7%的燒結(jié)試樣具有較良好的力學性能。

    [1] 楊忠臣. 17-4PH不銹鋼粉末注射成形工藝研究[D]. 長沙: 中南大學, 2013. YANG Zhongchen. Research on powder injection molding of 17-4PH stainless steel[D]. Changsha: Central South University, 2013.

    [2] 李益民, KHALIL K A, 黃伯云. 金屬注射成形17-4PH不銹鋼脫脂保形性研究[J]. 稀有金屬材料與工程, 2005, 34(1): 22?27. LI Yimin, KHALIL K A, HUANG Bayun. Compact shape retention for metal injection molding 17-4PH stainless steel[J]. Rare Metal Materials and Engineering, 2005, 34(1): 22?27.

    [3] JUN Wang, LIN Yuanhua, ZENG Dezhi, et al. Effects of the process parameters on the microstructure and properties of Nitrided 17-4PH stainless steel[J]. Metallurgical and Materials Transactions B, 2013, 44(2): 414?422.

    [4] 杜大明, 汪洋, 白小波. 熱處理對17-4PH不銹鋼組織和性能的影響[J]. 熱處理技術(shù)與裝備, 2012, 33(1): 30?32. DU Daming, WANG Yang, BAI Xiaobo. Effect of heat treatment on microstructure and property of 17-4PH stainless steel[J]. Heat Treatment Technology and Equipment, 2012, 33(1): 30?32.

    [5] 鄧德偉, 陳蕊, 田鑫, 等. 熱處理對17-4PH馬氏體不銹鋼顯微組織及性能的影響[J]. 金屬熱處理, 2013, 38(4): 32?36. DENG Dewei, CHEN Rui, TIAN Xin, et al. Influence of heat treatment on microstructure and properties of 17-4PH martensitic stainless steel[J]. Heat Treatment of Metals, 2013, 38(4): 32?36.

    [6] LI Yimin, KHALIL K A, HUANG Boyun. Rheological, mechanical and corrosive properties of injection molded 17-4PH stainless steel[J]. Chinese Journal of Nonferrous Metals, 2004, 14(5): 934?939.

    [7] BLEOMACHER M T P. BASF extends scope of its MIM process[J]. Metal Powder Report, 1994, 49(9): 20?21.

    [8] BLOEMACHER M. Acetyl based feedstock for injection moulding and catalytic debinding[J]. Metal Powder Report, 1998, 53(1): 40.

    [9] 張翔, 何浩, 李益民, 等. 碳含量對金屬注射成形17-4PH不銹鋼顯微組織和力學性能的影響[J]. 中國有色金屬學報, 2015(4): 945?951. ZHANG Xiang, HE Hao, LI Yimin, et al. Effect of carbon content on microstructure and mechanical properties of metal injection molded 17-4PH stainless steel[J]. The Chinese Journal of Nonferrous Metals, 2015(4): 945?951.

    [10] WU Yunxin, GERMAN R M, BLAINE D, et al. Effects of residual carbon content on sintering shrinkage, microstructure and mechanical properties of injection molded 17-4 PH stainless steel[J]. Journal of Materials Science, 2002, 37(17): 3573?3583.

    (編輯 湯金芝)

    Effect of powder loading on mechanical properties of metal injection molding 17-4PH stainless steel

    YU Jian1, 2, LI Yimin1, 2, LI Dongyang2, LI Xing2

    (1. Hunan Injection High Technology Co., Ltd, Changsha 410083, China; 2. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)

    The binder composition POM (polyformaldehyde) in the injection molded 17-4PH stainless steel body was catalytically degreased under nitric acid atmosphere, and then thermal degreasing and sintering were carried out in a vacuum sintering furnace. The effects of powder loading and catalytic degreasing time on the catalytic degreasing rate were studied, and the effects of powder loading on the microstructure, density and tensile strength of sintered products were also studied. The results show that the microstructure of the sintered products is composed of austenite and a small amount of ferrite. With increasing the powder loading from 55.1% to 65.7%, the catalytic degreasing rate of the sintered sample decreases from 7.8% to 5.2%; the density increases from 7.56 g/cm3to 7.66 g/cm3, and the tensile strength increases from 1 076 MPa to 1 204 MPa. With increasing the thermal retention time from 30 min to 90 min at 130 ℃, the catalytic degreasing rate increases from 4.9% to 6.7%. When the thermal retention time in the range of 90?150 min, the catalytic degreasing rate stabilise at about 6.7%.With the powder loading of 65.7%, the POM in the binder can be completely removed by 90min catalytic degreasing. The degreasing rate reaches 87%, and the injection blank forms a complete communicating channel.

    17-4PH stainless steel; powder loading; catalytic degreasing; tensile strength

    TF125

    A

    1673-0224(2018)01-32-06

    2017?03?17;

    2017?07?11

    李益民,教授,博士。電話:13908475507;E-mial: liyimin333@163.com

    猜你喜歡
    裝載量脫脂粘結(jié)劑
    蠟基溫拌添加劑對橡膠粉改性瀝青性能影響研究
    低脂/脫脂牛奶一定比全脂牛奶更健康嗎
    隧道復合式路面高粘改性乳化瀝青防水粘結(jié)劑開發(fā)
    石油瀝青(2019年3期)2019-07-16 08:48:20
    低脂/脫脂牛奶一定比全脂牛奶更健康嗎
    利用大鶴管裝車系統(tǒng)提高鐵路槽車裝載量淺析
    電子測試(2018年15期)2018-09-26 06:02:00
    一種垃圾車裝載量實時監(jiān)測裝置的創(chuàng)新設(shè)計
    平整液對鍍錫板脫脂效果的影響
    紅棗熱風干燥單因素試驗分析
    一種型煤粘結(jié)劑及其制備方法
    腐植酸(2016年1期)2016-12-16 08:28:50
    長焰煤型煤復合粘結(jié)劑的研究
    色在线成人网| 国产一区二区在线av高清观看| 欧美激情在线99| tocl精华| 久久久精品大字幕| 亚洲成a人片在线一区二区| 在线看三级毛片| 99久久精品国产亚洲精品| 成人av在线播放网站| 中国美女看黄片| 别揉我奶头~嗯~啊~动态视频| 一卡2卡三卡四卡精品乱码亚洲| 国产综合懂色| 国产免费男女视频| 少妇丰满av| 国内揄拍国产精品人妻在线| 精品久久久久久,| 日韩精品青青久久久久久| 免费av毛片视频| 精品久久久久久久毛片微露脸| 中文字幕熟女人妻在线| 中国美女看黄片| 久久草成人影院| 亚洲第一欧美日韩一区二区三区| 色尼玛亚洲综合影院| 国产在线精品亚洲第一网站| 国产熟女xx| 亚洲精品一卡2卡三卡4卡5卡| 亚洲精品在线观看二区| 99久久精品热视频| 午夜福利欧美成人| eeuss影院久久| www.999成人在线观看| 最新中文字幕久久久久| 国产伦精品一区二区三区视频9 | 午夜免费观看网址| 国产精品三级大全| 最近最新中文字幕大全免费视频| 亚洲aⅴ乱码一区二区在线播放| 国产精品女同一区二区软件 | 亚洲人成网站在线播| 99精品在免费线老司机午夜| 91九色精品人成在线观看| 国产探花极品一区二区| 日韩人妻高清精品专区| 老汉色∧v一级毛片| 人人妻人人澡欧美一区二区| 99国产极品粉嫩在线观看| 亚洲美女视频黄频| 天堂动漫精品| www日本黄色视频网| 国产欧美日韩一区二区三| 免费av毛片视频| 麻豆国产97在线/欧美| 国产一区二区激情短视频| 麻豆国产97在线/欧美| 欧美性猛交黑人性爽| 18禁黄网站禁片免费观看直播| 国产欧美日韩精品亚洲av| 非洲黑人性xxxx精品又粗又长| x7x7x7水蜜桃| 中出人妻视频一区二区| 亚洲欧美精品综合久久99| 欧美国产日韩亚洲一区| 午夜视频国产福利| 亚洲精品一卡2卡三卡4卡5卡| 999久久久精品免费观看国产| 女人高潮潮喷娇喘18禁视频| 午夜a级毛片| 亚洲18禁久久av| 国产精品精品国产色婷婷| 成年人黄色毛片网站| 美女 人体艺术 gogo| 国产探花在线观看一区二区| 白带黄色成豆腐渣| 日韩欧美 国产精品| 亚洲精品在线观看二区| 91麻豆精品激情在线观看国产| 女生性感内裤真人,穿戴方法视频| 欧美黑人巨大hd| 午夜精品久久久久久毛片777| 色av中文字幕| 亚洲欧美日韩高清在线视频| 少妇高潮的动态图| 亚洲中文字幕日韩| 男女午夜视频在线观看| 精品乱码久久久久久99久播| 日日干狠狠操夜夜爽| 日韩欧美精品免费久久 | 国产主播在线观看一区二区| 国产av不卡久久| 听说在线观看完整版免费高清| 麻豆国产av国片精品| 精品日产1卡2卡| 欧美最黄视频在线播放免费| 国产亚洲精品一区二区www| 国产精品1区2区在线观看.| 久久国产精品影院| 男女午夜视频在线观看| 午夜免费观看网址| 哪里可以看免费的av片| 国产精品三级大全| 免费观看的影片在线观看| 国产精品美女特级片免费视频播放器| 亚洲成a人片在线一区二区| 老司机午夜十八禁免费视频| 国产高清三级在线| 欧美3d第一页| 国产综合懂色| 国产精品野战在线观看| 亚洲成av人片在线播放无| 日本熟妇午夜| 免费无遮挡裸体视频| 免费av不卡在线播放| av天堂中文字幕网| 不卡一级毛片| h日本视频在线播放| 国产伦精品一区二区三区四那| 一本精品99久久精品77| 精品久久久久久久久久久久久| 精品一区二区三区av网在线观看| 可以在线观看毛片的网站| 亚洲av二区三区四区| 亚洲 欧美 日韩 在线 免费| 欧美最新免费一区二区三区 | 在线播放国产精品三级| 久久久国产成人精品二区| 欧美丝袜亚洲另类 | 99精品欧美一区二区三区四区| 最近最新中文字幕大全免费视频| 夜夜夜夜夜久久久久| 亚洲中文日韩欧美视频| 国产成人av激情在线播放| 男人和女人高潮做爰伦理| 毛片女人毛片| 欧美另类亚洲清纯唯美| 夜夜躁狠狠躁天天躁| 激情在线观看视频在线高清| 精品国产超薄肉色丝袜足j| 91久久精品电影网| 亚洲国产精品999在线| 日韩成人在线观看一区二区三区| 国产成年人精品一区二区| 精品熟女少妇八av免费久了| 国产熟女xx| 丁香欧美五月| 亚洲成av人片免费观看| 搞女人的毛片| 国产精品国产高清国产av| 国产99白浆流出| 亚洲av日韩精品久久久久久密| 国产成人欧美在线观看| 欧美日韩黄片免| 乱人视频在线观看| 黑人欧美特级aaaaaa片| 91av网一区二区| 一边摸一边抽搐一进一小说| 欧美日本视频| 99热只有精品国产| 成年女人毛片免费观看观看9| 婷婷精品国产亚洲av| 亚洲,欧美精品.| 无人区码免费观看不卡| 熟女电影av网| 18禁美女被吸乳视频| 精品人妻一区二区三区麻豆 | 19禁男女啪啪无遮挡网站| 两人在一起打扑克的视频| 老熟妇乱子伦视频在线观看| 一二三四社区在线视频社区8| 亚洲成a人片在线一区二区| 网址你懂的国产日韩在线| 波多野结衣高清作品| 国产日本99.免费观看| 国产黄片美女视频| 乱人视频在线观看| 色尼玛亚洲综合影院| 12—13女人毛片做爰片一| 观看美女的网站| 制服人妻中文乱码| 丁香欧美五月| 国产成人av教育| 岛国在线观看网站| a级毛片a级免费在线| 成人亚洲精品av一区二区| 亚洲 欧美 日韩 在线 免费| а√天堂www在线а√下载| xxx96com| 在线视频色国产色| 欧美日韩福利视频一区二区| 一级黄色大片毛片| 亚洲欧美一区二区三区黑人| 可以在线观看毛片的网站| 欧美bdsm另类| 中文字幕精品亚洲无线码一区| 少妇高潮的动态图| 一个人免费在线观看的高清视频| 国产 一区 欧美 日韩| 国产男靠女视频免费网站| 久久久久国内视频| 人人妻人人看人人澡| 亚洲美女视频黄频| 欧美中文日本在线观看视频| 精品人妻偷拍中文字幕| 中国美女看黄片| 亚洲中文日韩欧美视频| 色吧在线观看| 国产97色在线日韩免费| 精品不卡国产一区二区三区| 亚洲av一区综合| 最新美女视频免费是黄的| 亚洲精品在线观看二区| 最近最新免费中文字幕在线| 香蕉久久夜色| 国产成人福利小说| 18禁国产床啪视频网站| 乱人视频在线观看| 亚洲成人久久爱视频| 高潮久久久久久久久久久不卡| 成人国产综合亚洲| 亚洲真实伦在线观看| 琪琪午夜伦伦电影理论片6080| 女警被强在线播放| 人人妻人人看人人澡| 好男人电影高清在线观看| 亚洲精品国产精品久久久不卡| 可以在线观看的亚洲视频| 国产探花在线观看一区二区| 国产精品综合久久久久久久免费| 岛国视频午夜一区免费看| 男插女下体视频免费在线播放| 国产高清videossex| 在线观看66精品国产| 精品乱码久久久久久99久播| 午夜免费激情av| 99久久成人亚洲精品观看| 久久国产精品影院| 一进一出好大好爽视频| 亚洲精华国产精华精| 亚洲男人的天堂狠狠| 国产精品99久久99久久久不卡| 亚洲精品成人久久久久久| 日本免费a在线| 成熟少妇高潮喷水视频| 国产精品亚洲美女久久久| 亚洲成人精品中文字幕电影| 露出奶头的视频| 午夜精品在线福利| 亚洲av成人精品一区久久| 国产午夜福利久久久久久| 色吧在线观看| 亚洲最大成人手机在线| 夜夜躁狠狠躁天天躁| 老熟妇仑乱视频hdxx| 长腿黑丝高跟| 国产成人av教育| 亚洲无线观看免费| 男女午夜视频在线观看| 一个人免费在线观看的高清视频| 欧美3d第一页| 国产黄片美女视频| 亚洲18禁久久av| 女警被强在线播放| 国产伦在线观看视频一区| 日韩 欧美 亚洲 中文字幕| 欧美zozozo另类| 观看免费一级毛片| 国产免费一级a男人的天堂| 日韩欧美三级三区| 一本一本综合久久| 国产高清三级在线| 中文字幕av成人在线电影| 国产私拍福利视频在线观看| 我要搜黄色片| 老司机午夜十八禁免费视频| 久久久久免费精品人妻一区二区| 久久欧美精品欧美久久欧美| 叶爱在线成人免费视频播放| 国产视频内射| 搞女人的毛片| av欧美777| 在线观看午夜福利视频| 欧美3d第一页| 免费无遮挡裸体视频| 99热只有精品国产| 久久九九热精品免费| 亚洲国产欧美网| 精品人妻1区二区| 免费观看人在逋| 亚洲av电影不卡..在线观看| 日韩中文字幕欧美一区二区| 天天添夜夜摸| 18+在线观看网站| 国产欧美日韩精品亚洲av| 高清在线国产一区| 国产免费av片在线观看野外av| 成年免费大片在线观看| 免费看a级黄色片| 熟女人妻精品中文字幕| ponron亚洲| 给我免费播放毛片高清在线观看| 成人特级黄色片久久久久久久| 一个人观看的视频www高清免费观看| 国产精品亚洲美女久久久| 欧美日韩中文字幕国产精品一区二区三区| 99热精品在线国产| 国产黄a三级三级三级人| 国产aⅴ精品一区二区三区波| 中文字幕人成人乱码亚洲影| 精品日产1卡2卡| 国产午夜精品久久久久久一区二区三区 | 熟女人妻精品中文字幕| 午夜福利高清视频| 亚洲av免费高清在线观看| 在线观看免费视频日本深夜| 亚洲精华国产精华精| 久久久久国产精品人妻aⅴ院| av在线天堂中文字幕| 美女被艹到高潮喷水动态| 男女床上黄色一级片免费看| 欧美一级a爱片免费观看看| 欧美午夜高清在线| 国产 一区 欧美 日韩| 婷婷六月久久综合丁香| 亚洲精品乱码久久久v下载方式 | 国产激情偷乱视频一区二区| 亚洲内射少妇av| 亚洲在线观看片| 久久中文看片网| 国内久久婷婷六月综合欲色啪| 欧美在线黄色| 成年女人毛片免费观看观看9| 亚洲真实伦在线观看| 少妇人妻精品综合一区二区 | 少妇人妻一区二区三区视频| 国产成人欧美在线观看| 18禁黄网站禁片免费观看直播| www日本在线高清视频| 男女床上黄色一级片免费看| 亚洲第一欧美日韩一区二区三区| 久久久久久人人人人人| 在线观看66精品国产| 欧美午夜高清在线| 国产v大片淫在线免费观看| 国产精品亚洲美女久久久| 99精品欧美一区二区三区四区| 成年女人毛片免费观看观看9| 麻豆成人av在线观看| 噜噜噜噜噜久久久久久91| 国产色爽女视频免费观看| 大型黄色视频在线免费观看| 亚洲精品影视一区二区三区av| 搡老熟女国产l中国老女人| www.999成人在线观看| 精品日产1卡2卡| 国产精品一区二区三区四区免费观看 | 久久久久久久午夜电影| 免费av观看视频| 精品久久久久久成人av| 99热精品在线国产| 熟女电影av网| 变态另类丝袜制服| 欧洲精品卡2卡3卡4卡5卡区| 91九色精品人成在线观看| avwww免费| 青草久久国产| 国产午夜精品论理片| 国产伦精品一区二区三区视频9 | 丰满的人妻完整版| 亚洲狠狠婷婷综合久久图片| 非洲黑人性xxxx精品又粗又长| 日韩国内少妇激情av| 91麻豆精品激情在线观看国产| 在线观看日韩欧美| 亚洲国产精品合色在线| 亚洲av免费在线观看| 成人性生交大片免费视频hd| 国产探花在线观看一区二区| 久久精品国产自在天天线| 欧美色视频一区免费| 久久精品亚洲精品国产色婷小说| 18禁国产床啪视频网站| 99久久精品国产亚洲精品| 岛国在线观看网站| 五月玫瑰六月丁香| 狂野欧美激情性xxxx| 婷婷亚洲欧美| 国产高清激情床上av| 欧美成狂野欧美在线观看| 少妇的逼水好多| 午夜a级毛片| 国产欧美日韩一区二区精品| 婷婷亚洲欧美| 国产精品免费一区二区三区在线| 国产成人av教育| 国产亚洲精品一区二区www| 日韩欧美三级三区| 免费在线观看亚洲国产| 欧美日韩精品网址| 亚洲内射少妇av| 精品久久久久久成人av| 亚洲中文字幕一区二区三区有码在线看| 免费观看人在逋| 日韩欧美在线二视频| 久久精品人妻少妇| 欧美性猛交黑人性爽| 黄色丝袜av网址大全| 成人国产一区最新在线观看| 国产精品久久视频播放| 看黄色毛片网站| 高清日韩中文字幕在线| 18禁黄网站禁片午夜丰满| 黄色成人免费大全| 国产一区二区三区在线臀色熟女| 亚洲天堂国产精品一区在线| 2021天堂中文幕一二区在线观| 色精品久久人妻99蜜桃| 色综合婷婷激情| 亚洲av免费在线观看| 在线免费观看不下载黄p国产 | 天天躁日日操中文字幕| 午夜免费男女啪啪视频观看 | 国产伦精品一区二区三区视频9 | 国产伦精品一区二区三区四那| 日韩 欧美 亚洲 中文字幕| 成人性生交大片免费视频hd| 九九在线视频观看精品| 亚洲欧美一区二区三区黑人| 少妇的逼水好多| 天堂动漫精品| av黄色大香蕉| avwww免费| 免费看日本二区| 久久欧美精品欧美久久欧美| 欧美色视频一区免费| 三级男女做爰猛烈吃奶摸视频| 欧美成人性av电影在线观看| 午夜免费男女啪啪视频观看 | 黄片大片在线免费观看| 一个人看的www免费观看视频| 国产黄色小视频在线观看| 9191精品国产免费久久| 国产精品三级大全| 国产高清三级在线| 亚洲成人中文字幕在线播放| 国产亚洲欧美98| 精品电影一区二区在线| 午夜精品在线福利| 亚洲最大成人中文| av在线天堂中文字幕| 免费在线观看日本一区| 国产高清激情床上av| 女人被狂操c到高潮| 99国产极品粉嫩在线观看| 精品熟女少妇八av免费久了| 欧美一区二区精品小视频在线| 男人的好看免费观看在线视频| 岛国在线观看网站| 淫秽高清视频在线观看| 老师上课跳d突然被开到最大视频 久久午夜综合久久蜜桃 | 麻豆一二三区av精品| 午夜免费观看网址| 国产av不卡久久| 1024手机看黄色片| 无限看片的www在线观看| a级毛片a级免费在线| 国产av麻豆久久久久久久| 男女做爰动态图高潮gif福利片| 成年免费大片在线观看| 亚洲专区中文字幕在线| 亚洲av免费高清在线观看| 欧美三级亚洲精品| 性色avwww在线观看| 精品福利观看| 欧美激情在线99| 国产伦在线观看视频一区| 变态另类丝袜制服| 一本精品99久久精品77| 3wmmmm亚洲av在线观看| 国产亚洲精品久久久com| 日韩国内少妇激情av| 亚洲av第一区精品v没综合| 欧美大码av| 日韩精品青青久久久久久| 国产真实乱freesex| 成年女人看的毛片在线观看| 男插女下体视频免费在线播放| 国产精品99久久99久久久不卡| 90打野战视频偷拍视频| 国内精品久久久久精免费| 国产欧美日韩精品亚洲av| 国产色爽女视频免费观看| www.色视频.com| 欧美国产日韩亚洲一区| 欧美在线黄色| 少妇的丰满在线观看| 国产精品久久久久久亚洲av鲁大| 一进一出抽搐动态| 日韩免费av在线播放| 久久午夜亚洲精品久久| 天堂网av新在线| 88av欧美| 真实男女啪啪啪动态图| 国产免费av片在线观看野外av| 亚洲av电影不卡..在线观看| 免费看a级黄色片| 亚洲欧美激情综合另类| 1000部很黄的大片| 亚洲精品影视一区二区三区av| 免费av观看视频| 国产精品日韩av在线免费观看| 国产又黄又爽又无遮挡在线| 在线观看av片永久免费下载| 国产亚洲精品久久久com| 又紧又爽又黄一区二区| 69av精品久久久久久| 中文资源天堂在线| 天堂动漫精品| 久久人妻av系列| 亚洲美女视频黄频| 亚洲欧美精品综合久久99| 亚洲自拍偷在线| bbb黄色大片| 精品国产超薄肉色丝袜足j| 啪啪无遮挡十八禁网站| 香蕉久久夜色| 成人特级av手机在线观看| 国产成人a区在线观看| 日韩欧美一区二区三区在线观看| 成人亚洲精品av一区二区| 亚洲乱码一区二区免费版| 亚洲成人久久爱视频| 国产高清视频在线播放一区| 男人和女人高潮做爰伦理| 欧美日韩黄片免| 性色avwww在线观看| 在线天堂最新版资源| 亚洲精华国产精华精| 日韩精品中文字幕看吧| 少妇裸体淫交视频免费看高清| 久久久久久久久中文| 久久精品影院6| 99久久成人亚洲精品观看| 亚洲国产精品999在线| 一级作爱视频免费观看| 午夜福利在线观看免费完整高清在 | 狂野欧美激情性xxxx| 2021天堂中文幕一二区在线观| 18禁黄网站禁片午夜丰满| 一进一出抽搐gif免费好疼| 久久九九热精品免费| av福利片在线观看| 亚洲国产精品成人综合色| 国产精品国产高清国产av| 18禁裸乳无遮挡免费网站照片| 免费在线观看影片大全网站| 久久久久性生活片| 亚洲国产精品999在线| 欧美极品一区二区三区四区| 免费av毛片视频| 脱女人内裤的视频| 一个人免费在线观看的高清视频| 亚洲一区二区三区不卡视频| 免费人成视频x8x8入口观看| 少妇熟女aⅴ在线视频| 亚洲av第一区精品v没综合| 日韩欧美国产在线观看| 国产主播在线观看一区二区| 91麻豆av在线| 午夜福利欧美成人| 狂野欧美激情性xxxx| 国产真人三级小视频在线观看| 午夜激情福利司机影院| 久久久久亚洲av毛片大全| av片东京热男人的天堂| 亚洲精品在线观看二区| 桃色一区二区三区在线观看| 欧美+亚洲+日韩+国产| 最近在线观看免费完整版| 不卡一级毛片| 欧美日韩一级在线毛片| 欧美一区二区精品小视频在线| 好男人在线观看高清免费视频| 全区人妻精品视频| www.www免费av| 免费av不卡在线播放| 男女视频在线观看网站免费| 免费一级毛片在线播放高清视频| 老汉色av国产亚洲站长工具| 国产精品永久免费网站| 啦啦啦免费观看视频1| 欧美黄色淫秽网站| 国产男靠女视频免费网站| 久9热在线精品视频| 在线观看66精品国产| 国产精品久久久久久人妻精品电影| 国产熟女xx| 久久久精品欧美日韩精品| 日韩国内少妇激情av| 亚洲五月天丁香| 亚洲精品在线美女| 欧美成狂野欧美在线观看| 中文字幕av成人在线电影| 亚洲成a人片在线一区二区| 久久国产乱子伦精品免费另类| 亚洲精品456在线播放app | av片东京热男人的天堂| 亚洲乱码一区二区免费版| 国产精品久久久久久久久免 | 99国产精品一区二区三区| 亚洲精华国产精华精| 欧美日韩黄片免| 亚洲人成伊人成综合网2020| 久久国产乱子伦精品免费另类| 蜜桃亚洲精品一区二区三区|