ErxYb1-x（TPB）3Bath（x=0，0.218，0.799，0.896，0.987，1）配合物的近紅外發(fā)光性能

張慶瑞 鄧瑞平 劉英博 周 亮 張洪杰

ErxYb1-x（TPB）3Bath（x=0，0.218，0.799，0.896，0.987，1）配合物的近紅外發(fā)光性能

張慶瑞 鄧瑞平＊劉英博 周 亮 張洪杰＊

（中國科學院長春應用化學研究所，長春 130022）

采用4,4,4-三氟-1-苯基-1,3-丁二酮（TPB）為第一配體,4,7-二苯基-1,10-菲咯啉（Bath）為第二配體,分別制備了配合物Er（TPB）3Bath 和 Yb（TPB）3Bath,以及它們的混合配合物 ErxYb1-x（TPB）3Bath（x=0.218,0.799,0.896,0.987）,并對所制得配合物的發(fā)光性能進行了系統(tǒng)研究。研究結果表明,所有配合物均能發(fā)射所含稀土離子的近紅外特征光,并且可以通過調(diào)節(jié)混合配合物中的nEr/nYb來調(diào)控Yb3+/Er3+之間的能量傳遞,進而提高Er3+離子在1 530 nm處的發(fā)光。

稀土配合物；近紅外發(fā)光；能量傳遞

0 Introduction

Rare earth （RE）complexes are the most promising luminescent materials with appealing features，such as large stock shift，sharp emission bands，long lifetimes，and high quantum efficiency，etc.，which render them potential applications in the fields of bio-imaging，laser systems，optical amplification，organic lightemitting diodes，and pressure/disorder sensors［1-9]，etc.Among rare earth complexes，the nearinfrared emitting complexes，such as Yb3+，Er3+，Nd3+，Ho3+，Pr3+complexes，etc.，have been intensely studied in the past decades［10-15].There are two particular driving forces for these researches:one is the rapid development of telecommunication networks;the other is the vivo sensing and imaging in bio-applications［16].Er3+-basedmaterials play a special role in telecommunication technologies since they emit characteristic emission at～1.55 μm （0.8 eV），thus covering a spectroscopic window in which glass optical fibers show high transparency （the so-called third-communication window）［17].The organic erbium complexes have also attracted ever-increasing intention in recent years due to their advantages of easy processing and flexible molecular design，etc.，compared with their inorganic glass fibers counterparts［18].But for practical application in the fields of telecommunication，optical communication systems，or optical amplifiers，the NIR yield and efficiency of the organic RE complexes should still be improved enormously.

Because of their small energy gaps between the emissive states and the ground states，theNIR luminescent RE3+ions usually suffer the problem of quenching from many phonon-related nonradiative processes，especially the vibrations of the C-H，N-H and O-H bonds in the organic complexes［19-20].To achieve high yield of NIR emission，one of the strategies is to use heavy atoms to replace the H atom in the ligands，and fluorination is a beneficial method［19-20].Another drawback of the RE-based NIR emitting complexes is the pervasive energy mismatch between theligandsand thecenterions.FormostRE complexes，their absorption or excitation bands locate mainly in ultraviolet region，which means that the excited states energy levels of ligands are much higher than the RE NIR emitting levels，thus giving rise to inefficient energy transfer from the ligand to the center ion，and therefore the unsatisfactory NIR quantum efficiency［21].In the past decade，many groups have devoted to designing and synthesizing novel RE complexes with low exciting energy levels，such as large conjugated systems，heterometallic complexes，etc.Among them，d-f block complexes are feasible choices，in which long-lived3MLCT states of d-f transition metals （e.g.Ru2+，Re+，Os2+，Au+，Pt2+，Ir3+）can be excited by visible light and transfer efficiently their energy onto the 4fnmanifolds，thus providing an efficient pathway for energy migration within heterometallic complexes［7，21-23].Mixed RE complexes，which have RE3+/RE3+couples and possible mutual energy transfer，are another useful approach to enhance the expected NIR yield［24-27].Yb3+ion is usually a prime candidate of the sensitizer to be chosen due to its high luminescent efficiency and relatively simple electronic structure of two energy level manifolds:the2F7/2ground state and2F5/2excited state around at 10 000 cm-1in the NIR region，especially for the Er3+complexes.Thanks to the energy match between the4I11/2level of Er3+and the2F5/2level of Yb3+，the energy transfer between excited state Yb3+ion and ground state Er3+ion can occur resonantly.This process is very efficient since the absorption cross section of Yb3+（about 10-20cm2）is one order of magnitude higher than that of Er3+（about 10-21cm2）［28].In this case，the Yb3+ion functions as the bridge between ligands and Er3+ion，thus enhancing the emission intensity of Er3+.

Herein we synthesized erbium and ytterbium complexes using fluorinated ligand TPB and large conjugated ligand Bath as the first and the second ligands，respectively.In addition，the mixed complexes ErxYb1-x（TFB）3Bath （x=0.218，0.799，0.896，and 0.987，respectively）were also prepared aiming to improve the Er3+emission intensity.Photoluminescence properties of the as-prepared complexes were investigated in detail，and the experimental results reveal thatallthe complexesexhibitthe characteristic transition of the Er3+and/or Yb3+ion.In the Er3+-Yb3+mixed systems，the emission intensity of Er3+ion can be enhanced by modulating the nEr/nYbto facilitate the energy transfer from Yb3+to Er3+ion.

1 Experimental

1.1 Materials and instruments

Ytterbium(Ⅲ) nitrate pentahydrate （99.9%），and erbium(Ⅲ) nitrate pentahydrate （99.9%），4，4，4-trifluoro-1-phenyl-1，3-butanedione （99.9%），4，7-diphenyl-1，10-phenanthroline （98%）were obtained commercially from Aladdin company and used as received without further purification.Excitation and emission spectra were measured with an Edinburgh FLSP 920 fluorescence spectrophotometer.The Er3+and Yb3+ion contents were measured by Thermo iCAP6300 ICP-OES.

1.2 Preparation of Er（TPB）3Bath

0.648 g （3 mmol）TPB and 0.332 g （1 mmol）Bath were dissolved in 15 mL ethanol，and NaOH aqueous（1 mmol·L-1）was added into it under stirring and heating to adjust the pH value to 6～8.Then，the solution of 0.449 g Er（NO3）3·5H2O （1 mmol）in 10 mL ethanol was dropped into the above solution.A lot of precipitates appeared.The reaction was kept under reflux for 3 h.After that，the precipitates were filtered and washed by de-ionized water and ethanol for several times，respectively.Finally，the precipitates were dried and recrystallized with acetone/ethanol mixed solvent，and the resulted products were dried at 80 ℃ under vacuum.Yield:0.78 g （68%）.

1.3 Preparation of Yb（TPB）3Bath

The same procedure as that of Er（TPB）3Bath.Yield:76%.

1.4 Preparation of ErxYb1-x（TPB）3Bath

The same procedure as that of Er（TPB）3Bath，but herein the Er（NO3）3/Yb （NO3）3mixed solution with different nEr/nYb，instead of pure Er（NO3）3or Yb（NO3）3，was added.

Er0.218Yb0.782（TPB）3Bath:0.2 mmol Er（NO3）3+0.8 mmol Yb（NO3）3was added.Yield:65%.Elemental analysis:Er:28 540 μg·g-1，Yb:106 200 μg·g-1.

Er0.896Yb0.104（TPB）3Bath:0.5 mmol Er（NO3）3+0.5 mmol Yb（NO3）3was added.Yield:72%.Elemental analysis:Er:88 020 μg·g-1，Yb:11 300 μg·g-1.

Er0.799Yb0.201（TPB）3Bath:0.8 mmol Er（NO3）3+0.2 mmol Yb（NO3）3was added.Yield:70%.Elemental analysis:Er:137 800 μg·g-1，Yb:2 036 μg·g-1.

Er0.987Yb0.013（TPB）3Bath:0.9 mmol Er（NO3）3+0.1 mmol Yb（NO3）3was added.Yield:66%.Elemental analysis:Er:155 300 μg·g-1，Yb:11 300 μg·g-1.

2 Results and discussion

The preparation routes of these complexes are shown in Scheme 1.

Scheme 1 Preparation routes of RE（TPB）3Bath

The mixed complexes ErxYb1-x（TPB）3Bath were synthesized by using the Er（NO3）3/Yb （NO3）3mixed solution with differentnEr/nYbas the rare earth sources.The actual Er3+and Yb3+content in the as-prepared complexes were detected by means of ICP.And the mixed ErxYb1-x（TPB）3Bath complexes were denoted by the detected results，as shown in Table 1.

The photoluminescence properties of the Er（TPB）3Bath and Yb（TPB）3Bath were investigated firstly.Fig.1 shows the excitation and emission spectra of Er（TPB）3Bath and Yb（TPB）3Bath.There are three obvious bands in the excitation spectrum of Er（TPB）3Bath，locating at 374，463 and 520 nm，respectively.The strongest one at 374 nm can be ascribed to the π-π*transition of the ligands.And the band at 463 nm can be ascribed to the additive contribution from the ligands and the transition of4I15/2→4H7/2from Er3+ion［26].The sharp peak at 520 nm can be contributed to the transition of4I15/2→2H11/2［26，29].As depicted in its emission spectrum，the Er（TPB）3Bath complex emit its characteristic emission peaked at 1 530 nm，which is originated from the4I13/2→4I15/2transition of Er3+ion.

Table 1 Raw and detected nEr/nYbfor the mixed complexes ErxYb1-x（TPB）3Bath

Fig.1 Excitation （Ex）and emission （Em）spectra of Er（TPB）3Bath and Yb（TPB）3Bath

The Yb（TPB）3Bath exhibit similar excitation spectrum with that of Er（TPB）3Bath，locating mainly at 378 nm with a shoulder band at about 445 nm，which can beascribed to the contribution ofligands.However，the transition of the Yb3+ion is not observed in the excitation spectrum，which is rational because the Yb3+ion owns only one possible transition between its ground state and excited state locates in the NIR transition.Asshown in Fig.1，the Yb （TPB）3Bath complex shows a emission band in NIR region，split into three peaks at 976，1 005 and 1 031 nm，respectively，which is related with the coordination field effect of the ligands［30-32].

To enhance the emission yield of the Er3+ion，we prepared a series of mixed ErxYb1-x（TPB）3Bath （x=0.218，0.799，0.896，and 0.987，respectively）complexes because the presence of Yb3+was expected to facilitate the energy transfer from ligands to Er3+ions.The photoluminescence properties of these complexes were investigated.For better comparison，all the emission spectra were measured under the same conditions.Firstly，we investigate the effect of excitation source （374 or 378 nm）on the emission spectra，and the experimental results show that 378 nm excitation source causes slightly higher emission intensities of both Yb3+and Er3+ions than that from 374 nm source.Fig.2 compares the emission spectra of complexes Er0.896Yb0.104（TPB）3Bath and Er0.218Yb0.782（TPB）3Bath under the excitation of 374 and 378 nm，respectively.

What should be noted is the possible energy transfer from Yb3+to Er3+ion.As mentioned above，the 378 nm excitation source corresponds to the maximum excitation of the obtained Yb3+complex.Compared with Er3+ion，the Yb3+ion possesses wider absorption cross section，which is helpful in harvesting the energy from ligands.In this case，part excited energy of Yb3+ion would be transferred to the Er3+ion，thus enhancing the emission of Er3+ion.So，the enhanced Er3+emission can be interpreted as the improved energy transfer from Yb3+to Er3+ion.

The energy transfer between Yb3+/Er3+ions and the enhancement of Er3+emission were found to be more obvious by comparing the emission spectra of the mixed ErxYb1-x（TPB）3Bath （x=0.218，0.799，0.896，and 0.987，respectively）complexes with that of the pure Er（TPB）3Bath complex.Under excitation at 378 nm，the emission intensity of the ErxYb1-x（TPB）3Bath varied with different nEr/nYb（Fig.3）.Fig.3a depicts the emission spectra of the ErxYb1-x（TPB）3Bath （x=0.218，0.799，0.896，and 0.987，respectively）complexes and Er（TPB）3Bath.It could be found that the emission intensity of Yb3+ion （Em-Yb）is dominated in the cases of x=0.218 and 0.799，while Em-Yb and the emission intensity of Er3+ion （Em-Er）is comparable when x=0.896 （Fig.2a）.

Fig.2 Emission spectra of （a）Er0.896Yb0.104（TPB）3Bath and （b）Er0.218Yb0.782（TPB）3Bath

Fig.3 Emission spectra of the ErxYb1-x（TPB）3Bath （x=0.218，0.799，0.896，0.987，1，respectively）excited at 378 nm （a）whole emission spectra and （b）emission spectra of the Er3+ion

Scheme 2 Energy transfer between Yb3+/Er3+ion，here the higher energy levels of Er3+ion are omitted

As far as the Em-Er is concerned，it varies with the nEr/nYbalso，but the variation should be distinguished carefully.As shown in Fig.3b，the intensity order of the Em-Er of the mixed complexes is Er0.799Yb0.201（TPB）3Bath ＞ Er0.896Yb0.104（TPB）3Bath=Er0.218Yb0.782（TPB）3Bath ＞Er（TPB）3Bath ＞ Er0.987Yb0.013（TPB）3Bath.With the increasing ratio of Er3+ion from x=0.218 to 0.896，the mixed complexes show enhanced Em-Er，which is higher than that of Er（TPB）3Bath.This result confirm the presence of energy transfer from Yb3+ion to Er3+ion in these cases.Based on theory and experimental results，the energy processes involved in these mixed complexes was analyzed and depicted in Scheme 2.It is found that there is an optimal nEr/nYbfor the mixed complexes.The Em-Er is most desirable when x=0.799，but further increasing x to 0.896，it decreased to the level as that of the case of x=0.218，and further increasing x to 0.987 causes the rapid decrease of Em-Er to even lower than that of the Er（TPB）3Bath complex.In this case，back energy transfer from Er3+to Yb3+ion was suggested to responsible forthis phenomenon［26].Furtherinvestigation aboutthis phenomenon should be performed in future.

3 Conclusions

In summary，a series of complexes based on ErxYb1-x（TPB）3Bath （x=0，0.218，0.799，0.896，0.987，and 1，respectively）with TPB and Bath as the first and second ligands，respectively，were prepared.Their luminescence properties of these obtained complexes were investigated experimentally.Allthe mixed complexes exhibit the characteristic emission of Yb3+and Er3+ion.Interestingly，the emission intensity of Er3+ion can be enhanced by appropriately modulating the nEr/nYb.When x=0.799，the correspond mixed complexes realize the highest emission intensity of Er3+ion attributed to the energy transfer from Yb3+to Er3+ion.

［1]Chen X Y，Yang X，Holliday B.J.Am.Chem.Soc.，2008，130:1546-1547

［2]Xin H，Li F Y，Shi M，et al.J.Am.Chem.Soc.，2003，125:7166-7167

［3]Deng R P，Yu J B，Zhang H J，et al.Chem.Phys.Lett.，2007，443:258-263

［4]Harbuzaru B，Corma A，Rey F，et al.Angew.Chem.Int.Ed.，2009，48:6476-6479

［5]Harbuzaru B，Corma A，Rey F，et al.Angew.Chem.Int.Ed.，2008，47:1080-1083

［6]Bünzli J G.Chem.Rev.，2010，110:2729-2755

［7]Eliseeva S，Bünzli J G.Chem.Soc.Rev.，2010，39:189-227

［8]Stachowicz M，Kozanecki A，Lin J Y，et al.Opt.Mater.，2014，36:1730-1733

［9]Chen B T，Dong B，Wang J，et al.Nanoscale，2013，5:8541-8549

［10]Stacey O，Ward B，Amoroso A，et al.Dalton Trans.，2016，45:6674-6681

［11]Gai Y L，Xiong K C，Chen L，et al.Inorg.Chem.，2012，51:13128-13137

［12]Moore B F，Kumar G A，Tan M C，et al.J.Am.Chem.Soc.，2011，133:373-378

［13]Pawlak N，Oczko G，Starynowicz P，et al.Polyhedron，2015，101:152-159

［14]QIU Yan-Nan（仇衍楠），SUN Li-Ning （孫麗寧），LIU Tao（劉濤），et al.J.Chin.Soc.Rare Earths（中國稀土學報），2012，30（2）:129-145

［15]Mitra S，Jana S.J.Fluoresc.，2015，25:541-549

［16]Sun Q Y，Yan P F，Niu W Y，et al.RSC Adv.，2015，5:65856-65861

［17]Artizzu F，Mercuri M L，Serpe A，et al.Coord.Chem.Rev.，2011，255:2514-2529

［18]ZHOU Shi-Feng（周時鳳）.Thesis for the Doctorate of Zhejiang University（浙江大學博士論文）.2008.

［19]Glover P B，Bassett A P，Nockemann P，et al.Chem.Eur.J.，2007，13:6308-6320

［20]Bünzli J G.Coord.Chem.Rev.，2015，293-294:19-47

［21]Chen F F，Chen Z Q，Bian Z Q，et al.Coord.Chem.Rev.，2010，254:991-1010

［22]Lü Q，F(xiàn)eng W X，Hui Y N，et al.Eur.J.Inorg.Chem.，2010:2714-2722

［23]YU Gang（禹鋼），BIAN Zu-Qiang（卞祖強），LIU Zhi-Wei（劉志偉），et al.Sci.China Chem.（中國科學:化學），2014，44:267-276

［24]Yang T H，F(xiàn)u L S，Rute A S.Eur.J.Inorg.Chem.，2015:4861-4868

［25]Faulkner S，Pope S.J.Am.Chem.Soc.，2003，125:10526-10527

［26]Rodríquez V D，Tikhomirov V K，Méndez-Ramos J，et al.Sol.Energy Mater.Sol.Cells，2010，94:1612-1617

［27]Tikhomirov V K，Rodríguez V D，Méndez-Ramos J，et al.Sol.Energy Mater.Sol.Cells，2012，100:209-215

［28]Miritello M，Cardile P，Savio R，et al.Opt.Express，2011，19:20761-20772

［29]Johnson N J，He S，Diao S，et al.J.Am.Chem.Soc.，2017，139:3275-3282

［30]Li W Z，Li J Y，Li H F，et al.J.Lumin.，2014，146:205-210

［31]Kang T S，Harrison B S，Bouguettaya M，et al.Adv.Funct.Mater.，2003，13:205-210

［32]Shu Y B，Liu W S.Sci.Chin.Chem.，2016，59:436-441

Near Infrared Luminescence Properties of the Complexes of ErxYb1-x（TPB）3Bath （x=0,0.218,0.799,0.896,0.987,1）

ZHANG Qing-RuiDENG Rui-Ping＊LIU Ying-Bo ZHOU Liang ZHANG Hong-Jie＊
（Changchun Institute of Applied Chemistry,Chinese Academy of Sciences,Changchun 130022,China）

A series of near infrared （NIR）luminescent complexes based on ErxYb1-x（TPB）3Bath （where TPB=4，4，4-tri-fluoro-1-phenyl-1，3-butanedione，Bath=4，7-diphenyl-1，10-phenanthroline，x=0，0.218，0.799，0.896，0.987，1，respectively）were prepared by selecting TPB and Bath as the first and second ligands，respectively.Luminescence properties of these complexes were investigated in detail.All these complexes exhibit the characteristic emission of the Yb3+and/or Er3+ion in the NIR region，and the emission intensity of Er3+ion can be enhanced by modulating the nEr/nYb，which is related to the energy transfer from Yb3+to Er3+ions.

rare earth complex;near infrared luminescence;energy transfer

O614.3

A

1001-4861（2017）11-2011-06

10.11862/CJIC.2017.254

2017-08-18。收修改稿日期:2017-09-22。

國家自然科學基金（No.51502285）、自然科學基金創(chuàng)新群體（No.21521092）和科技部“973”計劃（No.2014CB643802）資助項目。

＊通信聯(lián)系人。E-mail:dengrp@ciac.ac.cn,hongjie@ciac.ac.cn