    Laser cut hole matrices in novel armour plate steel for appliqué battlefield vehicle protection

    2016-11-28 07:49:37DanielTHOMAS
    Defence Technology 2016年5期

    Daniel J.THOMAS*

    Engineering Manufacturing Centre,College of Engineering,Swansea University,Swansea,UK

    Available online 27 July 2016

    Laser cut hole matrices in novel armour plate steel for appliqué battlefield vehicle protection

    Daniel J.THOMAS*

    Engineering Manufacturing Centre,College of Engineering,Swansea University,Swansea,UK

    Available online 27 July 2016

    During this research,experimental rolled homogeneous armour steel was cast,annealed and laser cut to form an appliqué plate.This Martensitic–Bainitic microstructure steel grade was used to test a novel means of engineering lightweight armour.It was determined that a laser cutting speed of 1200 mm/min produced optimum hole formations with limited distortion.The array of holes acts as a double-edged solution,in that they provide weight saving of 45%,providing a protective advantage and increasing the surface area.Data collected were used to generate laser cut-edge hole projections in order to identify the optimum cutting speed,edge condition,cost and deformation performance.These parameters resulted in the generation of a surface,with less stress raising features.This can result in a distribution of stress across the wider surface.Provided that appropriate process parameters are used to generate laser cut edges,then the hardness properties of the surface can be controlled.This is due to compressive residual stresses produced in the near edge region as a result of metallurgical transformations.This way the traverse cutting speed parameter can be adjusted to alter critical surface characteristics and microstructural properties in close proximity to the cut-edge.A relationship was identified between the width of the laser HAZ and the hardness of the cut edge.It is the thickness of the HAZ that is affected by the laser process parameters which can be manipulated with adjusting the traverse cutting speed.

    ?2016 The Author.Production and hosting by Elsevier B.V.on behalf of China Ordnance Society.This is an open access article under the CC BY-NC-ND license(http://creativecommons.org/licenses/by-nc-nd/4.0/).

    Armour steels;Defence systems;Steel processing;Armour engineering

    1.Introduction

    Adaptive armour steel plate is a vital component towards providing a protective advantage for battlefield vehicles[1]. Currently,armour plate steels are an important component towards providing an energy absorbing barrier and countering threats from high energy projectiles,munitions and improvised explosive devices.Steel processing conditions and final microstructural and mechanical properties are critical factors that influence the characteristics of armour under dynamic loading conditions[2].

    Steels used in armour applications must have high yield strength,be hard and have high resistance to shock.These properties are critical towards resisting high velocity projectiles and critical knife-edge loads[3].Armour steels are produced by continuous casting,which is followed by hot rolling to theappropriate thickness.It is the hot rolling process that homogenises the grain structure,removing imperfections which can reduce the strength of the steel[4].Annealing and hot rolling elongatesthegrainmicrostructure,whichenablesadistributionof stress across a greater area.This is significant for knife-edge load energyresistance,asinthecaseoffragmentedmunitions,inwhich multiple highly localized forces impact across the steel structure, ratherthanconcentratedinasinglearea[5].Thealloyingelements, solidification temperature,and rolling heat treatment conditions arecriticaltowardstheprocessingofquenchedandtemperedsteel usedasarmour[6].Thehardnessofthearmourplaysasignificant role in the interaction with a projectile especially at high velocity [7].It is the resulting hardness which has a direct effect on the ballistic performance[8].

    Externally retrofitted armour steels are a useful means towards engineering low cost protection due to their usability and effective ballistic protection[9].A current armour technology is that of rolled homogeneous armour(RHA),which has martensitic/Bainitic or tempered martensitic/Bainitic matrix and is used in numerous battlefield equipment applications

    http://dx.doi.org/10.1016/j.dt.2016.07.002

    2214-9147/?2016 The Author.Production and hosting by Elsevier B.V.on behalf of China Ordnance Society.This is an open access article under the CC BY-NC-ND license(http://creativecommons.org/licenses/by-nc-nd/4.0/).

    Nomenclature

    Aelongation to failure

    HAZheat-affected zone

    HvVickers hardness

    kPakilopascal

    kVkilovolts

    Raarithmetic mean of departures from the mean line

    Rpmaximum height of profile above the mean line

    Rvmaximum depth of profile below the mean line

    Wtweight [10].Due to their crystalline lattice structure and microstructural properties,armour steels have combined strength,hardness and fracture toughness properties[11].This is combined with a high degree of energy absorption upon interaction with various projectiles.Armour failure is often caused by the decrease in resistance of the plate,often due to high retained austenite and coarser martensitic structure remaining after steel processing[12].The required performance level is determined by three factors:

    (1)The mass of the projectile;

    (2)The speed at which that projectile is travelling,and

    (3)The distance the projectile travels before intercepting the target.

    Bainitic-based microstructural steel offer a combined high strength and high toughness[13].Bainitic steels under high load conditions are attractive steels due to their increase in hardness in comparison with conventional to pearlite grades [14].Toughness is required for energy absorption of projectile energy under loading[15].Considering these approaches,tempered Bainitic steel having adequate hardness and toughness is a key combinative candidate as protective armour under high loading[16].

    Factors such as the heat-affected zone(HAZ)properties and the microstructural change of the material measured perpendicular to the surface of the cut-edge is critical in order to laser cut an array of holes[17].This is essentially caused by a rapid heating and cooling cycle during the laser cutting process.The size and properties of the HAZ are of importance due to the high potential for local degradation leading to embrittlement of the cut-edge hole.An important factor that influences the final condition of the HAZ includes the susceptibility of the steel chemistry to form a martensite phase near the cut-edge.

    Fig.1.Application of pierced rolled homogeneous armour steel plates retrofitted to a mobile battlefield equipment platform.

    Surface striations are primarily the cause for laser cut-edge roughness[18].Classifications of processing mechanisms to achieve an optimum cut-edge quality has been previously generated[19].To achieve high quality cut-edges in thicker steel plate,processing mechanisms comprise of a narrow operating window.It was found that quality can vary substantially with different cutting gas combinations and pressures[20].Furthermore,the influence of laser power and cutting speed are related to the formation of surface roughness,kerf width,heat-affected zone size,and surface morphology characteristics.

    Temperature distribution is localised in the thin cut-edge surface layer and the energy coupling at the workpiece surface is important in terms of determining the cut-edge quality.Using high power intensity can therefore result in the beam being absorbed by the workpiece material,which can cause undesirable solid-state heating,melting and vaporisation of the workpiece material as well as workpiece distortion[21].

    The key objective of this research is to find suitable laser process parameters to cut thousands of holes per square meter at a continuous operation to generate a perforated retrofit plate, as shown in Fig.1.

    The array of holes provide weight saving of 45%and also,by introducing holesto vehicle armour,providea protectiveadvantage[22–24].The perforated plate is a circular edge,rather than a hole,and when a projectile hits this edge it is deflected,which turns it from a sharp projectile into a blunt fragment;this makes it easier for the projectile to be stopped by vehicles with existing armour superstructure.Furthermore,the perforated armour also absorbs energy from land-based munitions across a greater surface area.

    2.Experimental methods

    2.1.Material properties

    The chemical composition and mechanical properties of the experimental armour steel used in this study are shown in Table 1.The steel was first cast and homogenisation annealing was performed on the slab at 1250°C,which was rolled at 1200°C through fifteen passes to produce a plate with a 10 mmthickness.It is annealed before laser cutting to give it the required high strength and hardness,for use in appliqué armour systems.The Martensitic and Bainitic microstructures of the steel are shown in Fig.2.

    Table 1 Steel chemistry(wt%)and mechanical properties.

    Fig.2.Experimental rolled homogeneous armour steel tempered Martensitic Bainitic microstructure,revealed with 5%Nital.

    Table 2 shows the heat treatment conditions applied on the experimental steel,which consists of austenisation,quenching, and finally tempering,in accordance to the standards of manufacturing armour steels.The mechanical properties and hardness were increased to produce tougher and more durable steel. Here the parent steel was heated up to a critical transformation temperature of 1000°C and then water quenched to cause the soft initial material to transform to a harder and stronger structure.

    Heating the material above the critical temperature causes carbon and the other elements to go into solid solution.The quenching process then freezes the microstructure,inducing stress.The steel plates were subsequently age tempered at 550°C for 60 min to transform the microstructure,achieve the appropriate hardness and eliminate the stresses.

    Tempering is done to develop the required combination of hardness,strength and toughness or to relieve the brittleness of fully hardened steels.The combination of quenching and tempering is important to make tough parts.Tempering is the process of reheating the steel at a relatively low temperature leading to precipitation and spheroidization of the carbides present in the microstructure.The tempering temperature and times are generally controlled to produce the final properties required of the steel.The result is a component with the appro-priate combination of hardness,strength and toughness for the intended application.

    Table 2 The heat treatment conditions of the armour steel.

    Fig.3.The Bystronic Bylas 3015 4.2 kW laser used to generate armour cut-edges.

    The steel is quenched and tempered to sustain a tough surface for providing a high degree of ballistic protection.

    2.2.Laser cut hole process parameters Laser cut-edges were performed using a Bystronic Bystar 4.2 kW laser,as shown in Fig.3.

    Table 3 shows the test matrix that was used for generating cut-edge specimens,in which the traverse cutting speed was the dominant process parameter.A set of cuts were also performed using 100%pure oxygen in order to test the interaction between cutting gas and the silicone content in the steel.

    Fig.4 shows the triangular lattice laser cutting configurations used during this study.The close proximity of each hole to the next hole results in 2800 holes per m2that were generated across the steel plate.

    2.3.Characterisation

    Surface micrographs of laser cut-edges were captured using a Leica optical light microscope.Microstructural characterisation and HAZ size measurements were analysed through observation of the specimens traverse to the cut-edge.Metallographic analysis of the near edge region microstructure was carried out by etching specimens using a 2%Nital reagent for 10 seconds.The microstructures were observed using a Reichert Polyvar optical microscope.In order to record and quantify cut-edge surface properties,a Taylor–Hobson form 2Talysurf was employed with scans being carried out across a two-dimensional surface area,providing an accurate representation of the cut-edge roughness and waviness data parameters together with the generation of axonometric profiles.The degree to which the cut-edge surfaces had hardened was measured as Hardness Vickers(Hv)microhardness,and measurements were taken using a Leco M-400-G2 hardness tester with a 500 g load.

    Table 3 Laser cutting test matrix of parameters used to generate holes and cut-edges test pieces.

    Fig.4.Dimensions of the triangular lattice hole configurations:10.0 mm diameter holes with spacing of 12.0 mm.

    Fig.5.90°V-bend formability test with an armour test piece.

    2.4.Formability testing

    Sections of the laser cut samples were cut to expose the edge as shown in Fig.5.The bending radius is the curvature,which was measured by bending the cut-edge samples.These were placed into a v-shaped die and then formed using a knife edge punch to a 90°angle.These samples were formed at a stoke speed of 250 mm/s using a Dartec 250 kN hydraulic testing machine.Following the test-piece unloading,edges were analysed under a microscope for visible signs of fractures.

    Induced cracking is based on both the hardness of the cutedge and also the roughness features formed on the surface during the cutting process.

    3.Results and discussion

    3.1.Topographical profiles of laser cut-edge surfaces

    The surface roughness profiles of the laser cut-edges are shown in Fig.6.There was observed to be only slightly different formations of striations across the range of traverse cutting speeds.This is due to the fact that the formation of striations is harnessed during the cutting process by the pulsing operation, which limits and controls the beam interaction.

    The surface roughness properties of the cut-edges examined are shown in Fig.7 where it was found that a traverse cutting speed of 1400 mm/min resulted in the smoothest cut-edge surface produced.Micrographs taken of the laser cut surfaces showed that there were more pronounced striations at a traverse cutting speed of 1000 mm/min.These features become less apparent as the traverse cutting speed was increased.However, these factors are important when considering the increase in surface area as striation properties are critical towards assessing the quality of the cut-edge surface.

    These features are also important from the perspective of their microstructural properties,which consists of martensite. At a low cutting speed of 1000 mm/min,due to the conductionof heat,this allows the temperature to rise away from the cut zone and applies more heat to the cut front and the formation of a wide isotherm.

    Fig.6.Surface axonometric profiles of laser cut-edges generated at cutting speeds of(a)1000 mm/min(b)1200 mm/min and(c)1400 mm/min.

    Fig.7.Surface roughness parameters of laser cut-edges showing the Ra(arithmetic mean of departures from the mean line),Rp(maximum height of profile above the mean line),and Rv(maximum depth of profile below the mean line) properties.

    Therefore,these results indicate that using a traverse cutting speed of 1400 mm/min will result in a surface which is optimum in terms of the formation of the most favourable surface roughness features.The microstructure around the zone of a cut-edge striation is shown in Fig.8,which consisted of martensite immediately close to the cut-edge,which was followed by the formation of some retained austenitic material, suggesting that the internal portion of the material would have cooled slower than the more critical surface.

    Fig.8.Cut through of the martensitic microstructure following the profile of a laser cut-edge striation.

    Furthermore,Fig.9 shows the striation patterns formed at the top and bottom regions of the cut-edges.There was a noted decrease in the definition of the striations towards the bottom of the cut-edges across the full range of traverse cutting speeds. This is as a result of the divergent beam which becomes less intense and with a larger diameter.In the region at the bottom of the cut-edge the cutting gas also becomes responsible for the cutting and generating the kerf[21].

    3.2.Laser heat-affected zone properties

    The HAZ thickness of a laser cut-edge is an important component in determining the cutting.As the traverse cutting speed is increased,less of the laser power is absorbed into the material during the cutting process.The energy is instead used to cut through the steel.The transverse profiles of the HAZ are shown in Fig.10,in which it was observed that at the lowest cutting speed of 1000 mm/min,the HAZ was widest.

    These results are quantified in Fig.11,in which the HAZ was observed to become thicker towards the bottom of the cut-edge across the full range of traverse cutting speeds.

    At the traverse cutting speed of 1000 mm/min the HAZ size was 0.05 mm wider in comparison with the cutting speed of 1200 mm/min.Between cutting speeds of 1200 mm/min and 1400 mm/min there was again a 0.05 mm reduced HAZ thickness.It was measured that the perpendicularity of laser cutedges did change as the traverse cutting speed was increased; these were measured as

    1000 mm/min=1.8°

    1200 mm/min=2.3°

    1400 mm/min=5.8°

    The slight angularity of the cut-edges produced as the traverse cutting speed was increased.As a result there are two independent factors that occur as the cutting speed is increased. There is a decrease in HAZ size and an increase in angularity of the cut-edge.Although this is less pronounced due to the use of pulsed laser cutting,it is important due to the fact that there is an increase in surface angle and subsequent surface area.This is critical towards the ballistic properties of the steel.

    Fig.9.The pattern of striations formed at(a)the top,and(b)the bottom of a cut-edge at a cutting speed of 1000 mm/min.

    Fig.10.Traverse profiles of the heat-affected zones generated at traverse cutting speeds of(a)1000 mm/min(b)1200 mm/min and(c)1400 mm/min.

    3.3.Laser cut-edge hole and surface characterisation

    Due to its highly focused properties and edge quality,laser cutting becomes the dominant procedure to perforate ultra hard armour products.Laser cutting was performed upon the steel in its post-annealed 725 Hv hardness condition.Fig.12 shows the quality of the cut holes produced at each set of cutting process parameters.The formation of a 10 mm laser cut hole provides an indication of cut-edge quality together with a suggestion of the quantity of dross generated during the process of cutting precise curvatures.These holes are later sectioned and bent to an angle of 45°to determine the formability limits of laser cut-edges.

    Fig.11.Heat-affected zone measured thickness formed transverse to the laser cut-edges.

    Laser through cuts are difficult to generate in the armour steel product due to the narrower spectrum of cutting process parameters as a result of the increased thickness of the material and the steel chemistry properties.

    Fig.12 shows the holes produced when using the matrix of cutting process parameters.It can be clearly seen that using a lower transverse cutting speed resulted in an increase in dross being deposited.Holes generated were also of lower quality, becoming slightly distorted at the location where the laser beam joins to form the final hole geometry.

    It was difficult to generate high quality laser cut-edges,as demonstrated by Fig.13(a).This was due to the fact that the steel product has 1.4%silicon as part of its chemistry which alters the viscosity of the laminar flow of liquid material as it reacts with the oxygen cutting gas during the laser cutting process.As a result,a mixture of 60%nitrogen and 40%oxygen cutting gas was used to produce high quality cut-edge surfaces at the most optimum speed,as shown in Fig.13(b).The increased concentration of Nitrogen was compensated by increasing the cutting gas pressure.

    As the traverse cutting speed was increased it was observed that the formation of striations at the bottom of the cut-edges became less pronounced,as shown in Fig.14.The striations became finer and further apart at the top of the cut-edge as the traverse cutting speed was increased because the pulsing frequency remained the same as the traverse cutting speed was increased.There were some irregular surface disruptions noticed on the cut surfaces.These are caused by an increased molten flow of steel.This happens as the number of holes cutincreases,resulting in the workpiece heating up.As a result there is increased surface melting.

    Fig.12.Underside regions of 10.0 mm laser cut-edge diameter holes generated using(a)1000 mm/min(b)1200 mm/min and(c)1400 mm/min cutting speeds, before removal of dross deposits.

    Fig.13.Micrographs of holes generated using(a)100%pure oxygen at 3.5 kW and 1000 mm/min and(b)40%oxygen,60%nitrogen at 3.5 kW and 1000 mm/min.

    The laser beam diameter and focal point on the steel workpiece is important to both the kerf width,hardness of the HAZ and the cut-edge surface roughness properties.A pulsing frequency on 65 Hz was used during the cutting process in order to in order to minimize the thermal distortion and reduce metallurgical deformations.

    Fig.15 shows the processes,which occur during the laser cutting operation in order to generate a hole.The first stage is the piercing mode,which involves the laser being momentarily switched to a high power piercing state 3.8 kW.This produces a hole in the workpiece before being switched back to the preset cutting speed and power parameters.During this process the cutting gas continues to flow at the same pressure.The laser hole piercing operation was carried out away from the cut-edge so that the edge would remain undamaged by splash formed during the piercing phase of the laser cutting process.

    3.4.Laser cut-edge hardness

    The transverse hardness profile of a laser cut-edge generated at different traverse cutting speeds is shown in Fig.16.When comparing the hardness properties of the laser cut-edges it was observed that there is a significant increase in the cut-edge hardness.It was observed that there is a gradual increase in the hardness through the thickness of the cut-edge.This is because the laser bed on which the steel is mounted acts as a heat sink and subsequently quenches the steel.Faster cutting rates result in an increase in hardness.Using cutting speeds of 1000 mm/ min results in maximum hardness,peaking to 1158 Hv;the hardness increases to 1358 Hvat a traverse cutting speed of 1400 mm/min.

    The profile at a traverse cutting speed of 1400 mm/min was observed to increase hardness by an average of 633 Hv compared with a cutting speed of 1000 mm/min in which the hardness increased by 433 Hv.

    These results suggest that there is an interrelationship between the HAZ thickness and the surface hardness,in that although there was a narrower HAZ at 1400 mm/min,the cutedge surface was harder.The reason why the cut-edge hardness increases by so much is significantly due to the cutting gas properties.The Nitrogen content of 60%results in a quick cooling cycle.Subsequently there is an alteration in the metallurgical properties of the steel.This results in the formation ofmartensitic phases in the area close to the cut-edge.The hardness properties of the steel in this case are not necessarily a negative attribute.

    Fig.14.Striations formed on laser cut-edge surfaces at each traverse cutting speed.Micrographs of laser cut-edge surfaces at traverse cutting speeds of(a) 1000 mm/min(b)1200 mm/min and(c)1400 mm/min.

    Fig.15.The operations performed during the laser cutting process(a)Piercing mode,(b)switch to pre-set process settings,and(c)continuous cutting of the hole.

    Fig.16.Transverse surface hardness profiles of laser cut-edges produced using the different process parameters.

    3.5.Laser cut-edge microstructural properties

    The microstructure and hardness of the steel was also observed to increase from the top to the bottom of the cut-edge. This is as a result of the interaction between the laser beam,the cutting gas properties and quenching from the laser bed.During this study the laser beam focuses on the surface of the steel, with the beam diverging throughout the workpiece thickness. As a result the cutting gas properties become very important. Here the pressure of the cutting gas and its properties pushes the molten steel through the kerf.Much of the heat is subsequently removed in the formation of the liquid metal.Some of this cooler material is deposited in the form of dross which becomes formed on the underside of the cut-edge.

    As seen it has been seen,every step in the formation of the armour steel alloy,from casting and heat treatment,to rolling and annealing,contributes to the microstructure properties of the final product.Laser cutting also has an effect on altering the metallurgical microstructure of the steel.This is important due to the large number of holes that are cut within the workpiece. During the cutting process the workpiece heats up as a result of thermal absorption of the laser energy.The steel as a result starts off cool and increases in temperature as each subsequent hole is cut.

    As the traverse cutting speed was increased to 1200 mm/min it was observed that there was a greater quantity of martensite in the region closest to the cut-edge surface as shown in Fig.17. At a 200 μm distance from the cut-edge there was still a component of martensite intermixed with wider regions of Bainitic phase found.

    These results indicate that as the traverse cutting speed is increased,there is the susceptibility for the formation of a greater quantity of martensitic material and it is this factor that results in the increase of the surface hardness.These observations also align to the HAZ and hardness measurements of the cut-edge and indicate that precisely controlling the traverse cutting speed can also influence the intrinsic mechanical properties of the cut-edge surface region.

    Fig.17.Micrograph of the microstructure in the HAZ regions generated at a traverse speed of 1200 mm/min.

    A significant proportion of heat is concentrated in the melted material and removed from the kerf via the pressurized shielding gas.It was concluded that the temperature distribution is localised in the thin cut-edge surface layer and the energy coupling at the workpiece surface is important in terms of determining the cut-edge quality.Using a lower traverse cutting speed,as was in the case when cutting at a speed of 1000 mm/ min results in the beam being absorbed by the workpiece material,can cause undesirable solid-state heating,melting and vaporisation of the workpiece material as well as further problems such as workpiece distortion.

    3.6.Edge formability properties

    During the process of 90°edge bending at a sudden impact speed of 250 mm/s there was significant region where cut-edge cracks were observed.This was when the bottom regions of the laser cut-edges were placed under the highest degree of tension during the bending process.

    Laser cracks were more predominant at lower traverse cutting speeds and after extensive analysis it was revealed that the cut-edge hardness was less critical and it was in fact the surface properties of the striation features that resulted in the formation of cracks.Fig.18 shows the cracks formed when the bottom of laser cut-edges were put under tension.The cut-edges produced at a traverse cutting speed of 1400 mm/min were harder than those produced at 1000 mm/min,although there were more cracks formed at a traverse cutting speed of 1000 mm/min.

    When comparing the data,it is logical to suggest that formability fractures produced during the bending operation initiated from deeper striations,and that this is more significant to cracking than the cut-edge hardness properties.As it is shown in Fig.18 at a traverse cutting speed of 1000 mm/min,this resulted in the formation of deep striations that as a result opened up to form cracks during the bending process.

    Although it could not be positively determined,the microstructure of the bottom region of the workpiece may also suggest that this was the region of crack initiation,which was determined to initiate from a corner region where hard martensite was formed during the cutting process.

    The regions close to the cut-edge were found to transform back to the parent Martensitic–Bainitic microstructure in a gradual process consisting of different microstructural regions as shown in Fig.13.

    Fig.18.Cracks formed with the bottom of the laser cut-edge in tension at traverse cutting speeds of(a)1000 mm/min(b)1200 mm/min,and(c)1400 mm/min.

    4.Conclusions

    The formation of an Appliqué armour plate has been found to be suitable for manufacturing using laser cutting processes.The array of holes acts as a double-edged solution,in that they provide weight saving of 45%and,although it may seem like an atypical solution,introducing holes to vehicle armour provides a protective advantage.The perforated armour is a circular edge rather than a holeandwhenaprojectilehitsthisedge,itgetsdeflectedandturns froma sharp projectile into a bluntfragmentwhichmakesiteasier to stop by the vehicles existing armour superstructure.Furthermore,the perforated armour also absorbs energy from explosions across a greater surface area.These manufactured plates can be retrofitted to an armoured fighting vehicle to withstand munitions thatcanpenetratetheoriginalarmourofthevehicle.Anadvantage of appliqué armour is the possibility to tailor the vehicle’s protection level to a specific threat scenario.

    Process parameters of laser cut-edges produced when using a traverse cutting speed of 1200 mm/min displayed the optimum intermediary properties.These parameters resulted in the generation of a surface with less stress rising features.This can result in a distribution of stress across the wider surface.It can,therefore,be concluded that the striation shape will significantly influence critical ballistic properties.

    Provided that appropriate process parameters are used to generate laser cut edges,the hardness properties of the surface can be controlled.This is due to compressive residual stresses produced in the near edge region as a result of metallurgical transformations.This way the traverse cutting speed parameter can be adjusted to alter critical surface characteristics and microstructural properties in close proximity to the cut-edge.

    Acknowledgment

    The author wishes to thank the support of Swansea University during the pursuit of this research.

    References

    [1]Edwards MR,Mathewson A.The ballistic properties of tool steel as a potential improvised armour plate.Int J Impact Eng 1997;19(4):297–309.

    [2]Demir T,übeyli M,Yildirim RO.Investigation on the ballistic impact behaviour of various alloys against 7.62 mm armour piercing projectile. Mater Des 2008;29(10):2009–16.

    [3]Gon?alves DP,de Melo FCL,Klein AN,Al-Qureshi HA.Analysis and investigation of ballistic impact on ceramic/metal composite armour.Int J Mach Tools Manuf 2004;44(2–3):307–16.

    [4]Shokrieh MM,Javadpour GH.Penetration analysis of a projectile in ceramic composite armour.Compos Struct 2008;82(2):269–76.

    [5]Karagoz S,Atapek SH,Yilmaz A.Microstructural and fractographical studiesonquenchedandtemperedarmoursteels.MaterTest 2010;52(5):316–22.

    [6]Gama BA,Bogetti TA,Fink BK,Yu CJ,Claar D,Eifert HH,et al. Aluminium foam integral armour:a new dimension in armour design. Compos Struct 2001;52(3–4):381–95.

    [7]Maweja K,Stumpf W.The design of advanced performance high strength low-carbon martensitic armour steels:part-1.Mechanical property considerations.Mater Sci Eng A Struct Mater 2008;485(1–2):140–53.

    [8]Dikshit SN.Influence of hardness on perforation velocity in steel armour plates.Def Sci J 2000;50(1):95–9.

    [9]Borvik T,Dey S,Clausen AH.Perforation resistance of five different high-strength steel plates subjected to small-arms projectiles.Int J Impact Eng 2009;36(7):948–64.

    [10]Hu CJ,Lee PY,Chen JS.Ballistic performance and microstructure of modifiedrolledhomogeneousarmoursteel.JChinInstEng 2002;25(1):99–107.

    [11]Sangoy L,Meunier Y,Pont G.Steels for ballistic protection.Israel J Technol 1988;24:319–26.

    [12]Jena PK,Kumar KS,Krishna VR,Singh AK,Bhat TB.Studies on the role of microstructure on performance of a high-strength armour steel.Eng Fail Anal 2008;15:1088–96.

    [13]Shipway PH,Wood SJ,Dent AH.The hardness and sliding wear behaviour of a bainitic steel.Wear 1997;203:196–205.

    [14]Shah SM,Bahadur S,Verhoeven JD.Erosion behaviour of high silicon bainitic structures;Part II:high silicon steels.Wear 1986;113:279–99.

    [15]Zhenming X,Qichuan J,Yuguang Z,Yanjun L,Zhenming H.A new type of wear resistant austenite bainite steel with granular carbides modified by boron and cerium rare earth.J Mater Sci Lett 1995;14:1410–11.

    [16]Ping L,Bahadur S,Verhoeven JD.Friction and wear behaviour of high silicon bainitic structures in austempered cast iron and steel.Wear 1990;138:269–84.

    [17]Meurling F,Melander A,Linder J,Larsson M,Trogen H.The influence of laser cutting on the fatigue properties of thin sheet steels.Swedish Institute for Metals Research Report IM-3691.1998.

    [18]Has?al?k A,Ay M.CO2 laser cut quality of Inconel 718 nickel–based superalloy.Opt Laser Technol 2013;48:554–64.

    [19]Eltawahni HA,Hagino M,Benyounis KY,Inoue T,Olabi AG.Effect of CO2 laser cutting process parameters on edge quality and operating cost of AISI316L.Opt Laser Technol 2012;44(4):1068–82.

    [20]Schulz W,Becker D,Frankr J,Kemmerling R,Herziger G.Heat conduction losses in laser cutting of metals.J Phys D Appl Phys 1993;26:1357–63.

    [21]Thomas DJ.The influence of the laser and plasma traverse cutting speed process parameter on the cut-edge characteristics and durability ofYellow Goods vehicle.J Manuf Process 2011;13:120–32.

    [22]Chocron S,Anderson C Jr,Grosch D,Popelar C.Impact of the 7.62-mm APM2 projectile against the edge of a metallic target.Int J Impact Eng 2001;25:423–37.

    [23]Radisavljevic I,Balos S,Nikacevic M,Sidjanin L.Optimization of geometrical characteristics of perforated plates.Mater Des 2013;49:81–9.

    [24]Balos S,Radisavljevic I,Rajnovic D,Dramicanin M,Tabakovic S, Eric-Cekic O,et al.Geometry,mechanical and ballistic properties ofADI material perforated plates.Mater Des 2015;83:66–74.

    Peer review under responsibility of China Ordnance Society.

    .Tel.:+4401656737349.

    E-mail address:D.J.Thomas@swansea.ac.uk(D.J.THOMAS).

    5 June 2016;revised 27 June 2016;accepted 19 July 2016

    亚洲av二区三区四区| 久久久国产精品麻豆| 亚洲狠狠婷婷综合久久图片| 免费搜索国产男女视频| 黄色片一级片一级黄色片| 成年女人毛片免费观看观看9| 国产aⅴ精品一区二区三区波| 精品久久久久久久人妻蜜臀av| 波野结衣二区三区在线 | 一进一出好大好爽视频| 久久久久久国产a免费观看| 精品乱码久久久久久99久播| 黄色视频,在线免费观看| 午夜老司机福利剧场| 亚洲人成电影免费在线| 淫妇啪啪啪对白视频| 国产伦在线观看视频一区| 不卡一级毛片| 国产一区在线观看成人免费| 香蕉丝袜av| 男人和女人高潮做爰伦理| 美女高潮的动态| 高潮久久久久久久久久久不卡| 国产毛片a区久久久久| 精品一区二区三区人妻视频| 免费电影在线观看免费观看| 国产精品 国内视频| 亚洲成人久久爱视频| 亚洲第一电影网av| 白带黄色成豆腐渣| 亚洲精品成人久久久久久| 哪里可以看免费的av片| 给我免费播放毛片高清在线观看| 级片在线观看| 又黄又爽又免费观看的视频| 亚洲 国产 在线| 亚洲片人在线观看| 免费观看人在逋| 一级作爱视频免费观看| 啦啦啦观看免费观看视频高清| 久久精品亚洲精品国产色婷小说| 无遮挡黄片免费观看| 国产精品一区二区三区四区久久| 别揉我奶头~嗯~啊~动态视频| 午夜福利成人在线免费观看| 老熟妇乱子伦视频在线观看| 3wmmmm亚洲av在线观看| 51午夜福利影视在线观看| 很黄的视频免费| 久久久久精品国产欧美久久久| 国产伦在线观看视频一区| 91久久精品电影网| 亚洲熟妇熟女久久| 精品一区二区三区视频在线 | 国内揄拍国产精品人妻在线| 综合色av麻豆| 亚洲人与动物交配视频| 亚洲av中文字字幕乱码综合| 久久久久久九九精品二区国产| 精品国产美女av久久久久小说| 18禁美女被吸乳视频| 午夜激情欧美在线| 特级一级黄色大片| 久久精品夜夜夜夜夜久久蜜豆| 最近最新中文字幕大全免费视频| 成人鲁丝片一二三区免费| 在线国产一区二区在线| 此物有八面人人有两片| 岛国在线免费视频观看| www.熟女人妻精品国产| 熟女电影av网| 天堂动漫精品| 国产真实乱freesex| 免费观看精品视频网站| 成人国产一区最新在线观看| 亚洲性夜色夜夜综合| 亚洲人与动物交配视频| 亚洲国产欧美网| 12—13女人毛片做爰片一| 波多野结衣高清作品| 免费观看的影片在线观看| 久久久久精品国产欧美久久久| 国产视频一区二区在线看| 国产不卡一卡二| 91在线精品国自产拍蜜月 | 亚洲片人在线观看| 高清毛片免费观看视频网站| 国产探花在线观看一区二区| 男女床上黄色一级片免费看| 高清毛片免费观看视频网站| 99热精品在线国产| 99国产极品粉嫩在线观看| or卡值多少钱| 99久久精品国产亚洲精品| 欧美日本视频| av天堂在线播放| 国产一区二区三区在线臀色熟女| 成年女人毛片免费观看观看9| 欧美激情久久久久久爽电影| 国产精品久久久久久精品电影| 国产精品精品国产色婷婷| 非洲黑人性xxxx精品又粗又长| av专区在线播放| 每晚都被弄得嗷嗷叫到高潮| 久久久久久大精品| 国产成人欧美在线观看| 九九在线视频观看精品| 亚洲av美国av| 日韩有码中文字幕| 老司机深夜福利视频在线观看| 村上凉子中文字幕在线| 亚洲av日韩精品久久久久久密| 丰满乱子伦码专区| av在线天堂中文字幕| 免费观看人在逋| 真人一进一出gif抽搐免费| 精品午夜福利视频在线观看一区| 国产成人a区在线观看| 色综合婷婷激情| 日本黄色视频三级网站网址| 亚洲精品一区av在线观看| 99精品欧美一区二区三区四区| 亚洲七黄色美女视频| 别揉我奶头~嗯~啊~动态视频| 国产精品 欧美亚洲| 成人永久免费在线观看视频| 麻豆成人av在线观看| 五月伊人婷婷丁香| 丰满人妻一区二区三区视频av | 少妇裸体淫交视频免费看高清| 老鸭窝网址在线观看| 亚洲欧美激情综合另类| 国产成人啪精品午夜网站| 国产成+人综合+亚洲专区| 亚洲电影在线观看av| eeuss影院久久| 久久精品综合一区二区三区| 久久天躁狠狠躁夜夜2o2o| 国产亚洲欧美98| 看免费av毛片| 国产视频一区二区在线看| 18禁黄网站禁片免费观看直播| 19禁男女啪啪无遮挡网站| 狠狠狠狠99中文字幕| 国产真实乱freesex| 校园春色视频在线观看| 在线观看66精品国产| 国产蜜桃级精品一区二区三区| 欧美激情在线99| 法律面前人人平等表现在哪些方面| 老司机在亚洲福利影院| 久久久久久久午夜电影| 亚洲国产中文字幕在线视频| 亚洲一区二区三区色噜噜| 国产精品日韩av在线免费观看| 桃色一区二区三区在线观看| 欧美日韩精品网址| 国产精品免费一区二区三区在线| 欧美黄色淫秽网站| 欧美区成人在线视频| www.999成人在线观看| 可以在线观看的亚洲视频| 免费av观看视频| 精品久久久久久,| 一个人免费在线观看电影| 欧美另类亚洲清纯唯美| 人妻夜夜爽99麻豆av| 一个人免费在线观看的高清视频| 午夜福利成人在线免费观看| 国产高潮美女av| 听说在线观看完整版免费高清| 老司机福利观看| av天堂中文字幕网| 久久精品综合一区二区三区| 亚洲不卡免费看| 国产午夜福利久久久久久| 九九热线精品视视频播放| 最新在线观看一区二区三区| 国产视频一区二区在线看| 中文字幕人妻丝袜一区二区| 国产精品久久久久久久久免 | 两个人的视频大全免费| 亚洲av熟女| 天堂网av新在线| 日本五十路高清| 最近最新免费中文字幕在线| 波多野结衣巨乳人妻| 亚洲美女黄片视频| 亚洲国产色片| 麻豆成人av在线观看| 国产一区二区激情短视频| 狂野欧美激情性xxxx| 欧美区成人在线视频| 有码 亚洲区| 色视频www国产| 色老头精品视频在线观看| 久久99热这里只有精品18| 精品熟女少妇八av免费久了| 亚洲av二区三区四区| 国产一区二区在线av高清观看| 成人鲁丝片一二三区免费| 变态另类成人亚洲欧美熟女| 亚洲av日韩精品久久久久久密| 亚洲avbb在线观看| ponron亚洲| 91久久精品国产一区二区成人 | 精华霜和精华液先用哪个| 免费看十八禁软件| 欧美+日韩+精品| 一进一出好大好爽视频| 精品午夜福利视频在线观看一区| 精品电影一区二区在线| 日本一二三区视频观看| 特级一级黄色大片| 国产精品日韩av在线免费观看| 校园春色视频在线观看| 在线观看av片永久免费下载| 成人午夜高清在线视频| 成人一区二区视频在线观看| 国产伦精品一区二区三区视频9 | 在线天堂最新版资源| 国产一区二区亚洲精品在线观看| 日韩欧美在线二视频| 大型黄色视频在线免费观看| av在线蜜桃| 一个人免费在线观看电影| 中文字幕人妻熟人妻熟丝袜美 | 国产精品亚洲av一区麻豆| 变态另类成人亚洲欧美熟女| 欧美性猛交黑人性爽| 成人18禁在线播放| 午夜影院日韩av| 国产精品久久视频播放| 国产成+人综合+亚洲专区| 日韩欧美三级三区| 亚洲av不卡在线观看| 亚洲一区二区三区色噜噜| 国产高清有码在线观看视频| 一级毛片高清免费大全| 美女黄网站色视频| 色综合欧美亚洲国产小说| 亚洲中文字幕一区二区三区有码在线看| 极品教师在线免费播放| 国产色婷婷99| 久久久成人免费电影| bbb黄色大片| 白带黄色成豆腐渣| 亚洲无线在线观看| 久久久精品大字幕| 草草在线视频免费看| 精品熟女少妇八av免费久了| 精品国产超薄肉色丝袜足j| 免费观看人在逋| 99精品在免费线老司机午夜| 久久精品国产清高在天天线| 亚洲第一欧美日韩一区二区三区| 女人高潮潮喷娇喘18禁视频| 一级作爱视频免费观看| 免费av不卡在线播放| 深爱激情五月婷婷| 亚洲av中文字字幕乱码综合| 亚洲av成人av| 蜜桃久久精品国产亚洲av| 国产三级中文精品| 好男人在线观看高清免费视频| 欧美精品啪啪一区二区三区| 听说在线观看完整版免费高清| 国产成人av激情在线播放| 精品国产三级普通话版| 国产成人欧美在线观看| 97碰自拍视频| 精品熟女少妇八av免费久了| 国产一级毛片七仙女欲春2| 成人午夜高清在线视频| 老司机深夜福利视频在线观看| 国产一区二区激情短视频| 中文字幕人妻熟人妻熟丝袜美 | 两个人看的免费小视频| 国产不卡一卡二| 久久久久性生活片| 日韩免费av在线播放| 午夜老司机福利剧场| 亚洲va日本ⅴa欧美va伊人久久| 琪琪午夜伦伦电影理论片6080| 最新美女视频免费是黄的| 午夜福利欧美成人| 亚洲欧美精品综合久久99| 大型黄色视频在线免费观看| 成人性生交大片免费视频hd| 精品国产亚洲在线| 日韩欧美精品免费久久 | 国产野战对白在线观看| 国产成人av教育| 亚洲中文字幕日韩| 国产亚洲av嫩草精品影院| 天堂影院成人在线观看| 午夜a级毛片| 国内精品久久久久久久电影| 老熟妇仑乱视频hdxx| 成人无遮挡网站| 成人永久免费在线观看视频| 国产一区二区在线观看日韩 | 亚洲精华国产精华精| 亚洲片人在线观看| or卡值多少钱| 国产久久久一区二区三区| 国产黄片美女视频| 宅男免费午夜| 熟女人妻精品中文字幕| 国产亚洲精品综合一区在线观看| 日韩免费av在线播放| 听说在线观看完整版免费高清| 又爽又黄无遮挡网站| 激情在线观看视频在线高清| 日本 av在线| 成人无遮挡网站| a级一级毛片免费在线观看| 亚洲国产精品sss在线观看| 国产精品 国内视频| 中文字幕久久专区| 午夜免费成人在线视频| 我要搜黄色片| 欧美大码av| 久久久久亚洲av毛片大全| 性色av乱码一区二区三区2| 久久人妻av系列| 精品一区二区三区人妻视频| 午夜亚洲福利在线播放| 精品人妻一区二区三区麻豆 | 国产精品1区2区在线观看.| 国产精品精品国产色婷婷| 国产激情欧美一区二区| 99在线人妻在线中文字幕| 黑人欧美特级aaaaaa片| 97超视频在线观看视频| 日韩欧美国产在线观看| 免费av毛片视频| 成人亚洲精品av一区二区| 亚洲国产精品sss在线观看| 成年免费大片在线观看| 日韩欧美精品v在线| 亚洲成a人片在线一区二区| 精品电影一区二区在线| 少妇人妻精品综合一区二区 | 久久久久亚洲av毛片大全| 可以在线观看的亚洲视频| 我的老师免费观看完整版| 午夜免费激情av| 波野结衣二区三区在线 | 成人永久免费在线观看视频| 一个人免费在线观看电影| 国产亚洲精品一区二区www| 舔av片在线| 亚洲午夜理论影院| 亚洲国产欧洲综合997久久,| 美女被艹到高潮喷水动态| 老汉色av国产亚洲站长工具| 中文字幕久久专区| 亚洲国产欧美人成| netflix在线观看网站| 国产一区二区三区在线臀色熟女| 久久久久久久久中文| 成人特级av手机在线观看| 精品久久久久久久久久免费视频| 深夜精品福利| 美女被艹到高潮喷水动态| 19禁男女啪啪无遮挡网站| 免费人成在线观看视频色| 长腿黑丝高跟| 国产成人av激情在线播放| 国产高清视频在线观看网站| 国产欧美日韩精品一区二区| 成年女人永久免费观看视频| 午夜免费男女啪啪视频观看 | 一本综合久久免费| 91在线精品国自产拍蜜月 | 给我免费播放毛片高清在线观看| 老汉色∧v一级毛片| 青草久久国产| 我的老师免费观看完整版| 麻豆国产av国片精品| 动漫黄色视频在线观看| 欧美日韩一级在线毛片| 成人国产一区最新在线观看| 成年免费大片在线观看| www日本黄色视频网| 欧美极品一区二区三区四区| 国内揄拍国产精品人妻在线| 天堂影院成人在线观看| 欧美黑人欧美精品刺激| 精品国内亚洲2022精品成人| 90打野战视频偷拍视频| 熟妇人妻久久中文字幕3abv| 狠狠狠狠99中文字幕| 少妇高潮的动态图| 18禁裸乳无遮挡免费网站照片| 全区人妻精品视频| 久久久色成人| 亚洲av成人不卡在线观看播放网| 国产精品亚洲av一区麻豆| 美女免费视频网站| 蜜桃久久精品国产亚洲av| 婷婷六月久久综合丁香| 中文在线观看免费www的网站| 欧美午夜高清在线| 精品久久久久久久久久免费视频| 女生性感内裤真人,穿戴方法视频| 国产成人a区在线观看| 天堂√8在线中文| 精品久久久久久久人妻蜜臀av| 精品久久久久久久毛片微露脸| 欧美乱码精品一区二区三区| 欧美zozozo另类| 欧美最新免费一区二区三区 | 99精品久久久久人妻精品| 中文字幕av成人在线电影| 51国产日韩欧美| 亚洲成人久久性| 一级作爱视频免费观看| 国产男靠女视频免费网站| 免费看日本二区| av国产免费在线观看| 欧美另类亚洲清纯唯美| 亚洲,欧美精品.| 脱女人内裤的视频| 国产精品爽爽va在线观看网站| 欧美日韩国产亚洲二区| 欧美激情在线99| 欧美日韩综合久久久久久 | 午夜免费观看网址| 99精品在免费线老司机午夜| av在线天堂中文字幕| 欧美日韩瑟瑟在线播放| 久久天躁狠狠躁夜夜2o2o| 亚洲 欧美 日韩 在线 免费| 在线观看日韩欧美| 亚洲自拍偷在线| 老司机福利观看| 国产精品久久久人人做人人爽| 高清在线国产一区| 国产黄a三级三级三级人| 精品久久久久久久人妻蜜臀av| 亚洲av五月六月丁香网| 亚洲av第一区精品v没综合| 国产乱人伦免费视频| 男插女下体视频免费在线播放| 不卡一级毛片| 夜夜夜夜夜久久久久| 国产一区二区在线观看日韩 | 一级a爱片免费观看的视频| 国产97色在线日韩免费| 久久久久久人人人人人| 欧美一区二区亚洲| 亚洲熟妇熟女久久| 国产成人啪精品午夜网站| 男女午夜视频在线观看| 一级作爱视频免费观看| 亚洲电影在线观看av| 国产精品久久视频播放| 又黄又爽又免费观看的视频| 国产精品精品国产色婷婷| 99久久精品一区二区三区| 日韩欧美三级三区| 成人18禁在线播放| 在线观看一区二区三区| 国产视频内射| 亚洲av成人不卡在线观看播放网| 一级作爱视频免费观看| 亚洲中文字幕一区二区三区有码在线看| 色精品久久人妻99蜜桃| 婷婷亚洲欧美| 亚洲七黄色美女视频| 老司机深夜福利视频在线观看| 极品教师在线免费播放| 少妇的逼水好多| 成年女人永久免费观看视频| 午夜精品一区二区三区免费看| 黄片小视频在线播放| 国产精品永久免费网站| 日韩 欧美 亚洲 中文字幕| 成年免费大片在线观看| 国产av在哪里看| 99热这里只有精品一区| 长腿黑丝高跟| 老司机深夜福利视频在线观看| 中国美女看黄片| 国产高清视频在线播放一区| 亚洲第一欧美日韩一区二区三区| 97超视频在线观看视频| 韩国av一区二区三区四区| 69av精品久久久久久| 在线天堂最新版资源| 在线免费观看不下载黄p国产 | 国产探花极品一区二区| 日韩高清综合在线| 91字幕亚洲| 成人亚洲精品av一区二区| 美女高潮喷水抽搐中文字幕| 欧美日韩国产亚洲二区| 一本久久中文字幕| 欧美+亚洲+日韩+国产| 精品日产1卡2卡| 88av欧美| 特级一级黄色大片| 毛片女人毛片| 精品一区二区三区视频在线观看免费| 99热6这里只有精品| 亚洲片人在线观看| 免费一级毛片在线播放高清视频| 偷拍熟女少妇极品色| 国产老妇女一区| 黄色片一级片一级黄色片| 男女下面进入的视频免费午夜| 日韩大尺度精品在线看网址| 69人妻影院| 日本黄大片高清| 国产单亲对白刺激| 欧美黑人欧美精品刺激| 欧美绝顶高潮抽搐喷水| 欧美成狂野欧美在线观看| 国产高清视频在线播放一区| 亚洲av电影不卡..在线观看| 国产成人福利小说| 欧美不卡视频在线免费观看| 在线观看免费午夜福利视频| 精品久久久久久,| 真实男女啪啪啪动态图| 乱人视频在线观看| 全区人妻精品视频| 亚洲一区高清亚洲精品| 欧美黑人欧美精品刺激| 日韩国内少妇激情av| 久久午夜亚洲精品久久| 中文字幕av成人在线电影| 内地一区二区视频在线| 九九热线精品视视频播放| 波野结衣二区三区在线 | 精品国产超薄肉色丝袜足j| 国产亚洲欧美98| 亚洲,欧美精品.| 成人永久免费在线观看视频| 给我免费播放毛片高清在线观看| 少妇人妻一区二区三区视频| 中文字幕人妻熟人妻熟丝袜美 | 国产精品乱码一区二三区的特点| 真人一进一出gif抽搐免费| 18禁黄网站禁片免费观看直播| 日韩大尺度精品在线看网址| 女人十人毛片免费观看3o分钟| 亚洲中文字幕一区二区三区有码在线看| 狂野欧美激情性xxxx| 午夜免费观看网址| 搡老熟女国产l中国老女人| 在线观看午夜福利视频| 亚洲精品一区av在线观看| 男女那种视频在线观看| 免费观看人在逋| av在线蜜桃| 欧美另类亚洲清纯唯美| 亚洲无线在线观看| 国产视频一区二区在线看| 欧美丝袜亚洲另类 | 日韩免费av在线播放| 亚洲不卡免费看| 精品久久久久久久毛片微露脸| 99视频精品全部免费 在线| av片东京热男人的天堂| 男女做爰动态图高潮gif福利片| 在线国产一区二区在线| 少妇裸体淫交视频免费看高清| 身体一侧抽搐| 老司机福利观看| 欧美日韩中文字幕国产精品一区二区三区| 免费av不卡在线播放| 国产视频内射| 波多野结衣高清作品| 欧美不卡视频在线免费观看| 美女 人体艺术 gogo| 久久中文看片网| 欧美日韩国产亚洲二区| 欧美色视频一区免费| 热99在线观看视频| 韩国av一区二区三区四区| 午夜福利视频1000在线观看| 亚洲国产精品999在线| 日本一本二区三区精品| 99国产精品一区二区蜜桃av| 国产高清视频在线播放一区| 国产精品永久免费网站| 香蕉丝袜av| 欧美一区二区精品小视频在线| 99热这里只有精品一区| 亚洲性夜色夜夜综合| 身体一侧抽搐| 亚洲国产精品久久男人天堂| 欧美性猛交╳xxx乱大交人| 身体一侧抽搐| svipshipincom国产片| 噜噜噜噜噜久久久久久91| 国产99白浆流出| 法律面前人人平等表现在哪些方面| 国产精品自产拍在线观看55亚洲| 国内精品美女久久久久久| 法律面前人人平等表现在哪些方面| 黄色视频,在线免费观看| 人妻夜夜爽99麻豆av| 日本在线视频免费播放| 亚洲av一区综合| 免费在线观看影片大全网站| 国产精品永久免费网站| 午夜亚洲福利在线播放| 好男人电影高清在线观看| 两个人看的免费小视频| 亚洲国产精品成人综合色| 精品电影一区二区在线|